A minimal strength loss caused by the dipped cord manufacturing process, it is possible to get the most potent in the code structure, provides a method for producing a high strength dipped cord.
A first step of applying A aramid fibers (raw yarn) at one twist (twist), and a second step of subjecting the ply-twisted with a plurality Hongo yarns twist cord, the adhesive on the twisted cord granted to a process for the preparation of aramid dipped cord and a third step of obtaining a dip cord, in a first step, drying the twist cord, until the following moisture content 7% in an atmosphere of temperature 50 ° C. or less aramid dipped cord manufacturing method to be. In a second step, subjecting the topcoat over the following tension 0.15 g / dtex and twist cord into a plurality Hongo yarn the code, after application and drying the adhesive in the third step, 0.15～0.60G / is preferably subjected to tension heat treatment tensioned in dtex, a manufacturing method of aramid dipped cord.
.BACKGROUND