1. 发明申请

WO2002092860A1 粒状金属鉄审中-公开
标题翻译：颗粒金属铁
公开(公告)号：WO2002092860A1
公开(公告)日：2002-11-21
申请号：PCT/JP2002/004677
申请日：2002-05-15
申请人：ミドレックスインターナショナルビー.ブイ. チューリッヒブランチ , 伊東修三 , 谷垣恭広 , 小林勲 , 津下修 , 本多啓介 , 徳田耕司 , 菊池晶一
发明人：伊東修三 , 谷垣恭広 , 小林勲 , 津下修 , 本多啓介 , 徳田耕司 , 菊池晶一
IPC分类号： C21B13/10
CPC分类号： C22C37/10 , B22F9/06 , B22F2998/10 , B22F2999/00 , C21B13/0006 , C21B13/0046 , C21B13/008 , C21B13/105 , C21B2100/42 , C22C37/00 , C22C38/02 , F27B9/16 , F27B9/39 , Y02P10/136 , B22F9/20 , B22F2201/30
摘要： A granular metallic iron which is produced by subjecting a raw material containing a carbonaceous reducing agent and an iron−containing material to reduction and melting, characterized in that it has an iron content of 94 mass % or more, a C content of 1.0 to 4.5 mass %, and a granule diameter of 1 to 30 mm.
摘要翻译：一种颗粒状金属铁，其通过使含有碳质还原剂和含铁材料的原料进行还原熔融而制造，其特征在于，铁含量为94质量％以上，C含量为1.0〜4.5 质量％，颗粒直径为1〜30mm。

2. 发明申请

WO2003020988A1 金属鉄の製法审中-公开
标题翻译：金属铁的生产方法
公开(公告)号：WO2003020988A1
公开(公告)日：2003-03-13
申请号：PCT/JP2002/005997
申请日：2002-06-17
申请人：株式会社神戸製鋼所 , 菊池晶一 , 徳田耕司 , 小林勲
发明人：菊池晶一 , 徳田耕司 , 小林勲
IPC分类号： C21B13/10
CPC分类号： C21B13/0086 , C21B13/0006 , C21B13/0046 , C21B13/0073 , C21B13/105 , Y02P10/136
摘要： A technique capable of producing metal iron high in metallization and iron purity with high yield and efficiency by minimizing a metal iron re-oxidizing problem encountered at the end of solid reduction when producing metal iron by heating/reducing material substances including an iron-oxide-containing substance and a carbonaceous reducing agent. A method of producing metal iron by heating material substances including an iron-oxide-containing substance and a carbonaceous reducing agent in a moving hearth type reducing/melting furnace, and reducing/melting the iron oxide in the material substances, wherein the reducing/melting furnace is partitioned into at least three sections in the moving direction of the hearth - namely, a solid reducing section on the upstream side in the hearth moving direction, a carburizing/melting section on the downstream side, and a reducing/aging section between the solid reducing section and the carburizing/melting section.
摘要翻译：通过使通过加热/还原材料物质（包括氧化铁 - 氧化物）生产金属铁来最小化在固体还原结束时遇到的金属铁再氧化问题，能够以高产率和高效率生产金属化和铁纯度高的金属铁和铁纯度的技术，含碳物质和碳质还原剂。一种通过在移动的炉床型还原/熔融炉中加热含氧化铁物质和碳质还原剂的物质物质来生产金属铁的方法，并且还原/熔化物质中的氧化铁，其中还原/熔融炉子沿炉床的移动方向分为至少三个部分，即炉床移动方向的上游侧的固体还原部分，下游侧的渗碳/熔化部分，以及下炉部分之间的还原/老化部分固体还原段和渗碳/熔化段。

3. 发明申请

WO2003008652A1 金属鉄の製法审中-公开
标题翻译：制造金属铁的方法
公开(公告)号：WO2003008652A1
公开(公告)日：2003-01-30
申请号：PCT/JP2002/005995
申请日：2002-06-17
申请人：ミドレックスインターナショナルビー.ブイ. チューリッヒブランチ , 津下修 , 谷垣恭広 , 小林勲 , 徳田耕司 , 菊池晶一 , 伊東修三
发明人：津下修 , 谷垣恭広 , 小林勲 , 徳田耕司 , 菊池晶一 , 伊東修三
IPC分类号： C21B13/10
CPC分类号： C21B13/10 , C21B13/0006 , C21B13/0046 , C21B13/0066 , C21B13/008 , C21B13/105 , C22B1/245 , C22B5/10 , Y02P10/136
摘要： A method of manufacturing metal iron capable of increasing the operation rate and maintainability of a hearth and being adapted to a long term continuous operation by allowing metal iron powder to be easily removed and the surface of the hearth to be easily repaired even if the metal iron powder is buried in the surface of the hearth or the surface is subjected to the invasion or erosion of slag in the production of the metal iron where a mixture containing carbonaceous reducer and iron oxide is fed onto the hearth of a movable floor type reducing melting furnace and heated to melt the iron oxide for reduction, and the metal iron thus obtained is cooled and discharged to the outside of the furnace for collection, comprising the steps of forming a renewable hearth by laying down hearth materials on the hearth in layer form before the mixture is supplied thereto and renewing a part or all of the renewed hearth deteriorated in the operation by using the hearth materials.
摘要翻译：一种制造金属铁的方法，其能够提高炉床的运行速度和维护性，并且通过允许容易地去除金属铁粉并且容易地修复炉床的表面，从而适用于长期的连续操作，即使金属铁粉末被埋在炉床的表面或表面在金属铁的生产中遭受炉渣的侵入或侵蚀，其中含有碳质还原剂和氧化铁的混合物被供给到可动地板型还原熔化炉的炉床上加热熔化氧化铁进行还原，将得到的金属铁冷却并排出到炉的外部进行收集，其特征在于，包括以下步骤：在炉床前形成炉床材料，形成可再生炉床向炉内供给混合物，并通过使用炉床材料更新操作中的一部分或全部更新的炉床。

4. 发明申请

WO2003062474A1 溶鉄の製法审中-公开
标题翻译：生产钢铁的工艺
公开(公告)号：WO2003062474A1
公开(公告)日：2003-07-31
申请号：PCT/JP2003/000298
申请日：2003-01-16
申请人：株式会社神戸製鋼所 , 小林勲 , 宮原逸雄 , 田中英年 , 徳田耕司
发明人：小林勲 , 宮原逸雄 , 田中英年 , 徳田耕司
IPC分类号： C21B13/10
CPC分类号： C21B13/105 , C21B13/006 , C21B13/14 , C21B13/143 , C21B2100/44 , C21B2100/66 , C21C2250/02 , Y02P10/136
摘要： A process for producing molten iron wherein a formed material containing iron oxide and a carbonaceous reducing agent is used as a raw material, and a rotary hearth furnace and a melting furnace are connected, characterized in that said formed material is first charged into a heating and reducing furnace, to enhance a metallization rate to 60 % or more prior to the feed to the melting furnace, and the secondary burning rate of a CO gas in said melting furnace is controlled to 40 % or less. The process allows the suppression of the loss by melting of refractories of the rotary hearth furnace and the melting furnace, in combination with the production of a molten iron having an enhanced purity of iron with good productivity.
摘要翻译：一种生产铁水的方法，其中使用含有氧化铁和碳质还原剂的成形材料作为原料，并且连接有转底炉和熔炉，其特征在于，首先将所述成形材料装入加热和还原炉，在进料到熔炉之前将金属化率提高到60％以上，将熔融炉中的CO气体的二次燃烧速度控制在40％以下。该方法结合生产具有提高的铁纯度的铁水，同时通过熔化转底炉和熔炉的耐火材料来抑制损失。