1. 发明授权

US5063183A Sinterable aluminum nitride composition, sintered body from this composition and process for producing the sintered body 失效
标题翻译：可烧结的氮化铝组合物，该组合物的烧结体以及生产烧结体的方法
公开(公告)号：US5063183A
公开(公告)日：1991-11-05
申请号：US569369
申请日：1990-08-14
申请人： Hitofumi Taniguchi , Nobuyuki Kuramoto
发明人： Hitofumi Taniguchi , Nobuyuki Kuramoto
IPC分类号： C04B35/581
CPC分类号： C04B35/581
摘要： A process for producing a sintered body of aluminum nitride, which comprises(1) forming a raw molded article from a homogeneous mixture of(A) a fine powder of aluminun nitride, and(B) a sintering aid composed substantially of (a) at least one halogen compound of at least one metal selected from the group consisting of alkaline earth metals, lanthanum group metals and yttrium, and (b) at least one halogen-free compound of at least one metal selected from the group consisting of alkaline earth metals, lanthanum group metals and yttrium; and(2) sintering the raw molded article at a temperature of 1600.degree. to 2100.degree. C. in a non-oxidizing atmosphere. A sintered body having a high thermal conductivity and a high density of at least 3.2 g/cm.sup.3 is prepared by the process.
摘要翻译：一种氮化铝烧结体的制造方法，其特征在于，包括：（1）由（A）微粉末的氮化铝的均匀混合物形成原料成型体，（B）基本上由（a）组成的烧结助剂至少一种选自碱土金属，镧族金属和钇的金属的至少一种卤素化合物，和（b）至少一种选自碱土金属的至少一种不含卤素的化合物，镧族金属和钇; 和（2）在非氧化性气氛中，在1600〜2100℃的温度下烧结原料模制品。通过该方法制备具有高导热性和高密度至少3.2g / cm 3的烧结体。

2. 发明授权

US4618592A Fine powder of aluminum nitride, composition and sintered body thereof and processes for their production 失效
标题翻译：氮化铝微粉，其组成和烧结体及其制造方法
公开(公告)号：US4618592A
公开(公告)日：1986-10-21
申请号：US588773
申请日：1984-03-12
申请人： Nobuyuki Kuramoto , Hitofumi Taniguchi
发明人： Nobuyuki Kuramoto , Hitofumi Taniguchi
IPC分类号： C01B21/072 , C04B35/581 , C04B35/58 , F27D7/06
CPC分类号： C04B35/581 , C01B21/0726 , C01P2004/03 , C01P2004/61 , C01P2006/10 , C01P2006/32 , C01P2006/80
摘要： A fine powder of aluminum nitride having an average particle diameter of not more than 2 microns and comprising at least 94% by weight of aluminum nitride, at most 3% by weight of bound oxygen and at most 0.5% by weight as metal of metal compounds as impurities.The fine aluminum nitride powder is prepared from a fine alumina powder and a fine carbon powder as starting materials.The fine aluminum nitride powder provides a sintered body having a high purity and a high density such as at least 2.9 g/cm.sup.3.The fine aluminum nitride powder is also useful as a raw material for alpha-Sialon, beta-Sialon and AlN polytypes, as an addition aid in various ceramics.
摘要翻译：平均粒径不大于2微米并且包含至少94重量％的氮化铝，至多3重量％的结合氧和至多0.5重量％的作为金属化合物的铝的细粉末作为杂质。由细氧化铝粉末和细碳粉末作为原料制备细小的氮化铝粉末。精细的氮化铝粉末提供具有高纯度和高密度的烧结体，例如至少2.9g / cm 3。细氮化铝粉末也可用作α-赛隆，β-赛隆和AlN多型体的原料，作为各种陶瓷的添加剂。

3. 发明授权

US5242872A Process for producing aluminum nitride sintered body 失效
标题翻译：生产氮化铝烧结体的方法
公开(公告)号：US5242872A
公开(公告)日：1993-09-07
申请号：US724520
申请日：1991-06-28
申请人： Hitofumi Taniguchi , Nobuyuki Kuramoto
发明人： Hitofumi Taniguchi , Nobuyuki Kuramoto
IPC分类号： C04B35/581
CPC分类号： C04B35/581
摘要： A process for producing a sintered body of aluminum nitride, which comprises mixing an aluminum nitride powder with (A) an alkaline earth metal aluminate, or both of (A-1) an oxide or oxide-forming compound of aluminum, and (A-2) an oxide or oxide-forming compound of an alkaline earth metal, and (B) an oxide or oxide-forming compound of yttrium or an element of the lanthanide series, and firing the resulting mixture.
摘要翻译：一种制造氮化铝烧结体的方法，其包括将氮化铝粉末与（A）碱土金属铝酸盐或（A-1）氧化物或氧化物形成化合物和（A- 2）碱土金属的氧化物或氧化物形成化合物，和（B）钇或镧系元素的氧化物或氧化物形成化合物，并焙烧所得混合物。

4. 发明授权

US4950435A Process for producing aluminum nitride sintered body 失效
标题翻译：氮化铝烧结体的制造方法
公开(公告)号：US4950435A
公开(公告)日：1990-08-21
申请号：US71252
申请日：1987-07-08
申请人： Hitofumi Taniguchi , Nobuyuki Kuramoto
发明人： Hitofumi Taniguchi , Nobuyuki Kuramoto
IPC分类号： C04B35/581
CPC分类号： C04B35/581
摘要： A process for producing a sintered body of aluminum nitride, which comprises mixing an aluminum nitride powder with (A) an alkaline earth metal aluminate, or both of (A-1) an oxide or oxide-forming compound of aluminum, and (A-2) an oxide or oxide-forming compound of an alkaline earth metal, and (B) an oxide or oxide-forming compound of yttrium or an element of the lanthanide series, and firing the resulting mixture.
摘要翻译：一种制造氮化铝烧结体的方法，其包括将氮化铝粉末与（A）碱土金属铝酸盐或（A-1）氧化物或氧化物形成化合物和（A- 2）碱土金属的氧化物或氧化物形成化合物，和（B）钇或镧系元素的氧化物或氧化物形成化合物，并焙烧所得混合物。

5. 发明授权

US4642298A Composite nitride sintered body 失效
标题翻译：复合氮化物烧结体
公开(公告)号：US4642298A
公开(公告)日：1987-02-10
申请号：US711215
申请日：1985-03-13
申请人： Nobuyuki Kuramoto , Kazuya Takada , Yoshihiko Numata
发明人： Nobuyuki Kuramoto , Kazuya Takada , Yoshihiko Numata
IPC分类号： C04B35/581 , C04B35/583 , C04B35/58
CPC分类号： C04B35/581 , C04B35/583
摘要： A composite nitride sintered body consisting essentially of aluminum nitride, boron nitride and at least one metal compound selected from the group consisting of compounds of metals of Groups IIa and IIIa of the periodic table.The composite nitride sintered body is produced by intimately mixing a powder of aluminum nitride, a powder of boron nitride and at least one metal compound selected from the group consisting of metal compounds of metals of Groups IIa and IIIa of the periodic table, and sintering the mixture under atmospheric or elevated pressures at a temperature in the range of 1600.degree. to 2400.degree. C.The sintered body has a good machinability.
摘要翻译：一种复合氮化物烧结体，主要由氮化铝，氮化硼和至少一种金属化合物组成，所述金属化合物选自周期表第IIa和Ⅲa族金属的化合物。复合氮化物烧结体通过将氮化铝粉末，氮化硼粉末和选自周期表第IIa和IIIa族金属的金属化合物中的至少一种金属化合物充分混合并烧结混合物在大气压或高压下，温度范围为1600〜2400℃。烧结体具有良好的机械加工性。

6. 发明授权

US4310499A Process for producing SIALON sintered product 失效
标题翻译：生产SIALON烧结产品的方法
公开(公告)号：US4310499A
公开(公告)日：1982-01-12
申请号：US215662
申请日：1980-12-12
申请人： Mamoru Mitomo , Nobuyuki Kuramoto , Yoshizo Inomata
发明人： Mamoru Mitomo , Nobuyuki Kuramoto , Yoshizo Inomata
IPC分类号： C04B35/599 , C04B35/597 , C01B21/00 , C04B35/14
CPC分类号： C04B35/597
摘要： SIALON sintered product having the formulaSi.sub.6-z Al.sub.z O.sub.z N.sub.8-z(z is 0 to 4.2) is produced by sintering a molded product of the starting materials for SIALON in the condition of covering the surface of said molded product with a mixed powder of Si.sub.3 N.sub.4 and SiO.sub.2 as main components in nitrogen gas atmosphere.
摘要翻译：具有式Si 6-z Al z O z N 8-z（z为0至4.2）的SIALON烧结产品是通过在SiAl 3 O 4和SiO 2的混合粉末覆盖所述模塑产品的表面的条件下烧结SIALON原料的模塑产品作为氮气气氛中的主要成分。

7. 发明授权

US07364715B2 As-grown single crystal of alkaline earth metal fluoride 失效
标题翻译：碱土金属氟化物的单晶生长
公开(公告)号：US07364715B2
公开(公告)日：2008-04-29
申请号：US10717281
申请日：2003-11-19
申请人： Teruhiko Nawata , Nobuyuki Kuramoto , Hiroyuki Yanagi , Tsuguo Fukuda
发明人： Teruhiko Nawata , Nobuyuki Kuramoto , Hiroyuki Yanagi , Tsuguo Fukuda
IPC分类号： C30B29/12 , C30B15/14 , G02B1/02
CPC分类号： C30B15/14 , C30B15/00 , C30B29/12
摘要： A single crystal of alkaline earth metal fluoride is produced by a single crystal pulling method, has a straight barrel part diameter of not less than 17 cm, preferably has a straight barrel part length of not less than 5 cm, and has a light transmittance, as measured at a wavelength of 632.8 nm, of not less than 80%, preferably 90 to 98%. Further, the main crystal growth plane of the single crystal is the {111} plane or the {100} plane. The single crystal of alkaline earth metal fluoride has a large diameter as described above, and in spite that it is in an as-grown state, the peripheral surface is not opaque and the visible light transmittance is high. Therefore, evaluation of bubbles or inclusions in the crystal becomes feasible without performing complicated machining of the crystal, and from the single crystal, a large-sized optical material having advantageous properties such as high quality and high uniformity can be cut out.
摘要翻译：碱土金属氟化物的单晶通过单晶拉制法制造，直筒直径不小于17cm，优选具有不小于5cm的直筒部分长度，并具有透光率，在632.8nm的波长下测得的，不小于80％，优选为90-98％。此外，单晶的主晶体生长面是{111}面或{100}面。碱土金属氟化物的单晶如上所述具有大的直径，尽管其处于生长状态，但是外周表面不透明，可见光透射率高。因此，不需要对晶体进行复杂的加工就可以对晶体中的气泡或夹杂物进行评价，从而可以切断具有高质量，高均匀性等优点的大尺寸的光学材料。

8. 发明授权

US4190514A Electrolytic cell 失效
标题翻译：电解池
公开(公告)号：US4190514A
公开(公告)日：1980-02-26
申请号：US912987
申请日：1978-06-06
申请人： Shunji Matsuura , Toshio Oku , Masaaki Kurumatani , Nobuyuki Kuramoto , Yasutaka Ozaki
发明人： Shunji Matsuura , Toshio Oku , Masaaki Kurumatani , Nobuyuki Kuramoto , Yasutaka Ozaki
IPC分类号： C25B1/46 , C25B11/04 , C25D3/14 , C25D3/12 , C25B11/02
CPC分类号： C25B1/46 , C25B11/04 , C25D3/14
摘要： An electrolytic cell equipped with a cathode, said cathode comprising a supporting structure composed of iron, nickel or an alloy of such a metal and a nickel coating formed thereon by electroplating in the presence of at least one S/N substance selected from the group consisting of a thiocyanate ion, a thiosulfate ion, a dithiocarbamate ion, a thiocarboxylate ion, an amino acid ion, a thiocarbamoyl compound and thiourea.
摘要翻译：一种装有阴极的电解槽，所述阴极包括由铁，镍或这种金属的合金构成的支撑结构，其中通过在至少一种S / N物质存在下，通过电镀形成镍镀层，所述S / N物质选自的硫氰酸根离子，硫代硫酸根离子，二硫代氨基甲酸根离子，硫代羧酸根离子，氨基酸离子，硫代氨基甲酰基化合物和硫脲。