1. 发明专利

JP2011202033A Coating composition, method for producing film using the same, and coated body using the same 有权
标题翻译：涂料组合物，使用其制造膜的方法和使用其的包衣体
公开(公告)号：JP2011202033A
公开(公告)日：2011-10-13
申请号：JP2010071130
申请日：2010-03-25
申请人： Du Pont Mitsui Fluorochem Co Ltd , Nippon Futsuso Kogyo Kk , 三井・デュポンフロロケミカル株式会社 , 日本フッソ工業株式会社
发明人： FUKUMURA NAOKI , TAKEYAMA MASAHIRO , NAKAZAWA RYO
IPC分类号： C09D127/12 , B05D7/24 , C09D5/00 , C09D7/12 , C09D143/02
摘要： PROBLEM TO BE SOLVED: To provide a primer composition containing chromium-free fluororesin, which can provide a coated body having excellent higher anti-corrosiveness by providing a fluororesin film and a primer layer having sufficient adhesive strength together with the fluororesin film to the surface of a base material such as metal, glass, ceramic, and heat resistant plastic, and to provide a method for producing a film using the primer composition, and a coated body using the primer composition.SOLUTION: A coating composition is provided, which contains fluororesin the melt flow rate (MFR) of which measured at 372°C under a load of 5 kg on the basis of ASTM D1238 is 10-100 g/10 min and organic titanate, wherein the titanium content of the organic titanate with respect to the fluororesin is 1-40 wt.%. There are also provided a method for producing a film using the coating composition, and a coated body using the coating composition.
摘要翻译：要解决的问题：提供含有无铬氟树脂的底漆组合物，其可以通过将氟树脂膜和具有足够粘合强度的底漆层与氟树脂膜一起提供给具有优异的较高抗腐蚀性的涂层体，基材，例如金属，玻璃，陶瓷和耐热塑料，并提供使用底漆组合物制备薄膜的方法和使用底漆组合物的涂布体。溶液：提供含有氟树脂的涂料组合物在372℃，基于ASTM D1238的5kg载荷下测量的熔体流动速率（MFR）为10-100g / 10min，有机钛酸盐，其中钛酸酯相对于氟树脂为1-40重量％。还提供了使用该涂料组合物制备薄膜的方法和使用该涂料组合物的涂布体。

2. 发明专利

JP2011202034A Coating composition, method for producing film using the same, and coated body using the same 有权
标题翻译：涂料组合物，使用其制造膜的方法和使用其的包衣体
公开(公告)号：JP2011202034A
公开(公告)日：2011-10-13
申请号：JP2010071131
申请日：2010-03-25
申请人： Du Pont Mitsui Fluorochem Co Ltd , Nippon Futsuso Kogyo Kk , 三井・デュポンフロロケミカル株式会社 , 日本フッソ工業株式会社
发明人： FUKUMURA NAOKI , TAKEYAMA MASAHIRO , NAKAZAWA RYO
IPC分类号： C09D127/12 , B05D7/24 , C09D5/00 , C09D127/18 , C09D181/04 , C09D185/00
摘要： PROBLEM TO BE SOLVED: To provide a primer composition containing chromium-free fluororesin, which can provide a coated body having excellent higher anti-corrosiveness by providing a fluororesin film and a primer layer having sufficient adhesive strength together with the fluororesin film to the surface of a base material such as metal, glass, ceramic, and heat resistant plastic, and to provide a method for producing a film using the primer composition, and a coated body using the primer composition.SOLUTION: A coating composition is provided, which contains fluororesin containing a reactive functional group and organic titanate, wherein the titanium content of the organic titanate with respect to the fluororesin is 1-40 wt.%. There are also provided a method for producing a film using the coating composition, and a coated body using the coating composition.
摘要翻译：要解决的问题：提供含有无铬氟树脂的底漆组合物，其可以通过将氟树脂膜和具有足够粘合强度的底漆层与氟树脂膜一起提供给具有优异的较高抗腐蚀性的涂层体，基材，例如金属，玻璃，陶瓷和耐热塑料，并提供使用底漆组合物制备薄膜的方法和使用底漆组合物的涂布体。溶液：提供含有氟树脂的涂料组合物含有反应性官能团和有机钛酸酯，其中有机钛酸酯相对于氟树脂的钛含量为1-40重量％。还提供了使用该涂料组合物制备薄膜的方法和使用该涂料组合物的涂布体。

3. 发明专利

JP2011116075A Fluororesin laminate having high friction abrasion resistance 有权
标题翻译：具有高摩擦耐磨性的氟橡胶层压板
公开(公告)号：JP2011116075A
公开(公告)日：2011-06-16
申请号：JP2009277527
申请日：2009-12-07
申请人： Du Pont Mitsui Fluorochem Co Ltd , 三井・デュポンフロロケミカル株式会社
发明人： MATSUDA HARUNA , TAKEYAMA MASAHIRO
IPC分类号： B32B27/20 , A47J36/04 , B32B27/30
摘要： PROBLEM TO BE SOLVED: To provide a fluororesin laminate having non-adhesiveness, corrosion resistance and steam resistance of the fluororesin laminate, suppressing lowering of the friction abrasion resistance by preventing separation of a hard filler while keeping adhesiveness to a metal base material, and having inexpensive and higher friction abrasion resistance.
SOLUTION: The fluororesin laminate is composed of at least three layers of a primer layer formed on the base material, an intermediate layer formed on the primer layer, and a top coat layer formed on the intermediate layer. The intermediate layer and top coat layer contain the hard filler with at least one kind of new Mohs hardness of 10 or more, respectively, and any hard filler contained in the top coat layer preferably has an average particle size smaller than that of any hard filler contained in the intermediate layer.
COPYRIGHT: (C)2011,JPO&INPIT
摘要翻译：解决问题的方案：为了提供氟树脂层压体的非粘合性，耐腐蚀性和耐蒸汽性的氟树脂层压体，通过防止硬质填料的分离同时保持与金属基材的粘合性来抑制摩擦耐磨性的降低并且具有廉价和更高的摩擦耐磨性。解决方案：氟树脂层压体由至少三层形成在基材上的底漆层，形成在底漆层上的中间层和形成在中间层上的顶涂层组成。中间层和顶涂层分别含有至少一种新的莫氏硬度为10以上的硬质填料，并且顶涂层中所含的任何硬质填料的平均粒径优选小于任何硬质填料的平均粒径包含在中间层中。版权所有（C）2011，JPO＆INPIT