1. 发明授权

US5618387A Method of preparing biodegradable, water-resistant paper utensils 失效
标题翻译：生物降解，防水纸用具的制备方法
公开(公告)号：US5618387A
公开(公告)日：1997-04-08
申请号：US370489
申请日：1995-01-09
申请人： Wen-Fuei Yeh , Long-Huei Wang , Yao-Tung Liu , Ying-Yu Cheng
发明人： Wen-Fuei Yeh , Long-Huei Wang , Yao-Tung Liu , Ying-Yu Cheng
IPC分类号： D21F11/00 , D21H11/04 , D21H11/12 , D21H17/14 , D21H17/27 , D21H17/62 , D21H21/24 , D21H23/16 , D21F13/00
CPC分类号： D21H21/24 , D21F11/00 , D21H17/14 , D21H23/16 , D21H11/04 , D21H11/12 , D21H17/27 , D21H17/62
摘要： A method of preparing biodegradable water-resistant paper utensils which includes the steps of: (a) preparing a pulp aqueous slurry at a consistency of about 4%; (b) adding surfactant to the slurry; (c) thereafter, adding between 8 and 30 percent weight of a biodegradable and water-resistant agent to the slurry to form a slurry mixture; (d) refining the slurry mixture at a consistency of about 4 percent to a desired drainage; (e) diluting the refined slurry mixture and adding an aggregating agent thereto to form a furnish; and (f) after step (e), forming the furnish to obtain biodegradable, water-resistant paper board or directly a paper utensil. The forming step can be through a hot-press at a temperature of 115.degree. to 170.degree. C.
摘要翻译：一种制备可生物降解的防水纸用具的方法，其包括以下步骤：（a）以约4％的稠度制备纸浆含水浆料; （b）向浆料中加入表面活性剂; （c）此后，向浆料中加入8-30重量％的可生物降解和防水剂以形成浆料混合物; （d）以约4％的浓度将所述浆料混合物精炼成所需的排水; （e）稀释精制浆料混合物并向其中加入聚集剂以形成配料; 和（f）步骤（e）之后，形成配料以获得可生物降解的防水纸板或直接用纸制品。成型步骤可以在115-170℃的温度下进行热压。

2. 发明授权

US5906713A Method of preparing biodegradable, water-resistant, and molded paper board 失效
标题翻译：生物降解，防水，成型纸板的制备方法
公开(公告)号：US5906713A
公开(公告)日：1999-05-25
申请号：US561781
申请日：1995-11-22
申请人： Wen-Fuei Yeh , Long-Huei Wang , Yao-Tung Liu , Ying-Yu Cheng
发明人： Wen-Fuei Yeh , Long-Huei Wang , Yao-Tung Liu , Ying-Yu Cheng
IPC分类号： D21F11/00 , D21H11/04 , D21H11/12 , D21H17/14 , D21H17/27 , D21H17/62 , D21H21/24 , D21H23/16 , D21H25/00
CPC分类号： D21H21/24 , D21F11/00 , D21H17/14 , D21H23/16 , D21H11/04 , D21H11/12 , D21H17/27 , D21H17/62
摘要： A method of preparing biodegradable, water-resistant, moldable paper board or molded paper utensil which includes the steps of: (a) preparing a pulp aqueous slurry at a consistency of about 4%; (b) adding surfactant selected from the group consisting of rosin soap, sodium oleate, sodium stearate, and sodium palmitate to the pulp aqueous slurry; (c) adding between 25-75% weight of a biodegradable and water-resistant agent selected from the group consisting of calcium stearate, cellulose stearate, calcium palmitate and cellulose palmitate to the pulp aqueous slurry to form a slurry mixture; (d) refining the slurry mixture at a consistency of about 4% to a desired drainage; (e) diluting the refined slurry mixture and adding thereto an aggregating agent as alum to form a furnish; (f) forming the furnish to obtain a dry moldable soft paper board; (g) preheating the moldable paper board obtained in step (f) at a temperature from 110.degree. to 170.degree. C.; and (h) hot-pressing the preheated moldable paper board obtained in step (g) in a mold at a temperature from 115.degree. to 170.degree. C. for 2 to 40 seconds to obtain a molded paper utensil.
摘要翻译：一种制备可生物降解，防水，可成型的纸板或模制纸用具的方法，其包括以下步骤：（a）以约4％的稠度制备纸浆含水浆料; （b）向纸浆水浆中加入选自松香皂，油酸钠，硬脂酸钠和棕榈酸钠的表面活性剂; （c）向纸浆含水浆料中加入25-75％重量的选自硬脂酸钙，硬脂酸钙，棕榈酸钙和棕榈酸钙的生物降解性和防水剂，以形成浆料混合物; （d）以约4％的浓度将浆料混合物精炼成所需的排水; （e）稀释精制浆料混合物并加入聚集剂作为明矾以形成配料; （f）形成配料以获得干燥成型的软纸板; （g）在110℃至170℃的温度下预热步骤（f）中得到的可成型纸板; 和（h）将在步骤（g）中获得的预热的可成型纸板在115-170℃的温度下热压2至40秒，得到模制纸用具。

3. 发明授权

US5863388A Biodegradable and water-resistant paper product 失效
标题翻译：可生物降解和防水的纸制品
公开(公告)号：US5863388A
公开(公告)日：1999-01-26
申请号：US559537
申请日：1995-11-16
申请人： Wen-Fuei Yeh , Long-Huei Wang , Yao-Tung Liu , Ying-Yu Cheng
发明人： Wen-Fuei Yeh , Long-Huei Wang , Yao-Tung Liu , Ying-Yu Cheng
IPC分类号： D21F11/00 , D21H11/04 , D21H11/12 , D21H17/14 , D21H17/27 , D21H17/62 , D21H21/24 , D21H23/16 , D21J1/04
CPC分类号： D21H21/24 , D21F11/00 , D21H17/14 , D21H23/16 , D21H11/04 , D21H11/12 , D21H17/27 , D21H17/62
摘要： A biodegradable and water-resistant paper product which has the compositions of 8-30% weight of a biodegradable and water-resistant agent selected from the group consisting of calcium stearate, cellulose stearate, calcium palmitate and cellulose palmitate, 92-70% weight of pulp, based on the sum of the dry weight of pulp and water-resistant agent; surfactant selected from the group consisting of rosin soap, sodium oleate, sodium stearate, and sodium palmitate; and aggregating agent as alum. The paper product is prepared by a method which includes the steps of: (a) preparing a pulp aqueous slurry at a consistency of about 4%; (b) adding surfactant to the slurry; (c) thereafter, adding between 8-30% weight of a biodegradable and water-resistant agent to the slurry to form a slurry mixture; (d) refining the slurry mixture at a consistency of about 4% to a desired drainage; (e) diluting the refined slurry mixture and adding an aggregating agent thereto to form a furnish; and (f) after step (e), forming the furnish to obtain biodegradable and water-resistant paper board or directly a paper utensil. The forming step can be through a hot-press at a temperature of 115.degree. to 170.degree. C.
摘要翻译：一种生物可降解和耐水的纸制品，其具有8-30重量％的生物降解和防水剂的组合物，其选自硬脂酸钙，硬脂酸纤维素，棕榈酸钙和棕榈酸棕榈酸酯，92-70重量％纸浆，基于纸浆和防水剂的干重之和; 选自松香皂，油酸钠，硬脂酸钠和棕榈酸钠的表面活性剂; 和聚集剂作为明矾。纸制品通过包括以下步骤的方法制备：（a）以约4％的稠度制备纸浆含水浆料; （b）向浆料中加入表面活性剂; （c）此后，向浆料中加入8-30重量％的可生物降解和防水剂以形成浆料混合物; （d）以约4％的浓度将浆料混合物精炼成所需的排水; （e）稀释精制浆料混合物并向其中加入聚集剂以形成配料; 和（f）在步骤（e）之后，形成配料以获得可生物降解和防水的纸板或直接用纸制品。成型步骤可以在115-170℃的温度下进行热压。