1. 发明申请

WO2002101108A1 スチールベルト用複相ステンレス鋼帯审中-公开
标题翻译：钢带双相不锈钢钢带
公开(公告)号：WO2002101108A1
公开(公告)日：2002-12-19
申请号：PCT/JP2002/005572
申请日：2002-06-06
申请人：日新製鋼株式会社 , 冨村宏紀 , 藤本廣 , 森本憲一 , 平松直人
发明人：冨村宏紀 , 藤本廣 , 森本憲一 , 平松直人
IPC分类号： C22C38/00
CPC分类号： C22C38/02 , C21D6/004 , C21D8/0205 , C21D9/52 , C22C38/04 , C22C38/42 , C22C38/44
摘要： A high strength double phase stainless steel strip, wherein it has a chemical composition in mass %: C: 0.04 to 0.15 %, Cr: 10.0 to 20.0 mass %, Ni: 0.5 to 4.0 mass %, and balance: substantially Fe, an old austenite average grain diameter is 10 μm or less, and it has a structure after transformation at an ordinary temperature which contains martensite in an amount of 20 to 85 vol % and ferrite in the balanced amount, and a hardness of HV300 or more. The double phase stainless steel strip can be used for the production of a steel belt excellent in surface characteristics, since the transformation strain associated with martensitic transformation is dispersed uniformly and thus no Luders band is formed during the correction of the shape of a steel belt.
摘要翻译：高强度双相不锈钢带，其具有质量％的化学组成：C：0.04〜0.15％，Cr：10.0〜20.0质量％，Ni：0.5〜4.0质量％，余量：实质上为Fe，旧奥氏体平均粒径为10μm以下，并且在含有20〜85体积％的马氏体和平均量的铁素体，HV300以上的硬度的常温下变形后的结构。双相不锈钢带可用于生产表面特性优异的钢带，因为与马氏体相变相关的变形应变均匀分散，因此在钢带形状校正过程中不会形成泸条带。

2. 发明申请

WO2008111656A1 温水容器およびその製造法审中-公开
标题翻译：热水容器及其生产方法
公开(公告)号：WO2008111656A1
公开(公告)日：2008-09-18
申请号：PCT/JP2008/054678
申请日：2008-03-07
申请人：日新製鋼株式会社 , 足立俊郎 , 野々村明廣 , 山本修 , 冨村宏紀
发明人：足立俊郎 , 野々村明廣 , 山本修 , 冨村宏紀
IPC分类号： B23K9/23 , B23K9/00 , B23K9/167 , C22C38/00 , C22C38/50 , F24H9/00 , B23K101/12 , B23K103/04
CPC分类号： B23K9/0026 , B23K9/028 , B23K9/032 , B23K9/167 , B23K9/23 , B23K2201/12 , B23K2203/02 , B23K2203/05 , C22C38/06 , C22C38/44 , C22C38/48 , C22C38/50 , F24H1/181 , Y10T29/49826
摘要：質量%で、C:0.025%以下、Si:1%以下、Mn:1%以下、P:0.045%以下、S:0.01%以下、Ni:0.1～1%、Cr:21超え～25%、Mo:0.1～2%、Al:0.02～0.3%、N:0.025%以下、Cu:0～1%であり、Ti:0.05～0.4%およびNb:0.05～0.5%の1種以上を含有し、残部Feおよび不可避的不純物である組成の鋼材どうしをバックガスシールなしでTIG溶接することにより形成された裏ビードを容器内面に有し、その溶接裏面の熱影響部において塩化物水溶液に可溶の酸化スケールが形成された部位の鋼素地におけるCr濃度が、鋼素地/酸化スケール界面から10nm以上の深さ領域で16質量%以上である温水容器である。
摘要翻译：由TIG焊接钢构件制成的热水容器，其具有质量含量为C：0.025％以下，Si：1％以下，Mn：1％以下，P：0.045％以下， S：0.01％以下，Ni：0.1〜1％，Cr：21％〜25％，Mo：0.1〜2％，Al：0.02〜0.3％，N：0.025％以下，Cu：0〜1 ％，Ti：0.05〜0.4％，Nb：0.05〜0.5％，余量由Fe和不可避免的杂质组成，无背气密封，内表面具有渗透珠，其中钢基材料的Cr浓度存在于焊接背面侧的热影响区域内形成的可溶于氯化物水溶液中的氧化垢的区域在10nm以上的深度区域中为16质量％以上，钢基材料和氧化垢。

3. 发明申请

WO2002092867A1 成形加工時の形状凍結性に優れたフェライト系ステンレス鋼帯及びその製造方法审中-公开
标题翻译：通过工作形成的冷冻不锈钢不锈钢条纹
公开(公告)号：WO2002092867A1
公开(公告)日：2002-11-21
申请号：PCT/JP2002/004524
申请日：2002-05-09
申请人：日新製鋼株式会社 , 冨村宏紀 , 藤本廣 , 森本憲一 , 國武保利 , 平松直人
发明人：冨村宏紀 , 藤本廣 , 森本憲一 , 國武保利 , 平松直人
IPC分类号： C22C38/00
CPC分类号： C21D8/0205 , C21D8/0226 , C21D8/0263 , C21D8/0405 , C22C38/001 , C22C38/004 , C22C38/18 , C22C38/40
摘要： A ferritic stainless steel strip, which has a chemical composition in mass %: C: 0.10 % or less, Si: 1.0 % or less, Mn: 1.0 % or less, P: 0.050 % or less, S: 0.020 % or less, Ni: 2.0 % or less, Cr: 8.0 to 22.0 %, N: 0.05 % or less, and optionally one or more of Al: 0.10 % or less, Mo: 1.0 % or less, Cu: 1.0 % or less, Ti: 0.01 to 0.50 %, Nb: 0.01 to 0.50 %, V: 0.01 to 0.30 %, Zr: 0.01 to 0.30 % and B: 0.0010 to 0.0100 %, balance: sustantially Fe, with the proviso that the FM value defined by the formula (1): FM = 420C - 11.5Si + 7Mn + 23Ni - 3.5Cr - 12Mo + 9Cu - 49Ti - 50Nb - 23V - 52Al + 470N + 20 ....(1) is 0 or less, and has an in-plane anisotropy (rmax - rmin) of 0.80 or less and a degree of anisotropy of 0.2 % offset yield strength (smax - smin) of 20 N/mm or less; and a method for producing the ferritic stainless steel strip which comprises hot-rolling a ferritic stainless steel having the above composition, and then subjecting the resultant steel to a batch annealing at 700 to 880 DEG C for 1 to 24 hr. The ferritic stainless steel strip is capable of providing a formed product which is reduced in the inferiority of shape such as springback, twist or the like.
摘要翻译：铁素体系不锈钢带，其质量％：C：0.10％以下，Si：1.0％以下，Mn：1.0％以下，P：0.050％以下，S：0.020％以下， Ni：2.0％以下，Cr：8.0〜22.0％，N：0.05％以下，Al：0.10％以下，Mo：1.0％以下，Cu：1.0％以下，Ti： 0.01〜0.50％，Nb：0.01〜0.50％，V：0.01〜0.30％，Zr：0.01〜0.30％，B：0.0010〜0.0100％，余量：维持Fe，条件是式 1）：FM = 420℃-11.5Si + 7Mn + 23Ni-3.5Cr-12Mo + 9Cu-49Ti-50Nb-23V-52Al + 470N + 20 ....（1）为0以下，各向异性（rmax-rmin）为0.80以下，各向异性为0.2％，偏移屈服强度（smax-smin）为20N / mm 2以下; 以及铁素体系不锈钢带的制造方法，其特征在于，对具有上述组成的铁素体系不锈钢进行热轧，然后对所得到的钢进行700〜880℃的间歇退火处理1〜24小时。铁素体不锈钢带能够提供成形产品，其形状减小，例如回弹，扭曲等。

4. 发明申请

WO2008120409A1 溶接構造温水容器用フェライト系ステンレス鋼および温水容器审中-公开
标题翻译：具有焊接结构的温水船用无机不锈钢和温水船
公开(公告)号：WO2008120409A1
公开(公告)日：2008-10-09
申请号：PCT/JP2007/069324
申请日：2007-09-26
申请人：日新製鋼株式会社 , 足立俊郎 , 野々村明廣 , 山本修 , 冨村宏紀
发明人：足立俊郎 , 野々村明廣 , 山本修 , 冨村宏紀
IPC分类号： C22C38/00 , C22C38/28 , C22C38/50 , F24H9/00 , C21D9/46
CPC分类号： F24H1/181 , C21D9/46 , C22C38/02 , C22C38/04 , C22C38/06 , C22C38/26 , C22C38/28 , F24H9/0047
摘要：質量%で、C:0.02%以下、Si:0.01～0.30%、Mn:1%以下、P:0.04%以下、S:0.03%以下、Cr:21超え～26%、Mo:2%以下、Nb:0.05～0.6%、Ti:0.05～0.4%、N:0.025%以下、Al:0.02～0.3%であり、さらに必要に応じてNi:2%以下好ましくは0.1～2%およびCu:1%以下好ましくは0.1～1%の1種以上を含み、残部Feおよび不可避的不純物からなる、溶接構造温水容器用フェライト系ステンレス鋼である。
摘要翻译：本发明提供一种用于具有焊接结构的温水容器的铁素体不锈钢，其质量为C：不大于0.02％，Si：0.01至0.30％，Mn：不大于1％，P：不大于 0.04％以上，S：0.03％以下，Cr：21〜26％，Mo：2％以下，Nb：0.05〜0.6％，Ti：0.05〜0.4％，N：0.025％，Al：0.02〜0.3％，进一步任选地包含Ni：不大于2％，优选0.1〜2％，Cu：1％以下，优选0.1〜1％的一种以上，余量由Fe 和不可避免的杂质。

5. 发明申请

WO2002085548A1 ステンレス鋼製無段変速機用ベルトの製造方法审中-公开
标题翻译：不锈钢连续可变传动带的生产方法
公开(公告)号：WO2002085548A1
公开(公告)日：2002-10-31
申请号：PCT/JP2002/002742
申请日：2002-03-22
申请人：日新製鋼株式会社 , 西尾克秀 , 榊正仁 , 馬越義幸 , 原健治 , 冨村宏紀
发明人：西尾克秀 , 榊正仁 , 馬越義幸 , 原健治 , 冨村宏紀
IPC分类号： B21B5/00
CPC分类号： B21B5/00 , B21B3/02 , B21B37/74 , B21B45/004
摘要： At the time of ring rolling a metastable austenite based stainless steel band having an Md(N) value dependent on the component/composition in the range of 20-100, the following relation is satisfied among the material temperature T, the equivalent distortion e, and the Md(N) value; -0.3913T+0.5650Md(N)+60.46 epsilon >/=65.87. A belt for a stainless steel continuously variable transmission exhibiting fatigue characteristics comparable to those of 18Ni maraging steel is produced by controlling the rolling conditions. The Md(N) value is defined by a formula Md(N)=580-520C-2S-16Mn-16Cr-23Ni-300N-10Mo, and the equivalent distortion e is defined by a formula epsilon =[ OR 4(1-R)) /3], (R: draft). Furthermore, quality and shape of a metal belt are stabilized when the variation DELTA T of material temperature is confined within a range of +/-6.4 DEG C.
摘要翻译：在环形轧制中，具有取决于组分/组成的Md（N）值在20-100的亚稳态奥氏体不锈钢带的材料温度T，等效变形e，和Md（N）值; -0.3913T + 0.5650Md（N）+60.46εε= 65.87。通过控制轧制条件，制造出具有与18Ni马氏体时效钢相当的疲劳特性的不锈钢无级变速器传动带。 Md（N）值由公式Md（N）= 580-520C-2S-16Mn-16Cr-23Ni-300N-10Mo定义，等效变形e由公式ε= [OR 4（1- R））2）/ 3]，（R：吃水）。此外，当材料温度的变化量DELTA T限制在+/- 6.4℃的范围内时，金属带的质量和形状是稳定的。