1. 发明授权

US5364819A Ultraviolet Faraday rotator glass 失效
标题翻译：紫外法拉第旋转玻璃
公开(公告)号：US5364819A
公开(公告)日：1994-11-15
申请号：US53287
申请日：1993-04-28
申请人： James L. Dexter , David G. Cooper , Douglas H. Blackburn , David C. Cranmer , Dale A. Kauffman
发明人： James L. Dexter , David G. Cooper , Douglas H. Blackburn , David C. Cranmer , Dale A. Kauffman
IPC分类号： C03C3/247 , C03C3/32 , C03C4/00 , G02F1/00
CPC分类号： G02F1/0036 , C03C3/247 , C03C3/325 , C03C4/00 , Y10S501/90 , Y10S501/905
摘要： A Faraday rotator glass composition based on a fluoride glass, phosphate glass, fluorophosphate glass or a mixture thereof is doped with a lanthanide in a concentration sufficient to provide a Verdet constant above at least 2870 deg/Tesla-meter [(1 min/cm-Oe).times.(1.667.times.10.sup.4)=1 deg/Tesla-meter] and optical transmission above at least 50 percent in a 25 mm thick polished glass sample at least at one wavelength in the 200 to 400 nm wavelength region. The Faraday rotator glass also includes monovalent non-lanthanide cations such as Na, Li, K or mixtures thereof in a concentration sufficient to provide a Verdet constant above at least 2870 deg/Tesla-meter and optical transmission above at least 50 percent in a 25 mm thick polished glass sample at least at one wavelength in the 200 to 400 nm wavelength region. The Faraday rotator glass further includes a concentration of divalent or trivalent non-lanthanide cations such as Mg, Be, Ca, Al or mixtures thereof sufficient to provide surface flatness of at least 1/10 of the operating wavelength at 632.8 nm.
摘要翻译：基于氟化物玻璃，磷酸盐玻璃，氟磷酸盐玻璃或其混合物的法拉第旋转玻璃组合物掺杂有镧系元素，其浓度足以提供至少2870度/特斯拉米[（1分钟/厘米2） Oe）×（1.667×104）= 1度/特斯拉计]，并且在200nm至400nm波长区域中的至少一个波长的25mm厚的抛光玻璃样品中的至少50％的光学透射率。法拉第旋转器玻璃还包括一定浓度的单价非镧系元素阳离子，例如Na，Li，K或其混合物，其浓度足以提供高于至少2870度/特斯拉计的维尔德恒定，并且在25以上的光透射率至少为50％至少在200至400nm波长区域中的一个波长处的mm厚的抛光玻璃样品。法拉第旋转玻璃还包括二价或三价非镧系元素阳离子如Mg，Be，Ca，Al或其混合物的浓度，其足以提供在632.8nm处至少1/10的工作波长的表面平坦度。