1. 发明专利

JP2003003278A Alkali soluble type lubricating surface treated metallic product having excellent continuous film formability 审中-公开
标题翻译： ALKALI可溶型润滑表面处理金属制品，具有卓越的连续膜流通性
公开(公告)号：JP2003003278A
公开(公告)日：2003-01-08
申请号：JP2002093774
申请日：2002-03-29
申请人： Mitsui Takeda Chemicals Inc , Nippon Steel Corp , 三井武田ケミカル株式会社 , 新日本製鐵株式会社
发明人： YAMAOKA IKURO , MORI YOICHIRO , KANAI HIROSHI , TAWA TSUTOMU , KODA CHIKAKO , NISHIMURA MITSUHIRO
IPC分类号： B05D7/14 , B05D7/24 , B32B15/08 , B32B15/095 , C23C26/00
摘要： PROBLEM TO BE SOLVED: To provide an alkali soluble type lubricating surface treated metallic product having excellent continuous film formability. SOLUTION: The lubricating surface treated metallic product which is 0.5 to 20 GPa in the modulus of elasticity after coating of the film at 25 deg.C and has excellent moldability is formed by coating both surfaces or one surface of metal with an alkali soluble type lubricating film consisting essentially of an alkali soluble type aqueous polyurethane composition containing a carboxyl group in a molecule and having a fluidization initiation temperature of >=170 deg.C and a lubricating function imparting agent of 1 to 30 wt.% of the alkali soluble type aqueous polyurethane composition in such a manner that the film thickness attains 0.5 to 10 μm.
摘要翻译：要解决的问题：提供具有优异的连续成膜性的碱溶性型润滑表面处理金属产品。解决方案：在25℃下涂膜后的弹性模量为0.5〜20GPa的润滑表面处理金属产品，具有优异的成型性，通过用碱溶性润滑剂涂覆金属表面或一个表面而形成基本上由在分子中含有羧基并且具有> = 170摄氏度的流化开始温度的碱溶性型水性聚氨酯组合物和润滑功能赋予剂的碱溶性型水性聚氨酯组合物的1〜30重量％聚氨酯组合物的厚度达到0.5〜10μm。

2. 发明专利

JP2002120323A SOLUBLE TYPE LUBRICATING SURFACE TREATMENT STAINLESS STEEL PLATE EXCELLENT IN MOLDABILITY FOR FUEL TANK, AND METHOD FOR PRODUCING FUEL TANK 失效
公开(公告)号：JP2002120323A
公开(公告)日：2002-04-23
申请号：JP2001176681
申请日：2001-06-12
申请人： NIPPON STEEL CORP , MITSUI TAKEDA CHEMICALS INC
发明人： MORI YOICHIRO , MIYASAKA AKIHIRO , KANAI HIROSHI , YAMAOKA IKURO , TAWA TSUTOMU , KODA CHIKAKO , NISHIMURA MITSUHIRO
IPC分类号： B60K15/03 , B32B15/08 , B32B15/095 , B32B15/18 , B32B27/18 , B32B27/40 , C22C38/00 , C22C38/58 , C23C26/00
摘要： PROBLEM TO BE SOLVED: To provide a soluble type lubricating surface treatment stainless steel plate excellent in moldability for a fuel tank in which both surfaces or one surface are coated with a soluble type lubricating coat, and a method for producing the fuel tank. SOLUTION: The stainless steel plate has the soluble type lubricating resin coat on both surfaces or one surface. Preferably, the resin coat contains an alkali-soluble polyurethane aqueous composition (A) which contains a carboxyl group or a sulfonate group in a molecule and the glass transition temperature of the dry coat of which is at least 100 deg.C and 1-30 mass % based on the polyurethane composition of a lubricant (B) as main components.

3. 发明专利

JP2002060971A ALKALI SOLUBLE TYPE LUBRICATING SURFACE TREATED METALLIC PRODUCT EXCELLENT IN FORMABILITY 失效
公开(公告)号：JP2002060971A
公开(公告)日：2002-02-28
申请号：JP2000240596
申请日：2000-08-09
申请人： NIPPON STEEL CORP , MITSUI TAKEDA CHEMICALS INC
发明人： MORI YOICHIRO , KANAI HIROSHI , YAMAOKA IKURO , TAWA TSUTOMU , KODA CHIKAKO , NISHIMURA MITSUHIRO
IPC分类号： B05D7/14 , B05D7/24 , B32B15/08 , B32B15/095 , C23C26/00
摘要： PROBLEM TO BE SOLVED: To provide a lubricating surface treated metallic product having excellent formability on which an alkali soluble type lubricating film is formed. SOLUTION: In this alkali soluble type lubricating surface treated metallic product excellent in formability, both sides or one side is provided with an alkali soluble type lubricating film essentially consisting of (A) an alkali soluble type polyurethane water-based composition containing a carboxyl group or a sulfonic group in the molecules, and in which the glass transition temperature of the dry film is >=100 deg.C and (B) a lubricating function imparting agent of 1 to 30 mass% to the polyurethane composition so as to control the film thickness to 50 to 10 μm.

4. 发明专利

JP2003062927A Soluble lubricating surface-treated metal product for hydroforming excellent in moldability and emulsion- resistant hydraulic oil properties, and molding processing method therefor 有权
标题翻译：可溶性润滑表面处理金属产品，用于在可塑性和抗乳液液压油性能方面进行优化，以及其成型加工方法
公开(公告)号：JP2003062927A
公开(公告)日：2003-03-05
申请号：JP2001255837
申请日：2001-08-27
申请人： Mitsui Takeda Chemicals Inc , Nippon Steel Corp , 三井武田ケミカル株式会社 , 新日本製鐵株式会社
发明人： MORI YOICHIRO , YOSHIDA TORU , KANAI HIROSHI , MIYASAKA AKIHIRO , TAWA TSUTOMU , KODA CHIKAKO , NISHIMURA MITSUHIRO
IPC分类号： B05D3/10 , B21D26/02 , B21D26/053 , B21D37/18 , B32B15/08 , C10M101/02 , C10M105/24 , C10M107/02 , C10M107/38 , C10M125/26 , C10M145/14 , C10M145/16 , C10M145/22 , C10M149/06 , C10M149/08 , C10M149/14 , C10M173/02 , C10N10/02 , C10N20/00 , C10N20/06 , C10N30/00 , C10N40/24 , C10N50/02
摘要： PROBLEM TO BE SOLVED: To provide a soluble lubricating surface-treated metal product for hydroforming used when a metal pipe such as a steel pipe, an aluminum pipe or the like is mounted in a mold and pushed into the mold in a pipe axis direction by applying internal pressure to the pipe to be processed into a predetermined shape or a soluble lubricating surface-treated metal product for sheet hydroforming used when a metal sheet such as a steel sheet, an aluminum sheet or the like is mounted in the mold to be processed into a predetermined shape by applying internal pressure to the sheet, and a molding processing method therefor.
SOLUTION: The soluble lubricating surface-treated metal product for hydroforming excellent in moldability and emulsion-resistant hydraulic oil properties has a soluble lubricating resin film on its surface. The soluble lubricating resin film desirably contains an aqueous composition (A) of soluble polyurethane, which contains an acid group in its molecule, containing a mixture of sodium hydroxide and an amine, a mixture of potassium hydroxide and the amine or a mixture of sodium hydroxide, potassium hydroxide and the amine as a neutralizing agent of the acid group and a lubricating function imparting agent (B) added in an amount of 1-50 mass % with respect to the polyurethane composition.
COPYRIGHT: (C)2003,JPO
摘要翻译：要解决的问题：提供一种用于液压成型的可溶性润滑表面处理金属产品，当将金属管如钢管，铝管等安装在模具中并在管轴方向上被推入模具时使用。在待加工的模具中安装钢板，铝板等的金属板时，将被加工的管内压施加到预定的形状或用于片材液压成形的可溶性润滑表面处理金属制品通过对片材施加内部压力而形成预定形状，以及其成型处理方法。解决方案：用于液压成型的可溶性润滑表面处理金属产品具有优异的成型性和耐乳液性液压油性能，其表面具有可溶性润滑树脂膜。可溶性润滑树脂膜理想地含有可溶性聚氨酯的水性组合物（A），其在分子中含有酸基，含有氢氧化钠和胺的混合物，氢氧化钾和胺的混合物或氢氧化钠的混合物，氢氧化钾和作为酸基的中和剂的胺和相对于聚氨酯组合物以1-50质量％的量加入的润滑功能赋予剂（B）。

5. 发明专利

JP2001342577A ALUMINUM ALLOY PLATE SUPERIOR IN PRESS FORMABILITY 失效
公开(公告)号：JP2001342577A
公开(公告)日：2001-12-14
申请号：JP2000167216
申请日：2000-06-05
申请人： NIPPON STEEL CORP , MITSUI TAKEDA CHEMICALS INC
发明人： MORI YOICHIRO , FUJII SHIRO , SATO YUICHI , TAKADA TAKESHI , TAWA TSUTOMU , KODA CHIKAKO , HIRATA FUMIAKI
IPC分类号： B05D7/14 , B32B15/08 , B32B15/095 , C22C21/02 , C22C21/06 , C23C26/00
摘要： PROBLEM TO BE SOLVED: To provide a specified urethane coated aluminum alloy plate superior in press formability. SOLUTION: Aluminum alloy plate superior in press formability is characterized by providing an alkaline soluble type of lubrication coating with a film thickness of 0.5-10 μm on its both sides or one side, which mainly consists of a polyurethane composition (A), of which the hydrophilic group is a carboxyl group or a sulfonate group with an acid value in the range of 30-180 and a neutralizer of the hydrophilic group is sodium hydroxide or potassium hydroxide, and a lubrication functionalization agent (B) of 1-30 weight % against the polyurethane composition; along with prescribing an alloy composition and a value of difference (TS-YS) between a tensile strength (TS) before press forming and 0.2% yield strength (YS). The alkaline soluble type of lubrication coating preferably further includes silica particles (C) of 1-30 weight % against the polyurethane composition, as a main component.

6. 发明专利

JP2003027256A Alkali soluble type lubricating surface treated metallic product having excellent formability and long term stable coating removability without depending on coating dry temperature 审中-公开
标题翻译： ALKALI可溶型润滑表面处理金属产品，具有优异的可塑性和长期稳定的涂层可移除性，不依赖于涂料干燥温度
公开(公告)号：JP2003027256A
公开(公告)日：2003-01-29
申请号：JP2002093773
申请日：2002-03-29
申请人： Mitsui Takeda Chemicals Inc , Nippon Steel Corp , 三井武田ケミカル株式会社 , 新日本製鐵株式会社
发明人： YAMAOKA IKURO , MORI YOICHIRO , KANAI HIROSHI , MIYASAKA AKIHIRO , TAWA TSUTOMU , KODA CHIKAKO , NISHIMURA MITSUHIRO
IPC分类号： B05D3/02 , B05D5/00 , B05D7/24 , C08G18/65 , C09D5/00 , C09D123/00 , C09D127/12 , C09D175/08 , C09D191/06 , C23C26/00
摘要： PROBLEM TO BE SOLVED: To provide an alkali soluble type lubricating surface treated metallic product which has excellent formability and long term stable coating removability without depending on coating dry temperature. SOLUTION: Alkali soluble type lubricating coating film essentially consisting of a polyether polyol skelton and carboxy group-containing alkali soluble type polyurethane aqueous composition and a lubricating function impartment agent of 1 to 30 mass% to the alkali soluble type polyurethane aqueous composition is formed to both sides or one side of a metal so as to control the coating thickness to 0.5 to 10 μm. Also, the elastic modulus of the film after the formation at 25 deg.C is 0.5 to 20 GPa.
摘要翻译：要解决的问题：提供一种碱溶性型润滑表面处理金属产品，其具有优异的成型性和长期稳定的涂层去除性，而不依赖于涂布干燥温度。解决方案：将基本上由聚醚多元醇骨架和含羧基的碱溶性聚氨酯水性组合物组成的碱溶性型润滑涂膜和对碱溶性型聚氨酯水性组合物的润滑功能赋形剂形成为1〜30质量％侧面或金属的一侧，以将涂层厚度控制在0.5〜10μm。此外，25℃下形成后的膜的弹性模量为0.5〜20GPa。

7. 发明专利

JP2002144478A ALKALI SOLUBLE LUBRICATING SURFACE-TREATED METAL PRODUCT EXCELLENT IN MOLDABILITY 失效
公开(公告)号：JP2002144478A
公开(公告)日：2002-05-21
申请号：JP2000350175
申请日：2000-11-16
申请人： NIPPON STEEL CORP , MITSUI TAKEDA CHEMICALS INC
发明人： YAMAOKA IKURO , KANAI HIROSHI , MIYASAKA AKIHIRO , MORI YOICHIRO , TAWA TSUTOMU , NISHIMURA MITSUHIRO , KODA CHIKAKO
IPC分类号： B05D7/14 , B05D7/24 , B21D22/20 , B32B15/095 , C08G18/08 , C08G18/12 , C08G18/66 , C08K3/36 , C08K5/09 , C08K5/10 , C08K5/20 , C08L23/02 , C08L23/06 , C08L27/12 , C08L75/04 , C08L91/06 , C09D5/00 , C09D123/00 , C09D127/12 , C09D175/04 , C09D175/06 , C09D175/12 , C09D191/08 , C10M101/02 , C10M105/12 , C10M105/22 , C10M105/32 , C10M105/68 , C10M107/02 , C10M107/38 , C10M109/00 , C10M125/26 , C10M149/18 , C10M151/04 , C10M173/02 , C10N10/02 , C10N10/04 , C10N10/08 , C10N20/00 , C10N20/06 , C10N40/24 , C10N50/02 , B32B15/08
摘要： PROBLEM TO BE SOLVED: To provide an alkali soluble lubricating surface-treated metal product excellent in moldability suitably adapted to a use putting a beautiful metal surface or a metal quality feeling to practical use and a use requiring weldability because there is no mold dragging even under a severe molding condition and no lubricating film remains after degreasing and extremely high in a value from an industrial aspect. SOLUTION: An alkali soluble lubricating film, which is based on an alkali soluble polyurethane aqueous composition containing a carboxyl group or sulfonic acid group in its molecule and a lubricating function imparting agent of which the amount is 1-30 mass % with respect to the alkali soluble polyurethane aqueous composition, is applied to the single surface or both surfaces of a metal so that the thickness thereof becomes 0.5-10 μm. The elastic modulus after coating of the film is 0.5-20 GPa.

8. 发明专利

JP2006104226A Aqueous polyurethane composition and its preparation method 有权
标题翻译：水性聚氨酯组合物及其制备方法
公开(公告)号：JP2006104226A
公开(公告)日：2006-04-20
申请号：JP2004288505
申请日：2004-09-30
申请人： Mitsui Takeda Chemicals Inc , 三井武田ケミカル株式会社
发明人： SHIRAKI HIROYUKI , KODA CHIKAKO , MIYOSHI SHINJI
IPC分类号： C08G18/80 , C08J3/03 , C08L75/04
摘要： PROBLEM TO BE SOLVED: To provide an aqueous polyurethane composition which has a good shelf stability and is capable of forming a cured coating film which is excellent in coating film strength, water resistance and solvent resistance through heat-curing, and a preparation method thereof.
SOLUTION: The aqueous polyurethane composition is prepared by compounding a polyurethane resin containing at least one silanol group within a molecule with a block polyisocyanate. In the preparation method of the aqueous polyurethane composition, a hydrophilic urethane prepolymer is mixed with a hydrophilic block polyisocyanate, dispersed in water and subsequently subjected to chain elongation using a chain-elongation agent containing a hydrolyzable silicon group-containing compound.
COPYRIGHT: (C)2006,JPO&NCIPI
摘要翻译：要解决的问题：提供一种水性聚氨酯组合物，其具有良好的储存稳定性，并且能够形成通过热固化而具有优异的涂膜强度，耐水性和耐溶剂性的固化涂膜，以及制备方法。解决方案：水性聚氨酯组合物通过在分子内含有至少一个硅烷醇基团的聚氨酯树脂与嵌段多异氰酸酯混合来制备。在水性聚氨酯组合物的制备方法中，将亲水性氨基甲酸酯预聚物与分散在水中的亲水性嵌段聚异氰酸酯混合，然后使用含有可水解含硅基团的化合物的链延长剂进行链延长。版权所有（C）2006，JPO＆NCIPI

9. 发明专利

JP2000309747A COATING COMPOSITION HAVING ABILITY TO FORM LUBRICATIVE FILM EXCELLENT IN PRESS-MOLDABILITY AND SCUFFING- RESISTANCE, AND OF ALKALI-SOLUBLE TYPE, AND METAL PRODUCT HAVING LUBRICATIVELY TREATED SURFACE USING THIS COMPOSITION 失效
公开(公告)号：JP2000309747A
公开(公告)日：2000-11-07
申请号：JP36047699
申请日：1999-12-20
申请人： NIPPON STEEL CORP , TAKEDA CHEMICAL INDUSTRIES LTD
发明人： MORI YOICHIRO , YAMAZAKI MAKOTO , FUDA MASAHIRO , WAKE RYOSUKE , TAWA TSUTOMU , KODA CHIKAKO , HIRATA FUMIAKI
IPC分类号： B05D7/14 , B05D7/24 , C08G18/08 , C08G18/12 , C08G18/66 , C09D5/00 , C09D175/04 , C09D175/06
摘要： PROBLEM TO BE SOLVED: To provide a coating composition having the ability to form a lubricative film excellent in press-moldability and scuffing-resistance, and of an alkali- soluble type, and provide a metal product having a lubricatively treated surface using this composition. SOLUTION: A coating composition having the ability to form a lubricative film excellent in press-moldability and scuffing-resistance, and of an alkali- soluble type, comprises as main components (A) a polyurethane aqueous composition and (B) a lubricity imparting agent of 1-30 wt.% relative to the solid content of the aforedescribed polyurethane aqueous composition. In addition, a metal product having a lubricatively treated surface of an excellent press- moldability and scuffing-resistance is formed by so covering this coating composition for the dried film thickness as to be 0.5-5 μm. Preferably, the coating composition contains furthermore as a main component (C) silica particles of 1-30 wt.% relative to the solid content of the polyurethane aqueous composition.

10. 发明专利

JP2000102765A COATING MATERIAL COMPOSITION FOR LUBRICATION SURFACE TREATMENT 失效
公开(公告)号：JP2000102765A
公开(公告)日：2000-04-11
申请号：JP27402798
申请日：1998-09-28
申请人： TAKEDA CHEMICAL INDUSTRIES LTD , NIPPON STEEL CORP
发明人： TAWA TSUTOMU , KODA CHIKAKO , HIRATA FUMIAKI , MORI YOICHIRO , YAMAZAKI MAKOTO , NIIGASHIRA HIDETOSHI
IPC分类号： B05D7/14 , C08K3/36 , C08L75/00 , C09D175/00
摘要： PROBLEM TO BE SOLVED: To provide a coating material composition for lubrication surface treatment forming a lubricative coating which exhibits excellent workability in the case of continuous press working and continuous ironing working of a steel sheet. SOLUTION: This coating material for lubrication surface treatment essentially contains (A) an aqueous polyurethane composition containing silanol groups in its molecule, (B) 3-30 wt.% lubricity imparting agent based on the amount of the polyurethane composition and (C) 1-30 wt.% silica particles based on the amount of the polyurethane composition.