    • Method for forming photoluminescent coating film and coated material
    • 形成光致发光涂层膜和涂层材料的方法
    • JP2010155246A
    • 2010-07-15
    • JP2010091457
    • 2010-04-12
    • Honda Motor Co LtdNippon Bee Chemical Co LtdNippon Paint Co Ltd日本ビー・ケミカル株式会社日本ペイント株式会社本田技研工業株式会社
    • OGAWA TSUYOSHIIHARA OSAMUUCHIYAMA TOSHIHIKOINOUE MASANOBUMIYASOI SEIGOSHIRAGA RYUICHI
    • B05D5/06B05D1/36
    • PROBLEM TO BE SOLVED: To provide a method for forming a photoluminescent coating film that gives feelings of luminosity of high-degree appearance using a water based paint together with a first base coating and a second base coating without preheating after the first base coating is performed.
      SOLUTION: The method for forming a photoluminescent coating film is such that a first base coating film is formed by applying a water first-base photoluminescent coating onto a coated film formation over each predetermined coating zone, subsequently, a second base coating film is formed by applying a water second-base photoluminescent coating onto the first base coating film, a clear coating film is formed by applying a clear coating onto the second base coating film, and the uncured coating film obtained above is heat cured at once with the conditions (A): the solid content of coating in the water first base photoluminescent coating is 10 to 45 mass% and the solid content of coating in the aqueous second-base photo luminescent coating is 10 to 40 mass%, and (B): the solid content ratio of coating of the water first base photoluminescent coating and the water second base photoluminescent coating satisfies (1.1/1) to (4/1).
      COPYRIGHT: (C)2010,JPO&INPIT
    • 要解决的问题:提供一种形成光致发光涂膜的方法,其使用水性涂料与第一基底涂层和第二基底涂层一起提供高度外观的光泽感,而在第一基底之后不预热 进行涂布。 解决方案:用于形成光致发光涂膜的方法是通过在每个预定涂布区域上的涂布膜上施加水第一基底光致发光涂层形成第一基底涂膜,随后形成第二基底涂膜 通过在第一基底涂膜上施加水第二基光致发光涂层而形成,通过在第二基底涂膜上施加透明涂层形成透明涂膜,并将上述获得的未固化涂膜用 条件(A):水中第一基底光致发光涂层中的涂层的固体含量为10〜45质量%,第二碱性光致发光涂料水溶液的固体成分为10〜40质量%,(B): 水第一基底光致发光涂层和水第二基底层发光涂层的涂层的固体含量比满足(1.1 / 1)至(4/1)。 版权所有(C)2010,JPO&INPIT