1. 发明授权

US5030297A Process for the manufacture of seamless pressure vessels and its named product 失效
标题翻译：制造无缝压力容器及其产品的方法
公开(公告)号：US5030297A
公开(公告)日：1991-07-09
申请号：US429215
申请日：1989-10-30
申请人： Dieter Vespermann , Bernhard Hoffmann , Heinz Muller , Ingo Von Hagen
发明人： Dieter Vespermann , Bernhard Hoffmann , Heinz Muller , Ingo Von Hagen
IPC分类号： C21D8/10 , C21D9/14 , C22C38/00 , C22C38/32
CPC分类号： C21D8/10 , C21D9/14 , C22C38/001 , C22C38/32
摘要： A process for the manufacture of a seamless pressure vessel and the seamless pressure vessel produced thereby, the process including the steps of employing an aluminum-killed CrMo steel which includes by wt. %: 0.28-0.39% C; 0.15-0.40% Si; 0.45-0.90% Mn; max. 0.02% P; max. 0.005% S; 0.90-1.30% Cr; 0.15-0.35% Mo; 0.0010-0.040% Ti; 0.001-0.003% B; and 0.003-0.010% N; hot working the alumninum-killed CrMo Steel to produce the seamless pressure vessel, austenizing the seamless pressure vessel at a temperature between about 830.degree. C. and about 880.degree. C.; cooling the seamless pressure vessel at a cooling rate of between about 5.degree. K/s and about 15.degree. K/s; and tempering the seamless pressure vessel at a temperature between about 510.degree. C. and about 660.degree. C.
摘要翻译：一种用于制造无缝压力容器的方法和由此制备的无缝压力容器，所述方法包括以下步骤：使用铝 - 杀死的CrMo钢，其包括wt。％：0.28-0.39％C; 0.15-0.40％Si; 0.45-0.90％Mn; 最大 0.02％P; 最大 0.005％S; 0.90-1.30％Cr; 0.15-0.35％Mo; 0.0010-0.040％Ti; 0.001-0.003％B; 和0.003-0.010％N; 热处理冲压的CrMo钢生产无缝压力容器，在约830℃至约880℃的温度下对无缝压力容器进行奥氏体化处理。以约5°K / s至约15°K / s的冷却速率冷却无缝压力容器; 并在约510℃至约660℃的温度下回火无缝压力容器。

2. 发明授权

US6095232A Process and device for producing metallic composite materials 失效
标题翻译：生产金属复合材料的工艺和装置
公开(公告)号：US6095232A
公开(公告)日：2000-08-01
申请号：US945468
申请日：1998-02-06
申请人： Tarek El Gammal , Gamal Mohamed Megahed , Fritz-Peter Pleschuitschnigg , Ingo Von Hagen
发明人： Tarek El Gammal , Gamal Mohamed Megahed , Fritz-Peter Pleschuitschnigg , Ingo Von Hagen
IPC分类号： B22D19/00 , B22D11/00 , B22D23/04 , B32B37/24 , C23C2/00
CPC分类号： B32B37/24 , B22D11/008 , C23C2/006 , B32B2309/62 , B32B2311/00
摘要： The invention is directed to a process for producing metallic composite material in which there is applied to at least one side of a parent strand a material having different material characteristics. For this purpose, according to the invention, the parent strand is guided through a melt having the same material composition as the parent strand, wherein melt crystallizes on by inversion casting and, at a predefinable distance from the surface of the molten bath, a composite section is fed to the carrier section after it has exited from the molten bath, this composite section being welded with the surface of the carrier section. The invention is further directed to a device for carrying out the process.
摘要翻译： PCT No.PCT / DE96 / 00907 Sec。 371日期1998年2月8日 102（e）1998年2月8日PCT PCT 1996年5月17日PCT公布。公开号WO96 / 36744 日期1996年11月21日本发明涉及一种生产金属复合材料的方法，其中在母线的至少一侧应用具有不同材料特性的材料。为此，根据本发明，母链通过具有与母线相同的材料成分的熔体引导，其中熔融物通过反转铸造结晶，并且在与熔融浴表面的预定距离处，复合材料在从熔融液体中排出之后，将该部分供给到载体部分，该复合部分与载体部分的表面焊接。本发明进一步涉及用于执行该过程的装置。

3. 发明授权

US06435218B2 Pipe with crack stopper feature, and process of protecting a pipe against propagation of cracks 失效
标题翻译：具有裂缝阻塞特征的管道，以及保护管道免受裂缝扩散的过程
公开(公告)号：US06435218B2
公开(公告)日：2002-08-20
申请号：US09782217
申请日：2001-02-13
申请人： Hans-Georg Hillenbrand , Ingo Von Hagen , Gerd Junker , Gerhard Knauf , Johannes Arndt
发明人： Hans-Georg Hillenbrand , Ingo Von Hagen , Gerd Junker , Gerhard Knauf , Johannes Arndt
IPC分类号： F16L914
CPC分类号： F16L58/1054 , F16L57/02 , Y10S138/02
摘要： A steel pipe, includes an outer corrosive-preventive protective sheath, which has a surface layer of plastic material, and a crack stopper zone extending over a section of the pipe. The crack stopper zone includes a bandage which is wrapped around the pipe section and made of high-strength fiber material imbedded in a compacted matrix of thermoplastic and thermosetting plastic. The bandage is comprised of a plurality of wound layers joined to one another via the matrix by welding or gluing.
摘要翻译：钢管包括外部防腐保护护套，其具有塑料材料的表面层，以及在管道的一部分上延伸的裂纹阻挡区域。裂缝停止区包括绷带，其缠绕在管段上并由嵌入在热塑性和热固性塑料的压实基质中的高强度纤维材料制成。该绷带由通过焊接或胶合经由基体彼此连接的多个缠绕层组成。

4. 发明授权

US06153028A Process and device for producing thin metal bars 失效
标题翻译：生产薄金属棒的工艺和装置
公开(公告)号：US06153028A
公开(公告)日：2000-11-28
申请号：US249905
申请日：1999-02-12
申请人： Fritz-Peter Pleschiutschnigg , Ingo Von Hagen , Markus Ring , Wolfgang Bleck , Tarek El Gammal , Paul Splinter , Peter Lorenz Hamacher , Oliver Richard Picht
发明人： Fritz-Peter Pleschiutschnigg , Ingo Von Hagen , Markus Ring , Wolfgang Bleck , Tarek El Gammal , Paul Splinter , Peter Lorenz Hamacher , Oliver Richard Picht
IPC分类号： B21B1/22 , B21B1/38 , B21B1/46 , B21B3/02 , B21B9/00 , B21B39/18 , B22D11/00 , C23C2/00 , B22D23/04
CPC分类号： C23C2/006 , B21B1/463 , B22D11/008 , B21B2001/228 , B21B2001/383 , B21B3/02 , B21B39/18 , B21B9/00 , Y10T428/12493
摘要： A device and a process for producing thin steel metal bars in which an elongated metal product is brought into contact with a molten metal causing the latter to crystallize. Different materials are used for the elongated metal product and the molten metal, whereby one of the materials is a stainless steel. A temperature of the elongated metal product, a temperature of the molten metal and a dwelling time of the elongated metal product in the molten metal are set in such a way that the molten metal crystallizes on the elongated metal product so as to form a layer having a thickness of 2% to 20% of a thickness of the elongated metal product.
摘要翻译：一种用于生产细钢金属棒的装置和方法，其中细长金属制品与熔融金属接触，导致其结晶。不同的材料用于细长金属产品和熔融金属，其中一种材料是不锈钢。细长金属制品的温度，熔融金属的温度和细长金属产品在熔融金属中的停留时间被设定为使得熔融金属在细长金属产品上结晶，从而形成具有厚度为细长金属制品厚度的2％至20％。

5. 发明授权

US5462615A Weldable high-strength structural steel with 13% chromium 失效
标题翻译： 13％铬的可焊接高强度结构钢
公开(公告)号：US5462615A
公开(公告)日：1995-10-31
申请号：US244334
申请日：1994-07-25
申请人： Ingo Von Hagen , Rolf Popperling , Hubertus Schlerkmann , Ulrike Zeislmair
发明人： Ingo Von Hagen , Rolf Popperling , Hubertus Schlerkmann , Ulrike Zeislmair
IPC分类号： C21D8/02 , C21D8/10 , C22C38/00 , C22C38/22 , C22C38/26 , C22C38/40 , C22C38/48
CPC分类号： C22C38/22 , C22C38/26
摘要： Disclosed is a process for producing seamless steel pipes or flat products (strip or sheet) for pipes or vessels which are intended for the conveyance, transport or processing of gaseous or liquid hydrocarbons containing CO.sub.2 and water and possibly small proportions of H.sub.2 S and are resistant to stress crack corrosion and have good welding properties at the same time and a 0.2-percent elongation limit of at least 450 N/mm.sup.2. The process uses a nickel-containing steel of the following composition (percent by weight): min. 0.015% C, 0.15-0.50% Si, max. 2.00% Mn, max. 0.020% P, max. 0.003% S, 12.0-13.8% Cr, 0.002-0.02% N, 0.01-0.05% Nb, remainder iron and usual impurities. It is presently suggested that the nickel content is limited to a maximum of 0.25%, the manganese content amounts to at least 1.0%, the carbon content is limited to 0.035%, and 0.01 to 1.2% molybdenum is contained as additional alloying component.
摘要翻译： PCT No.PCT / DE92 / 00987。 371日期：1994年7月25日 102（e）日期1994年7月25日PCT提交1992年11月23日PCT公布。出版物WO93 / 11270 日期1993年6月10日。公开是生产用于管道或容器的无缝钢管或扁平产品（带或片）的方法，用于运输，运输或加工含有二氧化碳和水的气态或液态烃，可能小 H2S的比例并且耐应力裂纹腐蚀并且同时具有良好的焊接性能以及至少为450N / mm 2的0.2％伸长极限。该方法使用以下组成的含镍钢（重量百分比）：分钟。 0.015％C，0.15-0.50％Si，最大。 2.00％Mn，最大 0.020％P，最大 0.003％S，12.0-13.8％Cr，0.002-0.02％N，0.01-0.05％Nb，余量为铁和常规杂质。目前建议将镍含量限制在最大0.25％，锰含量至少为1.0％，碳含量限制在0.035％，而作为附加合金成分含有0.01〜1.2％的钼。

6. 发明授权

US5992501A Floor lead-through element for an inversion casting vessel 失效
标题翻译：用于反转铸造容器的地板穿通元件
公开(公告)号：US5992501A
公开(公告)日：1999-11-30
申请号：US913181
申请日：1997-10-14
申请人： Tarek El Gammal , Peter Hamacher , Michael Vonderbank , Fritz-Peter Pleschiutschnigg , Ingo Von Hagen
发明人： Tarek El Gammal , Peter Hamacher , Michael Vonderbank , Fritz-Peter Pleschiutschnigg , Ingo Von Hagen
IPC分类号： B22D11/00 , B22D11/04 , B22D11/10 , B22D11/124 , C23C2/00 , B22D19/00 , B22D23/04
CPC分类号： C23C2/006 , B22D11/008
摘要： An inversion casting vessel includes a melt-filled container with a hole in the floor through which a metal strip is drawn. As the strip is drawn through the container, crystallization of the melt on the metal strip occurs, thereby forming a metal strand. The hole in the floor is a slit shaped channel through which the strip is run in a low-contact manner. The container also includes a cooling device for cooling the melt in the area of the slit shaped channel. The cooling device maintains the temperature of the melt around the channel to create a two-phase field of the melt, one of the phases being crystal, making up 50%-90% of the two phase field. The metal strip first contacts the melt at the two-phase field of the melt as the strip is run through the melt container.
摘要翻译： PCT No.PCT / DE96 / 00256 Sec。 371日期1997年10月14日第 102（e）日期1997年10月14日PCT PCT 1996年2月7日PCT公布。 WO96 / 27465 PCT公开号日期1996年9月12日反转铸造容器包括在地板中具有孔的熔融填充的容器，通过该容器拉出金属带。当条带被拉过容器时，金属条上的熔体结晶发生，从而形成金属线。地板上的孔是一个狭缝形通道，条带以低接触方式运行。容器还包括用于在狭缝形通道的区域中冷却熔体的冷却装置。冷却装置保持熔体在通道周围的温度以产生熔体的两相场，其中一相是晶体，构成两相场的50％-90％。当条带穿过熔体容器时，金属条首先在熔体的两相场处接触熔体。

7. 发明授权

US5855238A Process and device for the continuous production of sheet metal strips 失效
标题翻译：用于连续生产钣金带的工艺和装置
公开(公告)号：US5855238A
公开(公告)日：1999-01-05
申请号：US894466
申请日：1997-11-07
申请人： Fritz-Peter Pleschiutschnigg , Ingo Von Hagen
发明人： Fritz-Peter Pleschiutschnigg , Ingo Von Hagen
IPC分类号： B22D11/06 , B22D11/00 , B22D11/04 , B22D11/10 , B22D19/00 , B22D23/04 , C23C2/00
CPC分类号： B22D11/008 , C23C2/006
摘要： A mother strip with a metallically pure surface is passed through a melt bath of a metal and whereby the coating is smoothed by rolling immediately after leaving the melt bath. The mother strip, having been preheated, to a temperature clearly above ambient temperature, especially above 200.degree. C., is introduced into the metal bath. The preheating is carried out by indirect heat exchange with the melt bath in an oxygen-free environment. The melt freshly supplied to the melt bath has an increased temperature in accordance with the heat lost due to preheating.
摘要翻译： PCT No.PCT / DE96 / 00210 Sec。 371日期：1997年11月7日 102（e）日期1997年11月7日PCT提交1996年2月5日PCT公布。出版物WO96 / 27464 PCT 日期1996年9月12日具有金属纯净表面的母带通过金属熔融浴，从而通过在离开熔融浴后立即滚压使涂层平滑。将预热的母带导入明显高于环境温度，特别是高于200℃的温度，引入金属浴中。预热通过在无氧环境中与熔融液体的间接热交换进行。根据预热引起的热损失，新鲜地供应到熔池的熔体具有升高的温度。

8. 发明授权

US5573605A High-temperature steel for boiler making 失效
标题翻译：锅炉制造高温钢
公开(公告)号：US5573605A
公开(公告)日：1996-11-12
申请号：US399857
申请日：1995-03-07
申请人： Walter Bendick , Klaus Haarmann , Ingo Von Hagen
发明人： Walter Bendick , Klaus Haarmann , Ingo Von Hagen
IPC分类号： C22C38/22 , C22C38/24 , C22C38/28 , C22C38/32
CPC分类号： C22C38/32 , C22C38/22 , C22C38/24 , C22C38/28
摘要： A high-temperature steel for boiler making having improved creep strength and low tendency to hardening in welded condition, having the following melt analysis (wt. %):C 0.050 to 0.100%Si 0.15 to 0.45%Mn 0.30 to 0.70%P .ltoreq.0.020%S .ltoreq.0.010%Al .ltoreq.0.020%Cr 2.20 to 2.60%Mo 0.90 to 1.10%V 0.20 to 0.30%Ti 0.05 to 0.10%B 0.0015 to 0.0070%N .ltoreq.0.01%The balance of the steel is comprised of iron and ordinary impurities. The steel is annealed for a period of about 30 to about 60 minutes at about 980.degree. C. to about 1040.degree. C., thereupon cooled in air, and then tempered for at least one hour at about 730.degree. C. to about 760.degree. C.
摘要翻译：具有以下熔融分析（重量％）的具有改善的蠕变强度和低焊接硬化趋势的锅炉制造用高温钢：C 0.050〜0.100％Si 0.15〜0.45％Mn 0.30〜0.70％P < = 0.020％S

9. 发明授权

US5232740A Method of manufacturing plated hollow blocks 失效
标题翻译：制造中空块的方法
公开(公告)号：US5232740A
公开(公告)日：1993-08-03
申请号：US776306
申请日：1991-11-13
申请人： Ingo Von Hagen , Christoph Prasser , Fritz P. Pleschiutschnigg , Lothar Parschat
发明人： Ingo Von Hagen , Christoph Prasser , Fritz P. Pleschiutschnigg , Lothar Parschat
IPC分类号： B22D23/04 , C23C2/00 , C23C2/38
CPC分类号： C23C2/006
摘要： A method of manufacturing plated hollow metallic blocks for further processing into seamless tubes of the type in which a body is immersed one or more times into a melt includes: protecting the inner surfaces of a hollow body of plating material against the admission of a melt of support material during the immersion of the hollow body in the melt of support material; immersing such hollow body formed of plating material into the melt of support material; removing the hollow body from the melt of support material; and crystallizing a layer of support material on the outer surface of the hollow body.
摘要翻译： PCT No.PCT / DE90 / 00335 Sec。 371日期1991年11月13日 102（e）1991年11月13日PCT PCT 1990年5月8日PCT公布。 WO90 / 14446 PCT出版物日期：1990年11月29日。一种制造用于进一步加工成无缝管的电镀中空金属块的方法，其中将一种或多次浸入熔体中的类型的无缝管包括：保护电镀材料的中空体的内表面在中空体浸入支撑材料的熔体中时抵抗支撑材料的熔化; 将由电镀材料形成的中空体浸入支撑材料的熔体中; 从支撑材料的熔体中去除中空体; 并在所述中空体的外表面上结晶一层支撑材料。