1. 发明授权

US5725697A Method of manufacturing cold-rolled can steel sheet having less planar anisotropy and good workability 失效
标题翻译：制造平面各向异性小，加工性好的冷轧钢板的制造方法
公开(公告)号：US5725697A
公开(公告)日：1998-03-10
申请号：US360348
申请日：1994-12-21
申请人： Chikako Fujinaga , Akio Tosaka , Toshiyuki Kato , Kaku Sato , Hideo Kuguminato
发明人： Chikako Fujinaga , Akio Tosaka , Toshiyuki Kato , Kaku Sato , Hideo Kuguminato
IPC分类号： C21D8/04 , C22C38/12
CPC分类号： C22C38/12 , C21D8/0436 , C21D8/0426 , C21D8/0468
摘要： A method of manufacturing a cold-rolled can steel sheet having less planar anisotropy and achieving good workability. Rough-rolling is first performed on a continuously-cast slab. The slab has a composition essentially consisting of: C: 0.004 wt % or lower; Mn: 0.05-0.5 wt %; P: 0.02 wt % or lower; Al: 0.005-0.07 wt %; N: 0.004 wt % or lower; and Nb: 0.001-0.018 wt %, the rest being Fe and unavoidable impurities. A resultant sheet bar is then subjected to hot rolling which is completed at a finishing rolling temperature at an Ar.sub.3 transformation point or higher. The resultant sheet bar is coiled at a temperature range from 450.degree.-700.degree. C. Subsequently, the resultant sheet bar undergoes primary cold rolling before continuous annealing, which is performed at a recrystallization temperature or higher, and secondary cold rolling. The primary and secondary cold rolling are respectively performed at reduction ratios satisfying the following conditions of: 88%.gtoreq.CR.sub.1 %+0.36.times.CR.sub.2 .ltoreq.105% wherein CR.sub.1 : reduction ratio of the primary cold rolling CR.sub.2 : reduction ratio of the secondary cold rolling
摘要翻译：制造平面各向异性小的冷轧钢板的制造方法，加工性良好。首先在连续铸造的板坯上进行粗轧。板坯的组成基本上由以下组成：C：0.004重量％以下; Mn：0.05〜0.5重量％ P：0.02重量％以下; Al：0.005-0.07重量％ N：0.004重量％以下; 和Nb：0.001-0.018重量％，其余为Fe和不可避免的杂质。然后对得到的薄板坯进行在Ar3相变点以上的精轧条件下完成的热轧。所得板坯在450〜-90℃的温度范围内卷绕。接着，在再结晶温度以上进行二次冷轧，连续退火前进行一次冷轧。一次冷轧和二次冷轧分别以满足以下条件的压下率进行：88％> = CR1％+ 0.36×CR2 <105％其中CR1：二次冷轧CR2的减速比：次级冷轧

2. 发明授权

US5587027A Method of manufacturing canning steel sheet with non-aging property and superior workability 失效
标题翻译：制造具有不老化性能和优良加工性能的罐头钢板的方法
公开(公告)号：US5587027A
公开(公告)日：1996-12-24
申请号：US389045
申请日：1995-02-15
申请人： Akio Tosaka , Chikako Fujinaga , Toshiyuki Kato , Kaku Sato , Hideo Kuguminato
发明人： Akio Tosaka , Chikako Fujinaga , Toshiyuki Kato , Kaku Sato , Hideo Kuguminato
IPC分类号： C21D3/04 , C21D8/04 , C22C38/00 , C22C38/04 , C22C38/06 , C21D8/00
CPC分类号： C22C38/004 , C21D8/0473 , C22C38/002 , C22C38/04 , C21D3/04 , C21D8/0426
摘要： A method for manufacturing a canning steel sheet with non-aging property and superior workability uses, as a starting material, an ultra-low-carbon steel slab composed of from 0.0015% to 0.0100% by weight C, up to 0.20% by weight Si, from 0.10% to 1.20% by weight Mn, from 0.02% to 0.10% by weight Al, from 0.005% to 0.040% by weight P, up to 0.015% by weight S, up to 0.005% by weight N, and balance iron and unavoidable impurities. The manufacturing method includes hot rolling the steel, cold rolling the steel at a reduction ratio not less than 70% after pickling, and recrystallization annealing the steel by using a continuous annealing furnace in an atmosphere having a hydrogen content not less than 3% and a dew point not lower than -20.degree. C. at a temperature not lower than 730.degree. C. so that the content of remained C in the steel is kept less than 0.0015% by weight. At least one element selected from Nb, Ti and B may be added in predetermined amounts to the above composition. The steel sheet suitable for canning is efficiently manufactured by a continuous annealing process.
摘要翻译：制造具有非时效性和优良加工性的罐头钢板的制造方法使用由0.0015-0.0100重量％C，至多0.20重量％的Si组成的超低碳钢板坯作为原料，，0.10重量％至1.20重量％的Mn，0.02重量％至0.10重量％的Al，0.005重量％至0.040重量％的P，至多0.015重量％的S，至多0.005重量％的N，余量为和不可避免的杂质。该制造方法包括对钢进行热轧，酸洗后以不低于70％的压下量进行冷轧，在氢含量不低于3％的气氛中使用连续退火炉，对钢进行再结晶退火，在不低于730℃的温度下露点不低于-20℃，使得钢中残留C的含量保持在0.0015重量％以下。选自Nb，Ti和B中的至少一种元素可以以上述组成加入预定量。通过连续退火工艺有效地制造适于罐装的钢板。

3. 发明授权

US6063214A Method of producing high-strength steel sheet used for can 失效
标题翻译：生产用于罐头的高强度钢板的方法
公开(公告)号：US6063214A
公开(公告)日：2000-05-16
申请号：US287473
申请日：1994-08-08
申请人： Chikako Fujinaga , Akio Tosaka , Toshiyuki Kato , Kaku Sato , Hideo Kuguminato , Yoshihiro Okawa
发明人： Chikako Fujinaga , Akio Tosaka , Toshiyuki Kato , Kaku Sato , Hideo Kuguminato , Yoshihiro Okawa
IPC分类号： C21D8/02 , C21D8/04
CPC分类号： C21D9/48 , C21D8/0226 , C21D8/0236 , C21D8/0436 , C21D8/0442 , C21D8/0473 , C22C38/004 , C21D8/0268
摘要： A method of producing a steel sheet useful for making cans. The method steps include hot-rolling a slab consisting of about 0.0005 to 0.01 wt % C, about 0.001 to 0.04 wt % N (the total of C and N is at least about 0.008 wt %), about 0.05 to 2.0 wt % Mn, about 0.005 wt % or less Al, about 0.01 wt % or less O at a finish rolling temperature within a temperature range of about the Ar.sub.3 point to about 950.degree. C., coiling the rolled material at a temperature range of about 400 to 600.degree. C., cold rolling the material, continuously annealing the material at a temperature higher than the recrystallization temperature, and then temper-rolling the material. The steel sheet exhibits good workability during can making and which can be formed into a can having high strength.
摘要翻译：一种制造用于制造罐头的钢板的方法。方法步骤包括热轧由约0.0005至0.01重量％的C，约0.001至0.04重量％的N（C和N的总和至少约0.008重量％），约0.05至2.0重量％的Mn，约0.005重量％以下的Al，约0.01重量％以下的O，在约Ar3点〜约950℃的温度范围内的精轧温度下，在约400〜600℃的温度范围内卷取轧制材料 C.冷却材料，在高于再结晶温度的温度下对材料进行连续退火，然后对材料进行调质。钢板在制罐时表现出良好的加工性，并且可以形成具有高强度的罐。

4. 发明授权

US5534089A Method of manufacturing small planar anisotropic high-strength thin can steel plate 失效
标题翻译：制造小平面各向异性高强度薄罐钢板的方法
公开(公告)号：US5534089A
公开(公告)日：1996-07-09
申请号：US360250
申请日：1994-12-20
申请人： Chikako Fujinaga , Akio Tosaka , Toshiyuki Kato , Kaku Sato
发明人： Chikako Fujinaga , Akio Tosaka , Toshiyuki Kato , Kaku Sato
IPC分类号： C21D8/04 , C22C38/00 , C21D8/02
CPC分类号： C21D8/0426 , C22C38/001 , C21D8/0436 , C21D8/0473 , C21D8/0478
摘要： A method of manufacturing a small planar anisotropic high-strength can steel plate. Hot-rolling is first performed on a steel slab at an Ar.sub.3 transformation point or higher to obtain hot rolled steel strip. The slab has a composition which essentially consists of and which satisfies the conditions of: C.ltoreq.0.004%, Si.ltoreq.0.02%, Mn=0.5%-3%, P.ltoreq.0.02%, Al=0.02%-0.05%, 0.008%.ltoreq.N.ltoreq.0.024%, and the rest being Fe and unavoidable impurities, wherein the conditions have the relationship of:Al%/N%>2. Then, the resultant strip is cooled at a cooling rate of 10.degree. C./s or higher so as to reach a temperature of 650.degree. C. or lower. The resultant strip is further coiled at a temperature in a range of from 550.degree. C. to 400.degree. C. Cold-rolling is performed on the resultant strip at a reduction ratio of 82% or higher preceded by removing a scale to obtain cold rolled steel strip. Subsequently, continuous annealing is performed on the resultant cold rolled steel strip at a recrystallization temperature or higher, being followed by temper-rolling.
摘要翻译：一种制造小型平面各向异性高强度钢板的方法。首先在Ar3相变点以上的钢坯上进行热轧，得到热轧钢带。该板坯具有基本上由以下条件构成的组成：C≤0.004％，Si <0.02％，Mn = 0.5％-3％，P <= 0.02％，Al = 0.02％ 0.05％，0.008％，N = 0.024％，其余为Fe和不可避免的杂质，其中条件具有以下关系：Al％/ N％> 2。然后，以10℃/ s以上的冷却速度冷却所得到的带材，达到650℃以下的温度。所得到的带材在550℃至400℃的温度下进一步盘绕。在所得到的带材上以82％或更高的压下率进行冷轧，然后除去水垢以获得冷轧钢带。随后，在所得到的冷轧钢带上，在再结晶温度以上进行连续退火，随后进行回火处理。

5. 发明授权

US5496420A Can-making steel sheet 失效
标题翻译：制罐钢板
公开(公告)号：US5496420A
公开(公告)日：1996-03-05
申请号：US269488
申请日：1994-07-01
申请人： Hideo Kuguminato , Toshikatsu Kato , Chikako Fujinaga , Kyoko Hamahara
发明人： Hideo Kuguminato , Toshikatsu Kato , Chikako Fujinaga , Kyoko Hamahara
IPC分类号： C21D8/04 , C22C38/12 , C22C38/26
CPC分类号： C21D8/0426 , C22C38/12 , C21D8/0436 , C21D8/0473 , C21D8/0478
摘要： There is provided an ultra-thin and high strength three-piece can-making plated steel sheet which is excellent in weldability and flange forming processibility containing C .ltoreq. about 0.004 wt %, Si.ltoreq. about 0.03 wt %, Mn: about 0.05-0.6 wt %, P.ltoreq. about 0.02 wt %, S.ltoreq. about 0.02 wt %, N.ltoreq. about 0.01 wt % Al: about 0.005-0.1 wt %, Nb: about 0.001-0.1 wt % and the balance of inevitable impurities. The steel sheet has a maximum recrystallization grain size of 30 .mu.m or less and a ratio of area of 50% or more which is occupied by recrystallization grains of about 5-25 .mu.m.
摘要翻译：本发明提供一种超薄，高强度的三片可制膜电镀钢板，其焊接性和法兰形成加工性优异，其含有C≤0.004重量％，Si≤0.03重量％，Mn：约 0.05-0.6重量％，P <= 0.02重量％，S <= 0.02重量％，N <约0.01重量％Al：约0.005-0.1重量％，Nb：约0.001-0.1重量％和平衡不可避免的杂质。钢板的最大再结晶粒径为30μm以下，再结晶晶粒所占的面积比例为约5〜25μm的面积的50％以上。

6. 发明授权

US5360676A Tin mill black plate for canmaking, and method of manufacturing 失效
标题翻译：锡磨黑板用于制罐，以及制造方法
公开(公告)号：US5360676A
公开(公告)日：1994-11-01
申请号：US43189
申请日：1993-04-06
申请人： Hideo Kuguminato , Toshikatsu Kato , Chikako Fujinaga , Kyoko Hamahara
发明人： Hideo Kuguminato , Toshikatsu Kato , Chikako Fujinaga , Kyoko Hamahara
IPC分类号： C21D8/04 , C22C38/12 , C21D8/00 , C23C18/00
CPC分类号： C21D8/0426 , C22C38/12 , C21D8/0436 , C21D8/0473 , C21D8/0478 , Y10T428/12937 , Y10T428/12958
摘要： A raw plated steel sheet for can comprises recrystallized particles containing approximately C
摘要翻译：用于罐的生电镀钢板包括含有大约C <0.004％，Si <0.03％，Mn：0.05-0.6％，P <0.02％，S <0.02％，N <0.01％，Al：0.005-0.1％，Nb：0.001〜0.1％，B：0.0001-0.005重量％。颗粒的最大直径小于约30μm，约5-25μm的颗粒的面积比大于约50％。这种钢板具有优异的加工特性和良好的产品质量均匀性。