KR100368245B1 용접균열이 적은 니켈계 합금의 플라즈마 분말 육성용접방법 失效
标题翻译： 용접이적은니켈계합금의플라즈마분말육성용접방
公开(公告)号：KR100368245B1
公开(公告)日：2003-01-24
申请号：KR1020000079916
申请日：2000-12-21
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원 , 제일 엠.피.티 주식회사
发明人： 윤병현 , 김형준
IPC分类号： B23K9/18
摘要： PURPOSE: A method for plasma transferred arc(PTA) welding Ni based alloys, especially Ni based alloys added with Nb is provided to inhibit the growth of Laves phase due to segregation of Nb precipitates along boundaries of dendrite. CONSTITUTION: In a method for plasma transferred arc welding Ni based alloys, the present invention is characterized in that welding operation is regulated to adjust dilution rate within the range of 15 to 35% and Ni based alloy powder is fed at a rate of 3.3 kg/hr as applying electric current of 170-210A.
摘要翻译：目的：提供等离子转移电弧（PTA）焊接Ni基合金，尤其是添加有Nb的Ni基合金的方法，以抑制由于Nb析出物沿枝晶边界偏析而引起的Laves相的生长。构成：在等离子体转移电弧焊接Ni基合金的方法中，本发明的特征在于，调节焊接操作以将稀释率调节到15-35％的范围内，并且将Ni基合金粉末以3.3kg /小时，施加170-210A的电流。

2. 实用新型

KR200277220Y1 강판 연속 용융도금용 로울러 失效
标题翻译：钢板连续热压滚筒
公开(公告)号：KR200277220Y1
公开(公告)日：2002-06-03
申请号：KR2020020001611
申请日：2002-01-18
申请人： 제일 엠.피.티 주식회사
发明人： 박영서 , 김신태 , 이운동
IPC分类号： C23C2/00
摘要： 본 고안은 강판 연속 용융도금용 로울러인 싱크롤(sink roll)과 스테이빌라이징롤(stabilizing roll)에 관한 것으로, 강판 연속 용융도금용 로울러의 용사피막층 위에 그 화학적 치밀화 처리를 위해 증류수에 무수크롬산(Cr
2 O
3 )을 혼합한 크롬산수용액과 질화붕소(boron nitride)를 혼합하여 조성한 코팅액을 도포하여 화학치밀화층을 형성함으로써, 용사피막층에 존재하는 기공을 충진함과 동시에 그 자체가 피막을 형성하여 드로스 형성을 억제할 수 있는 동시에 내마모성과 내열충격성 및 내식성을 향상시킨 강판 연속 용융도금용 로울러를 제공함.

3. 发明公开

KR1020020051950A 용접균열이 적은 니켈계 합금의 플라즈마 분말 육성용접방법 失效
标题翻译：用于等离子体转移弧焊的方法，具有低裂纹的基于镍的合金
公开(公告)号：KR1020020051950A
公开(公告)日：2002-07-02
申请号：KR1020000079916
申请日：2000-12-21
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원 , 제일 엠.피.티 주식회사
发明人： 윤병현 , 김형준
IPC分类号： B23K9/18
摘要： PURPOSE: A method for plasma transferred arc(PTA) welding Ni based alloys, especially Ni based alloys added with Nb is provided to inhibit the growth of Laves phase due to segregation of Nb precipitates along boundaries of dendrite. CONSTITUTION: In a method for plasma transferred arc welding Ni based alloys, the present invention is characterized in that welding operation is regulated to adjust dilution rate within the range of 15 to 35% and Ni based alloy powder is fed at a rate of 3.3 kg/hr as applying electric current of 170-210A.
摘要翻译：目的：提供等离子体转移电弧（PTA）焊接方法，特别是添加有Nb的Ni基合金，以抑制由于Nb析出物沿着枝晶边界的偏析而导致的Laves相的生长。构成：在等离子体转移电弧焊接Ni基合金的方法中，本发明的特征在于调节焊接操作以将稀释率调节在15至35％的范围内，并将Ni基合金粉末以3.3kg的速率 / hr，施加170-210A的电流。

4. 发明授权

KR100273896B1 연속용융알루미늄 도금강판 제조용 설비중 욕조(POT)내 설치된 침지롤(SINKROLL)및 지지롤(STABILIZINGROLL)의 세라믹 플라즈마 용사 제조방법 有权
标题翻译：陶瓷等离子体喷涂涂层方法，用于抛光辊和稳定辊
公开(公告)号：KR100273896B1
公开(公告)日：2000-12-15
申请号：KR1019980019451
申请日：1998-05-28
申请人： 제일 엠.피.티 주식회사
发明人： 김기영 , 김신태
IPC分类号： C23C4/10
摘要： PURPOSE: A ceramic plasma thermal spraying method for sink roll and stabilizing roll installed in a pot of a manufacturing facility for continuous melted aluminum plated steel plate is provided. The manufactured ceramic coating sink roll does not generate any corrosion phenomenon and has a hardness of 400 DPH that is two times higher than that of the iron roll. CONSTITUTION: The manufacturing method is as follows: (i) endow the roll surface with roughness by iron grit using surface shot blast of sink roll or stabilizing roll; (ii) degrease, wash and dry; (iii) primary thermal spray treatment by 100 μ m with mixed powder of 50-60 wt.% of cobalt, 25-30 wt.% of chrome, 5-10 wt.% of nickel, 5-7 wt.% of tungsten and 0.5 wt.% of carbon; (iv) secondary thermal spray treatment by 100μm with 50:50 mixture of mixed powder of 50-60 wt.% of cobalt, 25-30 wt.% of chrome, 5-10 wt.% of nickel, 5-7 wt.% of tungsten and 0.5 wt.% of carbon and mixed powder of 94 wt.% of alumina, 1.0 wt.% of silica and 5 wt.% of calcium oxide; (v) tertiary thermal spray treatment on the secondary treated surface of roll by 500μm with mixed powder of 94 wt.% of alumina, 5 wt.% of calcium oxide and 1 wt.% of silica; and (vi) biquadratic thermal spray treatment on the surface of the tertiary treated roll by 60-70μm with mixed powder of 70 wt.% of alumina, 25 wt.% of zirconia and 5 wt.% of silica.
摘要翻译：目的：提供一种安装在用于连续熔融镀铝钢板的制造设备的罐中的沉辊和稳定辊的陶瓷等离子体热喷涂方法。制造的陶瓷涂布槽不产生任何腐蚀现象，硬度为400DPH，高于铁辊的两倍。构成：制造方法如下：（i）使用沉辊或稳定辊的表面喷丸，通过铁砂使辊表面具有粗糙度; （ii）脱脂，洗涤和干燥; （iii）100微米的初步热喷涂处理，混合粉末为50-60重量％的钴，25-30重量％的铬，5-10重量％的镍，5-7重量％的钨和0.5重量％的碳; （iv）用50-60重量％的钴，25-30重量％的铬，5-10重量％的镍，5-7重量％的钴的混合粉末混合50次的二次热喷涂处理。的钨和0.5重量％的碳的混合粉末和94重量％的氧化铝，1.0重量％的二氧化硅和5重量％的氧化钙的混合粉末; （v）使用94重量％的氧化铝，5重量％的氧化钙和1重量％的二氧化硅的混合粉末对辊的二次处理的表面进行三次热喷涂处理500μm; 和（vi）三次处理的辊的表面上的二次热喷涂处理为60-70μm，混合粉末为70重量％的氧化铝，25重量％的氧化锆和5重量％的二氧化硅。

5. 发明公开

KR1019980043113A 연속용융알루미늄 도금강판 제조용 설비중 욕조(POT)내 설치된 침지롤(SINKROLL)및 지지롤(STABILIZINGROLL)의 세라믹 플라즈마 용사 제조방법 有权
标题翻译：用于制造用于制造连续熔融镀铝钢板的设备（POT）中浸渍辊（SINKROLL）和安装在槽（POT）中的支撑辊（STABILIZINGROL）的陶瓷等离子喷涂的工艺
公开(公告)号：KR1019980043113A
公开(公告)日：1998-08-17
申请号：KR1019980019451
申请日：1998-05-28
申请人： 제일 엠.피.티 주식회사
发明人： 김기영 , 김신태
IPC分类号： C23C4/10
摘要： (목적) 용융도금강판의 표면성을 향상하기 위하여 도금욕안에서의 거동은 매우 중요하며 철계 침지롤 및 지지롤의 마모 및 침식 부위가 연속용융도금시 도금 강판 표면에 전사되어 표면성을 악화시키게 되고, 철계 침지롤 수명이 단축되는 문제점을 해결키 위하여 용융알루미늄 도금욕에서 내마모성과 내침식성이 우수한 다단계 세라믹 코팅 침지롤 및 지지롤을 제조하는 방법을 제공함을 목적으로 한다.
(구성) 침지롤 또는 지지롤의 표면 쇼트 블라스트기를 사용하여 철계 그리트(grit)로 롤 표면의 표면 조도를 부여한 후 이를 탈지, 수세, 건조 후, 이에 코발트 50∼60wt%, 크롬 25∼30wt%, 니켈 5∼10wt%, 텅스텐 5∼7wt%, 탄소 0.5wt%의 혼합 분말을 100㎛ 정도로 1차 용사처리하고, 1차 용사 처리한 롤 표면에 코발트 60wt%, 크롬 30wt%, 니켈 5wt%, 텅스텐 4.5wt%, 탄소 0.5wt%의 혼합 분말과 알루미나 94wt%, 실리카 1.0wt%, 칼슘산화물 5wt%의 혼합 분말을 50：50의 비율로 혼합하여 이를 약100㎛ 정도로 2차 용사처리하며, 2차 용사 처리한 롤 표면에 알루미나 94wt%, 칼슘산화물 5wt%, 실리카 1wt%의 혼합 분말을 500㎛ 정도로 3차 용사처리하고, 3차 용사 처리한 롤 표면에 알루미나 70wt%, 지르코니아 25wt%, 실리카 5wt%의 혼합 분말을 60∼70㎛ 정도로 4차 용사처리 하여 연속용융알루미늄 도금강� �� 제조용 다단계 용사처리 세라믹 코팅된 침지롤 또는 지지롤을 제조한다.