1. 发明专利

JP2013023768A Magnesium alloy material, and method of treating surface of magnesium alloy 有权
标题翻译：镁合金材料及其处理镁合金表面的方法
公开(公告)号：JP2013023768A
公开(公告)日：2013-02-04
申请号：JP2011163232
申请日：2011-07-26
申请人： National Institute Of Advanced Industrial Science & Technology , 独立行政法人産業技術総合研究所 , A & A Material Corp , 株式会社エーアンドエーマテリアル
发明人： ISHIZAKI TAKAHIRO , FUTOMI KENJI , KUDO RURIKO
IPC分类号： C23C22/07 , C23C22/60 , C23C22/73
CPC分类号： C23C22/60 , C23C22/73 , C23C22/83
摘要： PROBLEM TO BE SOLVED: To provide magnesium alloy material with high corrosion resistance and high adhesion, and a method of treating a surface of magnesium alloy.SOLUTION: The magnesium alloy material is obtained by performing a surface treatment on the magnesium alloy 11 using a liquid, and subsequently bringing it into contact with water 13 in the form of droplets and/or gas having passed through a membrane filter with a pore size of 10-100 nm in a container 10 with a container pressure of 0.35-0.5 MPa at a temperature of 145-160°C. The method of treating the surface of the magnesium alloy includes the steps of: performing the surface treatment on the magnesium alloy using the liquid; and bringing the magnesium alloy subjected to the surface treatment into contact with the water in the form of droplets and/or gas having passed through the membrane filter with the pore size of 10-100 nm in the container with the container pressure of 0.35-0.5 MPa at a temperature of 145-160°C.
摘要翻译：要解决的问题：提供具有高耐蚀性和高附着力的镁合金材料，以及一种处理镁合金表面的方法。解决方案：镁合金材料是通过使用液体对镁合金11进行表面处理而获得的，随后使其与通过膜过滤器的液滴和/或气体形式的水13接触，在容器10中的孔径为10-100nm，容器压力为0.35-0.5MPa，温度为145-160℃。处理镁合金表面的方法包括以下步骤：使用液体对镁合金进行表面处理; 并使容器中经过表面处理的镁合金与液体和/或气体形式的水接触，所述液体和/或气体通过容器内的孔径为10-100nm的膜过滤器，容器压力为0.35-0.5 在145-160℃的温度下进行。版权所有（C）2013，JPO＆INPIT

2. 发明专利

JP2011093784A Silica film, method of forming the same, silica film attached material and production method thereof 有权
标题翻译：硅胶膜，其形成方法，二氧化硅膜连接材料及其生产方法
公开(公告)号：JP2011093784A
公开(公告)日：2011-05-12
申请号：JP2010209693
申请日：2010-09-17
申请人： A & A Material Corp , National Institute Of Advanced Industrial Science & Technology , 株式会社エーアンドエーマテリアル , 独立行政法人産業技術総合研究所
发明人： TSUNEMATSU SHUJI , TSUNEMATSU KINUE , NISHIKUBO KEIKO , KUDO RURIKO , FUTOMI KENJI , SAKIYAMA MASATO
IPC分类号： C01B33/12 , C01B33/187
摘要： PROBLEM TO BE SOLVED: To provide a method of forming a silica film having excellent corrosion resistance, impact resistance as well as having a high silica purity.
SOLUTION: The silica film is formed by carbonating and steam-curing an alkali silicate metal salt. The method of forming the silica film includes a process of carbonating and steam-curing for carbonating and steam-curing the alkali silicate metal salt.
COPYRIGHT: (C)2011,JPO&INPIT
摘要翻译：要解决的问题：提供一种形成具有优异的耐腐蚀性，耐冲击性以及二氧化硅纯度高的二氧化硅膜的方法。解决方案：通过碳酸化和蒸汽固化碱金属硅酸盐金属盐形成二氧化硅膜。形成二氧化硅膜的方法包括碳酸化和蒸汽固化用于碳酸化和蒸汽固化碱金属硅酸盐金属盐的方法。版权所有（C）2011，JPO＆INPIT

3. 发明专利

JP2012082451A Method for treating surface of magnesium alloy member 有权
标题翻译：用于处理镁合金构件表面的方法
公开(公告)号：JP2012082451A
公开(公告)日：2012-04-26
申请号：JP2010227535
申请日：2010-10-07
申请人： A & A Material Corp , National Institute Of Advanced Industrial Science & Technology , 株式会社エーアンドエーマテリアル , 独立行政法人産業技術総合研究所
发明人： ISHIZAKI TAKAHIRO , SAKAMOTO MITSURU , FUTOMI KENJI , KAWASAKI EIJI , KUDO RURIKO , SAKIYAMA MASATO
IPC分类号： C23C8/10 , C23C8/16
摘要： PROBLEM TO BE SOLVED: To provide a method for treating a surface of a magnesium alloy member, which can obtain a more preferable corrosion resistance than before.SOLUTION: The method for treating a surface of a magnesium alloy member, includes the steps of: (a) preparing a magnesium alloy member containing aluminum; and (b) holding the magnesium alloy member in an environment containing water vapor at the pressure of 0.25-1.0 MPa in the temperature of 170-190 °C.
摘要翻译：要解决的问题：提供一种可以获得比以前更优选的耐腐蚀性的镁合金构件的表面处理方法。解决方案：用于处理镁合金构件表面的方法包括以下步骤：（a）制备含有铝的镁合金构件; 和（b）将镁合金构件保持在温度为170-190℃的压力为0.25-1.0MPa的水蒸气环境中。版权所有（C）2012，JPO＆INPIT

4. 发明专利

JP2009242198A Porous self-supporting clay film and its producing method 有权
标题翻译：多孔自支撑粘膜及其生产方法
公开(公告)号：JP2009242198A
公开(公告)日：2009-10-22
申请号：JP2008092850
申请日：2008-03-31
申请人： A & A Material Corp , National Institute Of Advanced Industrial & Technology , 株式会社エーアンドエーマテリアル , 独立行政法人産業技術総合研究所
发明人： KAWASAKI EIJI , FUTOMI KENJI , SAKIYAMA MASATO , EBINA TAKEO , MIZUKAMI FUJIO
IPC分类号： C01B33/40
摘要： PROBLEM TO BE SOLVED: To provide a porous self-supporting clay film excellent in not only heat resistance but also thermal insulation properties and a method for producing the porous self-supporting clay film. SOLUTION: The porous self-supporting clay film is based on clay, has such a structure that clay layered crystals are layered on one another, is used as a self-supporting film, has a void among the adjacent clay layered crystals, and has a hole which penetrates the clay layered crystals and reaches the surface of the clay film. COPYRIGHT: (C)2010,JPO&INPIT
摘要翻译：要解决的问题：提供不仅耐热性优异而且绝热性优异的多孔自支撑粘土膜以及多孔自支撑粘土膜的制造方法。解决方案：多孔自支撑粘土膜基于粘土，具有使粘土层状结晶彼此层叠的结构，用作自支撑膜，在相邻的粘土层状晶体中具有空隙，并且具有穿透粘土层状结晶并到达粘土膜表面的孔。版权所有（C）2010，JPO＆INPIT

5. 发明专利

JP2010235691A Coated porous inorganic particle and molded article using the same 有权
标题翻译：包覆无机颗粒和使用它的成型品
公开(公告)号：JP2010235691A
公开(公告)日：2010-10-21
申请号：JP2009082905
申请日：2009-03-30
申请人： A & A Material Corp , Niigata Univ , 国立大学法人新潟大学 , 株式会社エーアンドエーマテリアル
发明人： TANAKA MASATO , SAITO KAFU , INOUE TOMOHIRO , FUTOMI KENJI , SAKIYAMA MASATO
IPC分类号： C08K9/04 , C01B33/12 , C01B33/24
摘要： PROBLEM TO BE SOLVED: To provide a molded article exhibiting both excellent insulating property and strength.
SOLUTION: The particle is made by coating the surface of a porous aggregate of silicic acid calcium hydrate crystal with a thermosetting resin, and the molded article is obtained by using the same.
COPYRIGHT: (C)2011,JPO&INPIT
摘要翻译：要解决的问题：提供具有优异的绝缘性能和强度的模塑制品。解决方案：通过用热固性树脂涂覆硅酸钙水合物晶体的多孔骨料的表面来制备颗粒，并且通过使用它们获得模塑制品。版权所有（C）2011，JPO＆INPIT

6. 发明专利

JP2012213857A Coated panel and method for manufacturing the same 有权
标题翻译：涂层面板及其制造方法
公开(公告)号：JP2012213857A
公开(公告)日：2012-11-08
申请号：JP2011078862
申请日：2011-03-31
申请人： A & A Material Corp , 株式会社エーアンドエーマテリアル
发明人： KAWASAKI EIJI , INOUE TOMOHIRO , AOKI MASAMI , FUTOMI KENJI
IPC分类号： B32B27/00 , B05D7/00 , B05D7/24 , B32B13/12
摘要： PROBLEM TO BE SOLVED: To provide a coated panel that has high durability although that is free from asbestos as a raw material of a substrate, and also maintains a predetermined reflectance even when being washed periodically, and to provide a method for manufacturing the same.SOLUTION: The coated panel including a fiber-reinforced cement panel as the substrate, includes an impregnated sealer layer, a surfacer layer and a top coat layer with an organopolysiloxane-based coating material, which are laminated on one surface of the substrate in this order.
摘要翻译：要解决的问题：提供一种具有高耐久性的涂层面板，尽管不含作为基材的原料的石棉，并且即使在周期性洗涤时也保持预定的反射率，并且提供一种制造方法一样。解决方案：包括纤维增强水泥面板作为基材的涂布面板包括浸渍的密封层，表面层和具有有机聚硅氧烷基涂层材料的顶涂层，其层压在基材的一个表面上按此顺序版权所有（C）2013，JPO＆INPIT

7. 发明专利

JP2011213750A Coated porous inorganic particle containing heat storage substance and heat storage material including the same 有权
标题翻译：包含热存储物质和热存储材料的包衣多孔无机颗粒
公开(公告)号：JP2011213750A
公开(公告)日：2011-10-27
申请号：JP2010080188
申请日：2010-03-31
申请人： A & A Material Corp , Niigata Univ , 国立大学法人新潟大学 , 株式会社エーアンドエーマテリアル
发明人： TANAKA MASATO , SAITO KAFU , INOUE TOMOHIRO , FUTOMI KENJI , SAKIYAMA MASATO
IPC分类号： C09K5/08 , C01B33/24 , C09K5/06
摘要： PROBLEM TO BE SOLVED: To provide a heat storage material having high thermal response and mechanical strength and a broad application range.SOLUTION: A particle includes a heat storage substance inside porous aggregate of a crystalline calcium silicate hydrate and has a surface coated with a thermosetting resin.
摘要翻译：要解决的问题：提供一种具有高热响应性和机械强度以及广泛应用范围的储热材料。解决方案：一种颗粒包括结晶硅酸钙水合物的多孔聚集体内的蓄热物质，其表面涂有热固性树脂。

8. 发明专利

JP2011163069A Decorative plate and method for manufacturing the same 有权
标题翻译：装饰板及其制造方法
公开(公告)号：JP2011163069A
公开(公告)日：2011-08-25
申请号：JP2010029754
申请日：2010-02-15
申请人： A & A Material Corp , 株式会社エーアンドエーマテリアル
发明人： INOUE TOMOHIRO , FUTOMI KENJI , KAWASAKI EIJI
IPC分类号： E04C2/16 , B05D7/00 , B32B13/02 , B32B13/14 , E04F13/14
摘要： PROBLEM TO BE SOLVED: To provide a decorative plate having an incombustible property and excelling in surface smoothness, appearance, water resistance, weather resistance and handleability. SOLUTION: The decorative plate is formed by applying impregnation sealer treatment 104 on one side of a fiber reinforced cement plate 102, and forming a surfacer coating film 106, an enamel coating film 108 and a clear coating film 110 on the treated surface. The decorative plate fulfills the following conditions (1)-(3): (1) the fiber reinforced cement plate has a thickness of 3-6.5 mm, an apparent density of 1.4-1.8 g/cm 3 , and the content ratio of pulp which is reinforcing fiber being 5-8 mass%, (2) the sum total of organic solid contents contained in components of the impregnation sealer, components of the surfacer coating film, components of the enamel coating film and components of the clear coating film is 63-130 g per unit area (m 2 ) of the fiber reinforced cement plate, and (3) the heating value of the decorative plate is 8 MJ/m 2 or less. COPYRIGHT: (C)2011,JPO&INPIT
摘要翻译：要解决的问题：提供一种具有不燃性和表面平滑性，外观，耐水性，耐候性和可操作性优异的装饰板。解决方案：装饰板通过在纤维增强水泥板102的一侧上施加浸渍密封剂处理104并在处理表面上形成表面涂层膜106，搪瓷涂膜108和透明涂层膜110而形成。装饰板满足以下条件（1） - （3）：（1）纤维增强水泥板的厚度为3-6.5mm，表观密度为1.4-1.8g / cm 3 SP / ，增强纤维的纸浆含量比例为5-8质量％，（2）浸渍封口剂的成分，表面涂膜的成分，搪瓷涂膜的成分和搪瓷涂膜的成分中含有的有机固体成分的总和透明涂膜的部件为纤维增强水泥板的单位面积（m 2 ）为63〜130g，（3）装饰板的加热值为8MJ / m·SP > 2 以下。版权所有（C）2011，JPO＆INPIT

9. 发明专利

JP2010137435A Decorative plate and method of manufacturing the same 有权
标题翻译：装饰板及其制造方法
公开(公告)号：JP2010137435A
公开(公告)日：2010-06-24
申请号：JP2008315602
申请日：2008-12-11
申请人： A & A Material Corp , 株式会社エーアンドエーマテリアル
发明人： KAWASAKI EIJI , FUTOMI KENJI
IPC分类号： B32B13/02 , B27M3/00 , B27N3/00 , B32B33/00 , E04F13/18
CPC分类号： C04B28/02 , C04B28/188 , C04B41/009 , C04B41/52 , C04B2111/00318 , C04B2111/00612 , C04B2111/12 , C04B2201/20 , C04B2201/30 , C04B14/00 , C04B14/043 , C04B14/38 , C04B16/06 , C04B20/0048 , C04B20/008 , C04B40/0259 , C04B7/00 , C04B41/46 , C04B2111/20
摘要： PROBLEM TO BE SOLVED: To provide a decorative plate which causes less deflection by self-weight even when being a thin plate and has good handling properties in transportation and construction, ease of work and excellent incombustibility and a method of manufacturing the same. SOLUTION: The decorative plate uses, as a substrate, a thin inorganic papermaking plate obtained by wet-mixing a blend comprising 30-70 mass% of a hydrating material for formation of a matrix, 3-6 mass% of a natural fiber and 0.5-3 mass% of an inorganic fiber and/or a synthetic fiber, excluding asbestos, 5-30 mass% of calcium silicate hydrate, 5-20 mass% of Wollastonite and 1-15 mass% of an inorganic filler to form a slurry, papermaking the slurry to obtain a green plate and pressure-dehydrating and curing and hardening the green plate and has, on one surface, a decorative layer consisting of a base-coat reinforcing layer, a decorative layer and a surface protecting layer. COPYRIGHT: (C)2010,JPO&INPIT
摘要翻译：要解决的问题：提供一种装饰板，即使在薄板状况下也能够通过自重进行较小的偏转，并且在运输和施工中具有良好的操作性能，易于加工和优异的不燃性及其制造方法。解决方案：装饰板使用通过湿混合包含30-70质量％的用于形成基质的水合材料的共混物而获得的薄无机造纸板，3-6质量％的天然纤维和0.5-3质量％的无机纤维和/或合成纤维，不包括石棉，5-30质量％的硅酸钙水合物，5-20质量％的硅灰石和1-15质量％的无机填料形成将浆料造纸，得到绿板，对生坯板进行加压脱水固化硬化，在一个表面上形成由基底增强层，装饰层和表面保护层构成的装饰层。版权所有（C）2010，JPO＆INPIT