1. 发明专利

JP2011020157A Sheet material for brazing, sheet constituting body for brazing, composition for brazing, brazing method and heat exchanger made of stainless steel 有权
标题翻译：用于制动的片材，用于制动的组织物，用于制动的组合物，不锈钢的制动方法和热交换器
公开(公告)号：JP2011020157A
公开(公告)日：2011-02-03
申请号：JP2009168613
申请日：2009-07-17
申请人： Denso Corp , Harima Chemicals Inc , ハリマ化成株式会社 , 株式会社デンソー
发明人： TATE KOICHI , TAKAHASHI MASASHI , KONDO YUTA , OGURA ATSUHIRO , AKAZAWA TOMOAKI , YANAKA ICHIRO
IPC分类号： B23K35/14 , B22F1/00 , B23K1/00 , B23K35/30 , B23K35/363 , B23K35/40 , B23K101/14 , B23K103/04 , C22C19/05
摘要： PROBLEM TO BE SOLVED: To provide a sheet material for brazing, a brazing method using the sheet material for brazing, and the like by which a required amount of brazing filler metal can be correctly fed to a portion to be subjected to brazing when the brazing is performed by using a brazing filler metal containing nickel based alloy powder, and also the fed brazing filler metal is detained at the portion to suppress displacement or the like. SOLUTION: In the sheet material 1 for brazing comprising nickel based alloy powder of 50 to 90 mass% and a binder resin of 10 to 50 mass%, the binder resin is obtained by cross-linking an acrylic resin with a hydroxyl group having a glass transition temperature of ≤0°C and a weight average molecular weight of ≥100,000 with a crosslinking agent. COPYRIGHT: (C)2011,JPO&INPIT
摘要翻译：要解决的问题：为了提供钎焊用片材，使用钎焊用片材的钎焊方法等，能够将所需量的钎料可以正确地供给到要进行钎焊的部分当通过使用含有镍基合金粉末的钎料进行钎焊时，还将该供给的钎料扣在该部分以抑制位移等。解决方案：在含有50-90质量％的镍基合金粉末和10至50质量％的粘合剂树脂的钎焊用片材1中，通过将丙烯酸树脂与羟基交联而得到粘合剂树脂具有玻璃化转变温度≤0℃，重均分子量≥100,000的交联剂。版权所有（C）2011，JPO＆INPIT

2. 发明专利

JP2014097514A PASTE FOR Al-Cu BRAZING AND Al-Cu BRAZING METHOD 有权
标题翻译：用于Al-Cu烧结和Al-Cu烧结方法
公开(公告)号：JP2014097514A
公开(公告)日：2014-05-29
申请号：JP2012249586
申请日：2012-11-13
申请人： Harima Chemicals Inc , ハリマ化成株式会社 , Denso Corp , 株式会社デンソー , Uacj Corp , 株式会社Uacj
发明人： OGURA ATSUHIRO , AKAZAWA TOMOAKI , MORIMOTO MASAKAZU , IGUCHI TAKESHI , TEJIMA KIYOHIDE , MURASE TAKASHI , KITAWAKI KOTARO
IPC分类号： B23K35/22 , B23K1/19 , B23K3/06 , B23K35/28 , B23K35/363 , B23K103/18 , C22C21/00
摘要： PROBLEM TO BE SOLVED: To provide a paste for Al-Cu brazing which can satisfactorily join aluminum or an alloy thereof and copper or an alloy thereof, and is excellent in storage stability and productivity, and to provide an Al-Cu brazing method using the paste for Al-Cu brazing.SOLUTION: In a paste for Al-Cu brazing, (a) an Al-Cu-Si-Zn-based alloy, (b) Cs-Al-F compound-based flux, (c) a binder formed of a butyl rubber and/or a methacrylic resin, and (d) a hydrocarbon organic solvent are contained. The content ratio of (a) is 40 to 80 pts.mass. and the content ratio of (b) is 20 to 60 pts.mass. with respect to 100 pts.mass of the total of (a) and (b). The content ratio of (c) is 0.1 to 10 pts.mass. with respect to 100 pts.mass of the total of (a), (b), and (c). The viscosity at 25°C which is measured by a spiral pump type viscometer (stirring speed of 10 rpm and amount of measured sample of 150 mL) is 1 to 300 Pa s.
摘要翻译：要解决的问题：为了提供可以令人满意地接合铝或其合金以及铜或其合金的Al-Cu钎焊的糊料，并且保存稳定性和生产率优异，并且提供使用（a）Al-Cu-Si-Zn基合金，（b）Cs-Al-F化合物基助熔剂，（c）a-Cu钎料由丁基橡胶和/或甲基丙烯酸树脂形成的粘合剂和（d）烃有机溶剂。（a）的含量比为40〜80份。（b）的含量比为20〜60pts.mass。相对于（a）和（b）的总共100个点。（c）的含量比为0.1〜10磅。相对于（a），（b）和（c）的总共100个点。通过螺旋泵式粘度计（搅拌速度10rpm，测定样品量150mL）测定的25℃下的粘度为1〜300Pa·s。

3. 发明专利

JP2014237145A ろう付け用ペースト有权
标题翻译：搅拌浆
公开(公告)号：JP2014237145A
公开(公告)日：2014-12-18
申请号：JP2013119925
申请日：2013-06-06
申请人：ハリマ化成株式会社 , Harima Chemicals Inc , 株式会社デンソー , Denso Corp
发明人： OGURA ATSUHIRO , MORIMOTO MASAKAZU , SODA MASAHIRO , IGUCHI TAKESHI
IPC分类号： B23K35/22 , B23K35/363
摘要：【課題】ろう付け性に優れるろう付け用ペーストを提供すること。【解決手段】金属粉末、フラックス、バインダおよび溶剤を含むろう付け用ペーストにおいて、フラックスに、Cs−Al−F系フラックスとK−Al−F系フラックスとを、それらの総量100質量部に対してCs−Al−F系フラックスが20質量部以上(但し、100質量部を除く)になるように含有させ、さらに、窒素雰囲気下、昇温速度20℃/分にて測定される示差熱分析曲線(DTA曲線)において、金属粉末の融点を含む吸熱ピークの温度領域の少なくとも一部と、フラックスの融点を含む吸熱ピークの温度領域の少なくとも一部とが重複するように、金属粉末およびフラックスを選択して用いる。【選択図】なし
摘要翻译：要解决的问题：提供钎焊性优异的钎焊膏。解决方案：钎焊膏包括金属粉末，焊剂，粘合剂和溶剂。磁通量包括基于Cs-Al-F的焊剂和K-Al-F基焊剂，使得Cs-Al-F基焊剂相对于100质量份的焊剂包含20质量份以上（除了100质量份）他们的总金额。选择并使用金属粉末和助熔剂，使得至少部分包含金属粉末的熔点的热吸附峰的温度区域和包含熔点的热吸附峰的温度区域的至少一部分在氮气气氛下以20℃/分钟的编程速率在差热分析曲线（DTA曲线）中重叠通量。

4. 发明专利

JP2014184476A Composition for brazing and heat exchanger 有权
标题翻译：制冷和热交换器组成
公开(公告)号：JP2014184476A
公开(公告)日：2014-10-02
申请号：JP2013062373
申请日：2013-03-25
申请人： Harima Chemicals Inc , ハリマ化成株式会社 , Denso Corp , 株式会社デンソー
发明人： OGURA ATSUHIRO , YAMADA SHOGO , TEJIMA KIYOHIDE , TACHI KOICHI
IPC分类号： B23K35/363 , B23K35/30 , C22C19/05 , F28F9/18
摘要： PROBLEM TO BE SOLVED: To provide: a composition for brazing which enables stainless steel to be excellently brazed at a relatively low temperature under an inert atmosphere (under an inert gas atmosphere or under a vacuum), and furthermore is excellent in application work efficiency, adhesion and storage stability; and a heat exchanger obtained by using the composition for brazing.SOLUTION: The composition for brazing used for brazing the stainless steel under the inert atmosphere contains (a) Ni-Cr-Si-P-based nickel brazing material powder, (b) butyl rubber, (c) a hydrocarbon -based organic solvent and (d) hardened castor oil, a blending rate of (b) the butyl rubber is set to 0.5 pts.mass-1.0 pts.mass, and a blending rate of (d) the hardened castor oil is set to 0.05 pts.mass-1.0 pts.mass, to 100 pts.mass of the composition for brazing.
摘要翻译：要解决的问题：提供：一种用于钎焊的组合物，其使得不锈钢在惰性气氛（在惰性气体气氛或真空下）下在相对低的温度下被优良地钎焊，并且还具有优异的施加工作效率，粘附和储存稳定性; 以及使用该组合物进行钎焊而得到的热交换器。溶液：用于在惰性气氛下钎焊不锈钢的钎焊用组合物含有（a）Ni-Cr-Si-P系镍钎焊材料粉末，（b）橡胶，（c）烃基有机溶剂和（d）硬化蓖麻油，（b）丁基橡胶的配合速率设定为0.5pts.mass-1.0pts.mass，并且（d）硬化的蓖麻油被设定为0.05pts.mass-1.0pts.mass，至100pts.mass的组合物用于钎焊。

5. 发明专利

JP2011131247A Composition for brazing aluminum 有权
标题翻译：烧结铝组合物
公开(公告)号：JP2011131247A
公开(公告)日：2011-07-07
申请号：JP2009293456
申请日：2009-12-24
申请人： Harima Chemicals Inc , ハリマ化成株式会社
发明人： OTA YASUO , OGURA ATSUHIRO
IPC分类号： B23K35/363 , B23K1/19 , B23K35/22 , B23K101/14 , B23K103/10
摘要： PROBLEM TO BE SOLVED: To ensure the excellent appearance of the composition for aqueous aluminum brazing after the brazing without impairing the solubility in water during the saponification.
SOLUTION: The composition for the aqueous aluminum brazing contains (A) water-soluble saponified substance of methacrylic ester-based polymer, (B) non-reactive flux, (C) water-soluble alcohol, and (D) water. The acid value of the polymer (A) is 1-19. The content (in terms of solid content) of the component (A) is 3-15 wt.%, and that of the component (B) is 25-50 wt.%, that of the component (C) is 35-55 wt.%, and that of the component (D) is 5-15 wt.%. In order to adjust the blending ratio of water-soluble alcohol to be higher while setting the acid value of a binder resin to be lower, water solubility after the saponification is guaranteed, and the appearance after the brazing is ensured.
COPYRIGHT: (C)2011,JPO&INPIT
摘要翻译：要解决的问题：为了确保钎焊后的铝水硬化组合物的优异外观，而不损害在皂化期间在水中的溶解度。水溶性铝钎焊用组合物含有（A）甲基丙烯酸酯类聚合物的水溶性皂化物，（B）无反应性助熔剂，（C）水溶性醇和（D）水。聚合物（A）的酸值为1-19。组分（A）的含量（以固体含量计）为3-15重量％，组分（B）的含量为25-50重量％，组分（C）的含量为35-55 重量％，组分（D）的重量百分比为5-15％（重量）。为了在将粘合剂树脂的酸值设定得较低的同时将水溶性醇的配合比例调整为更高，可以确保皂化后的水溶性，并确保钎焊后的外观。版权所有（C）2011，JPO＆INPIT

6. 发明专利

JP2012024788A Manufacturing method for aluminum brazing composition and brazing method for inner fin tube 有权
标题翻译：铝管制造铝合金制造方法及制造方法
公开(公告)号：JP2012024788A
公开(公告)日：2012-02-09
申请号：JP2010163927
申请日：2010-07-21
申请人： Harima Chemicals Inc , ハリマ化成株式会社
发明人： OGURA ATSUHIRO , OTA YASUO , AKAZAWA TOMOAKI
IPC分类号： B23K35/40 , B23K1/00 , B23K1/19 , B23K35/363 , B23K101/14 , B23K103/10 , F28F1/40
摘要： PROBLEM TO BE SOLVED: To improve adherence to an aluminum member while suppressing a binder amount and securing a brazing property.SOLUTION: The manufacturing method for an aluminum brazing composition uses a roll mill to knead a brazing composition of aluminum or an aluminum alloy containing a (meth)acrylic resin binder (A), a fluoride-based flux (B), and an organic solvent (C), wherein the content (in equivalent solid gradient) of the gradient (A) in the brazing composition is 1 to 20 wt.% with respect to the total amount of the gradients (A), (B). The roll mill is applied to the brazing composition for kneading, so that the composition is sufficiently dispersed with the flux even if the binder amount is suppressed, adherence to the aluminum member can be improved while securing the brazing property, and the composition is particularly suitable for inner brazing of an inner fin tube.
摘要翻译：要解决的问题：为了提高对铝构件的附着性，同时抑制粘结剂量并确保钎焊性能。解决方案：铝钎焊组合物的制造方法使用辊磨机来捏合含有（甲基）丙烯酸树脂粘合剂（A），氟化物系焊剂（B）和铝（A）的铝合金的钎焊组合物，有机溶剂（C），其中钎焊组合物中梯度（A）的含量（以等效的固体梯度）相对于梯度（A），（B）的总量为1〜20重量％。将该辊磨机施加到用于捏合的钎焊组合物上，使得即使粘合剂量被抑制，组合物也充分地与助熔剂分散，同时确保钎焊性能可以提高对铝构件的粘合性，并且该组合物特别合适用于内翅片管的内部钎焊。版权所有（C）2012，JPO＆INPIT