1. 发明授权

KR100852759B1 전해질이 첨가된 니켈-알루미늄 합금 용융탄산염연료전지용 연료극 및 그 제조방법 有权
标题翻译：电解质添加的NI-AL合金的碳酸钙燃料电池的阳极及其制备方法
公开(公告)号：KR100852759B1
公开(公告)日：2008-08-18
申请号：KR1020070029759
申请日：2007-03-27
申请人： 한국과학기술연구원
发明人： 함형철 , 윤성필 , 한종희 , 남석우 , 임태훈 , 오인환 , 이광수 , 김창원
IPC分类号： H01M4/86 , H01M4/04
CPC分类号： H01M4/8605 , H01M4/8857 , H01M4/8885 , H01M2008/147 , H01M2300/0051 , Y02E60/526
摘要： An anode for a molten carbonate fuel cell obtained by adding an electrolyte to nickel-aluminum alloy powder is provided to increase the amount of an electrolyte infiltrated into an anode with an electrolyte, thereby maintaining stable fuel cell quality. An anode for a molten carbonate fuel cell is obtained by adding an electrolyte to nickel-aluminum alloy powder, and is mounted directly to a fuel cell without heat treatment, followed by in-situ sintering during pretreatment of the fuel cell. The nickel-aluminum alloy comprises aluminum in an amount of 1-5 wt% based on the total weight of the alloy. The electrolyte is present in an amount of 1-60 wt% based on the total weight of the anode.
摘要翻译：提供了通过向镍 - 铝合金粉末中添加电解质而获得的熔融碳酸盐燃料电池的阳极，以增加用电解质渗入阳极的电解质的量，从而保持燃料电池的稳定性。通过向镍 - 铝合金粉末中加入电解液，可以获得熔融碳酸盐燃料电池的阳极，并且在没有热处理的情况下直接安装在燃料电池上，随后在燃料电池的预处理期间进行原位烧结。该镍 - 铝合金包括相对于合金总重量为1-5重量％的铝。基于阳极的总重量，电解质的存在量为1-60重量％。

2. 发明授权

KR100785052B1 축전 탈이온 법 및 화학적 환원법을 이용하여 제조된 수소방출 반응용 비귀금속-붕소 촉매/담지체 및 그 제조 방법 失效
标题翻译：非极性金属-B催化剂/结构化的支持使用电化学发生和化学还原的氢生成及其制备方法
公开(公告)号：KR100785052B1
公开(公告)日：2007-12-12
申请号：KR1020060066244
申请日：2006-07-14
申请人： 한국과학기술연구원
发明人： 이재영 , 남석우 , 임태훈 , 윤성필 , 김형준 , 한종희 , 하흥용 , 조은애 , 이광수 , 정창렬 , 함형철
IPC分类号： B01J21/02 , B01J23/755 , B01J23/75 , B01J21/18
CPC分类号： B01J21/02 , B01J21/18 , B01J23/75 , B01J23/755 , B01J37/16 , B01J2523/305
摘要： A cobalt-boron catalyst/carrier for generating hydrogen and a method for manufacturing the same are provided to substitute for noble metal catalysts and be usable in a hydrogen generation reaction of other borohydrides as well as NaBH4, by using capacitive deionization and chemical reduction. One or more types of non-noble-boron catalysts are supported within a carrier, wherein the one or two types of non-noble-boron catalysts are non-noble-boron oxides or non-noble-boron compounds except non-noble-carbon oxides. The carrier has a capacitive deionization performance. The non-noble ion is adsorbed on the carrier by capacitive deionization, and reduced by alkaline borohydride as a reducing agent.
摘要翻译：提供了用于产生氢的钴 - 硼催化剂/载体及其制造方法以代替贵金属催化剂，并且可以通过使用电容去离子和化学还原在其它硼氢化物以及NaBH 4的氢产生反应中使用。一种或多种类型的非贵重硼催化剂负载在载体中，其中一种或两种非贵重硼催化剂是非贵重硼氧化物或非贵金属硼化合物，除非贵金属碳氧化物。载体具有电容去离子性能。非贵重离子通过电容去离子吸附在载体上，并通过碱性硼氢化物还原作为还原剂。

3. 发明公开

KR1020030070725A 용융탄산염 연료전지용 연료극 및 이를 포함하는용융탄산염 연료전지 失效
标题翻译：用于碳酸钙燃料电池的燃料电极和含有电极的碳酸氢盐燃料电池
公开(公告)号：KR1020030070725A
公开(公告)日：2003-09-02
申请号：KR1020020010246
申请日：2002-02-26
申请人： 한국과학기술연구원
发明人： 홍성안 , 오인환 , 임태훈 , 남석우 , 하흥용 , 윤성필 , 한종희 , 이광수
IPC分类号： H01M4/86
摘要： PURPOSE: A fuel electrode for a molten carbonate fuel cell and a molten carbonate fuel cell containing the electrode are provided, to inhibit the deterioration of the performance of fuel cell due to the cracking of an electrolyte matrix and the increase of polarization of fuel cell and to lower the manufacturing cost. CONSTITUTION: The fuel electrode is prepared by mixing at least one reinforcing powder selected from the group consisting of a Ni-containing metal mixture, a Ni-containing alloy and a Ni-containing metal compound for improving the resistance against sintering and compression molding during the operation of a fuel electrode, and a pure Ni or Cu powder for improving the sintering property. Preferably the content of the reinforcing powder is 30-70 vol%.
摘要翻译：目的：提供一种用于熔融碳酸盐燃料电池的燃料电极和包含该电极的熔融碳酸盐燃料电池，以抑制由于电解质基质的破裂和燃料电池的极化增加引起的燃料电池的性能的劣化，以及降低制造成本。构成：燃料电极通过混合至少一种选自由含Ni金属混合物，含Ni合金和含Ni金属化合物组成的组的增强粉末来制备，以提高耐烧结和压缩成型的能力燃料电极的操作，以及用于提高烧结性能的纯Ni或Cu粉末。优选地，增强粉末的含量为30-70体积％。

4. 发明公开

KR1020030070447A 연료전지 운전용 가스 공급 장치 失效
标题翻译：用于燃料电池运行的气体供应装置
公开(公告)号：KR1020030070447A
公开(公告)日：2003-08-30
申请号：KR1020020009991
申请日：2002-02-25
申请人： 한국과학기술연구원
发明人： 오인환 , 신석재 , 하흥용 , 홍성안 , 임태훈 , 남석우 , 윤성필 , 한종희 , 김영천 , 이광수
IPC分类号： H01M8/04
摘要： PURPOSE: A gas supply apparatus for the operation of a fuel cell is provided, to allow the apparatus to be operated under a high pressure, the humidification state of the gas supplied to a fuel cell to be controlled easily and the water necessary for the humidification to be supplemented even during operation. CONSTITUTION: The gas supply apparatus supplies the reaction gas to a fuel cell after humidifying the reaction gas supplied from a gas source in a humidifier, wherein the humidifier comprises a container(30) receiving the reaction gas and humidifying it by using water; a humidifier gas supply pipe(13) whose one side is inserted into the container to supply the reaction gas to be humidified; a water supply pipe(33) supplying the water to be used for humidifying the reaction gas to the container; and a fuel cell gas supply pipe(15) connected with the container to supply the humidified reaction gas to a fuel cell. Preferably a detachable jacket-shaped container heater(35) is set at the outer circumference of the container for humidifying the reaction gas by heating; and a water supplement valve(34) is set at the water supply pipe.
摘要翻译：目的：提供一种用于操作燃料电池的气体供应装置，以使设备能够在高压下操作，供给燃料电池的气体的加湿状态容易控制，加湿所需的水即使在操作期间也要补充。构成：在加湿从加湿器中的气源供给的反应气体之后，气体供给装置向燃料电池供给反应气体，其中，加湿器包括容纳反应气体的容器（30），并通过使用水对其进行加湿; 加湿器供气管（13），其一侧插入容器中以供应待加湿的反应气体; 向所述容器供给用于将所述反应气体加湿的水的供水管道（33）以及与容器连接以将加湿的反应气体供给到燃料电池的燃料电池气体供给管（15）。优选地，在容器的外周设置可拆卸的夹套形容器加热器（35），用于通过加热来加湿反应气体; 并且在供水管上设置补水阀（34）。

5. 发明公开

KR1020010038320A 용융탄산염 연료전지용 세라믹 섬유 강화 매트릭스 및 그의 제조 방법 失效
标题翻译：用于碳酸钙燃料电池的陶瓷纤维增强基体及其制造方法
公开(公告)号：KR1020010038320A
公开(公告)日：2001-05-15
申请号：KR1019990046261
申请日：1999-10-25
申请人： 한국과학기술연구원
发明人： 홍성안 , 오인환 , 임태훈 , 남석우 , 하흥용 , 강범석 , 이광수
IPC分类号： H01M8/02
CPC分类号： Y02P70/56
摘要： PURPOSE: A ceramic fiber-reinforced matrix for a molten carbonate fuel cell and a method for manufacturing the same are provided which restrains cracks of matrix due to the thermal cycling that can be generated during the long term running of the molten carbonate fuel cell and the resulting deterioration of the cell. CONSTITUTION: The method for manufacturing the fiber-reinforced matrix for a molten carbonate fuel cell comprises the steps of preparing a slurry by ball milling the mixture after mixing LiAlO2 powder, dispersant, antifoaming agent and solvent; adding binder, plasticizer and ceramic fiber to the prepared slurry, mixing the materials, and ball milling the mixture; degassing the ball milled slurry; and drying after molding the degassed slurry in a tape casting process, wherein the LiAlO2 powder is selected from the group consisting of γ-LiAlO2, β-LiAlO2 and α-Al2O3, the LiAlO2 powder is a mixture of LiAlO2 HSA (high surface area) having a size of 5 microns or less and LiAlO2 LSA (low surface area) having a size of 10 microns or less, and the LSA is 10 to 30 weight parts based on the 100 weight parts of fiber and powder, wherein the ceramic fiber is selected from the group consisting of α-Al2O3, γ-LiAlO2, β-LiAlO2, α-LiAlO2, LiZrO3, Y2O3 stabilized ZrO3, LiTaO3, LiNbO3 and CeO2, and used in an amount of 5 to 20 weight parts based on 100 weight parts of powder and fiber, and wherein 10 to 40 weight parts of binder, 10 to 40 weight parts of plasticizer, 1 to 5 weight parts of antifoaming agent, 1 to 2 weight parts of dispersant and 150 to 250 weight parts of solvent are used based on 100 weight parts of powder and fiber.
摘要翻译：目的：提供一种用于熔融碳酸盐燃料电池的陶瓷纤维增强基体及其制造方法，其抑制由于在熔融碳酸盐燃料电池的长期运行期间可能产生的热循环，从而抑制基体的裂纹导致电池劣化。构成：用于制造熔融碳酸盐燃料电池的纤维增强基质的方法包括以下步骤：在混合LiAlO 2粉末，分散剂，消泡剂和溶剂之后通过球磨该混合物制备浆料; 向制备的浆料中加入粘合剂，增塑剂和陶瓷纤维，混合材料，并对混合物进行球磨; 对球磨浆进行脱气; 并在成型后将脱气后的浆料干燥，其中LiAlO 2粉末选自γ-LiAlO 2，β-LiAlO 2和α-Al 2 O 3，LiAlO 2粉末是LiAlO 2 HSA（高表面积）具有5微米或更小的尺寸和尺寸为10微米或更小的LiAlO 2 LSA（低表面积），并且LSA基于100重量份纤维和粉末为10至30重量份，其中陶瓷纤维为选自α-Al 2 O 3，γ-LiAlO 2，β-LiAlO 2，α-LiAlO 2，LiZrO 3，Y 2 O 3稳定的ZrO 3，LiTaO 3，LiNbO 3和CeO 2，并且以基于100重量份的5至20重量份的粉末和纤维，并且其中使用10至40重量份的粘合剂，10至40重量份的增塑剂，1至5重量份的消泡剂，1至2重量份的分散剂和150至250重量份的溶剂在100重量份的粉末和纤维上。

6. 发明授权

KR100960870B1 벌집형 고체산화물연료전지의 단전지, 이를 이용한 스택 및이들의 제조방법 失效
标题翻译：蜂窝型固体氧化物燃料电池的单位电池，使用单电池的堆叠以及用于制造单位电池和堆叠的方法
公开(公告)号：KR100960870B1
公开(公告)日：2010-06-04
申请号：KR1020080090965
申请日：2008-09-17
申请人： 한국과학기술연구원
发明人： 윤성필 , 임태훈 , 홍성안 , 오인환 , 남석우 , 한종희 , 정종필 , 이광수 , 김영천 , 김형준 , 조은애 , 김수길 , 이상엽
IPC分类号： H01M8/10 , H01M8/24
CPC分类号： H01M8/2435 , H01M4/9033 , H01M4/9066 , H01M8/1246 , H01M8/2404 , H01M8/2483 , Y02E60/525 , Y02P70/56
摘要： 본 발명에서는, 복수의 채널을 구비하는 벌집형 SOFC의 단전지로서, 상기 단전지는 공기극이 형성된 공기극 채널과 연료극이 형성된 연료극 채널이 교대로 형성되는 채널들을 구비하고, 상기 공기극 채널 및 연료극 채널의 각각의 내부에는 집전체가 설치되어 있고, 상기 집전체가 설치된 상기 채널들에는 충전 재료가 충전되는 벌집형 SOFC의 단전지, 이를 이용한 스택 및 이들의 제조방법을 제공한다. 본 발명에 따르면, 고성능의 특히 휴대용 또는 소형 벌집형 SOFC에 있어서, 효과적이고 용이한 전기 집전이 가능할 뿐만 아니라, 적층과 밀봉이 용이하며, 연료를 채널 내부에서 직접 개질 하는 것이 가능하다.
벌집형, 고체산화물연료전지, 연료극, 공기극, 단전지, 스택, 집전, 비드

7. 发明公开

KR1020100032023A 벌집형 고체산화물연료전지의 단전지, 이를 이용한 스택 및이들의 제조방법 失效
标题翻译：蜂窝型固体氧化物燃料电池单元，使用单元电池的堆栈和制造单元电池和堆叠的方法
公开(公告)号：KR1020100032023A
公开(公告)日：2010-03-25
申请号：KR1020080090965
申请日：2008-09-17
申请人： 한국과학기술연구원
发明人： 윤성필 , 임태훈 , 홍성안 , 오인환 , 남석우 , 한종희 , 정종필 , 이광수 , 김영천 , 김형준 , 조은애 , 김수길 , 이상엽
IPC分类号： H01M8/10 , H01M8/24
CPC分类号： H01M8/2435 , H01M4/9033 , H01M4/9066 , H01M8/1246 , H01M8/2404 , H01M8/2483 , Y02E60/525 , Y02P70/56
摘要： PURPOSE: A unit cell of a honeycomb-type solid oxide fuel cell is provided to enable effective and easy electric collection, and to facilitate lamination and sealing in portable or small honeycomb-type solid oxide fuel cell. CONSTITUTION: A unit cell of a honeycomb-type SOFC(100) comprises a plurality of channels. The unit cell comprises channels in which an air electrode channel(10) is formed and a fuel electrode channel(20) in which a fuel electrode is formed; current collectors(30,40) inside the air electrode and fuel electrode. A filling material is filled into the channels in which the current collector is installed.
摘要翻译：目的：提供蜂窝型固体氧化物燃料电池的单体电池，以便有效且容易的电收集，并且便于便携式或小型蜂窝型固体氧化物燃料电池中的层压和密封。构成：蜂窝型SOFC（100）的单元电池包括多个通道。单元电池包括形成有空气电极通道（10）的通道和形成有燃料电极的燃料电极通道（20）; 空气电极和燃料电极内的集电器（30,40）。将填充材料填充到其中安装集电器的通道中。

8. 发明授权

KR100759831B1 용융탄산염 연료전지용 강화 매트릭스 및 그 제조 방법 失效
标题翻译：用于碳酸氢盐燃料电池的增强基质及其制备方法
公开(公告)号：KR100759831B1
公开(公告)日：2007-09-18
申请号：KR1020060112314
申请日：2006-11-14
申请人： 한국과학기술연구원
发明人： 함형철 , 홍성안 , 오인환 , 임태훈 , 남석우 , 윤성필 , 한종희 , 이재영 , 김형준 , 조은애 , 이광수 , 하흥용 , 이상엽
IPC分类号： H01M8/02 , H01M8/14
CPC分类号： H01M8/142 , Y02P70/56
摘要： A reinforced matrix for a molten carbonate fuel cell, and a method for preparing the reinforced matrix are provided to improve mechanical strength and to lower manufacturing cost by using a reinforcing agent having a melting point. A reinforced matrix is a sintered body of a mixture comprising LiAlO2 as a matrix powder particle and B2O3 as a reinforcing agent. Preferably the LiAlO2 powder has a particle size of 1 micrometer or less. Preferably the reinforced matrix comprises 100 parts by weight of LiAlO2 and B2O3; 10-40 parts by weight of a binder; 10-40 parts by weight of a plasticizer; 1-5 parts by weight of an antifoaming agent; 1-2 parts by weight of a dispersant; and 140-350 parts by weight of a solvent.
摘要翻译：提供了一种用于熔融碳酸盐燃料电池的增强基体和用于制备增强基体的方法，以通过使用具有熔点的增强剂来提高机械强度并降低制造成本。增强基体是包含LiAlO 2作为基质粉末颗粒和B 2 O 3作为增强剂的混合物的烧结体。优选地，LiAlO 2粉末具有1微米或更小的粒度。优选地，增强基体包含100重量份的LiAlO 2和B 2 O 3; 10-40重量份的粘合剂; 10-40重量份的增塑剂; 1-5重量份的消泡剂; 1-2重量份的分散剂; 和140-350重量份的溶剂。

9. 发明授权

KR100779741B1 소결보조제 함유 용융탄산염 연료전지용 강화 매트릭스 失效
标题翻译：含有碳酸钙燃料电池的加固基质
公开(公告)号：KR100779741B1
公开(公告)日：2007-11-28
申请号：KR1020060132459
申请日：2006-12-22
申请人： 한국과학기술연구원
发明人： 함형철 , 윤성필 , 남석우 , 한종희 , 임태훈 , 오인환 , 이광수 , 김영천
IPC分类号： H01M8/02 , H01M8/14 , B82Y30/00
CPC分类号： Y02E60/526 , H01M8/142 , H01M2008/147
摘要： A reinforced matrix for a molten carbonate fuel cell and a method for preparing the reinforced matrix are provided to improve mechanical strength by increasing sintering velocity. A reinforced matrix for a molten carbonate fuel cell is prepared by mixing a LiAlO2 powder as a matrix and 0.5-10 wt% of a gamma-Al2O3 powder as a sintering aid based on the weight of the LiAlO2 powder; and sintering the mixture. Preferably the gamma-Al2O3 powder has a particle size of 10-90 nm; and the LiAlO2 powder comprises a powder having a particle size of 1 micrometer or less, or a mixture comprising a powder having a particle size of 1 micrometer or less and a powder having a particle size of 10 micrometers or more.
摘要翻译：提供了一种用于熔融碳酸盐燃料电池的增强基体和用于制备增强基体的方法，以通过提高烧结速度来提高机械强度。通过以作为基质的LiAlO 2粉末和基于LiAlO 2粉末的重量的0.5-10重量％的作为烧结助剂的γ-Al 2 O 3粉末混合来制备用于熔融碳酸盐燃料电池的增强基体; 并烧结混合物。优选地，γ-Al 2 O 3粉末具有10-90nm的粒径; 并且LiAlO 2粉末包含粒径为1微米或更小的粉末，或包含粒径为1微米或更小的粉末和具有10微米或更大的粒度的粉末的混合物。

10. 发明授权

KR100445380B1 연료전지 운전용 가스 공급 장치 失效
标题翻译：联络电话机
公开(公告)号：KR100445380B1
公开(公告)日：2004-08-25
申请号：KR1020020009991
申请日：2002-02-25
申请人： 한국과학기술연구원
发明人： 오인환 , 신석재 , 하흥용 , 홍성안 , 임태훈 , 남석우 , 윤성필 , 한종희 , 김영천 , 이광수
IPC分类号： H01M8/04
摘要： 본 발명은 연료전지 운전용 가스 공급 장치에 관한 것으로, 특히 고압에서도 운전이 가능하고, 연료전지에 공급되는 가스의 가습 상태를 간단하게 조절할 수 있으며, 운전 중에도 가습에 필요한 물을 보충할 수 있는 연료전지 운전용 가스 공급 장치에 관한 것이다.
종래 연료전지 가스 공급 장치는 항상 반응가스를 가습시킨 후에 연료전지에 공급하기 때문에 가습에 필요한 물을 빈번하게 보충해야 하고, 개폐식 마개가 구비된 가습병을 사용하기 때문에 가습병에 물을 보충 할 경우 연료전지 운전을 중지해야 하며, 가습된 반응가스와 연료전지 가스 공급관의 온도차로 인하여 반응가스가 응축되어 연료전지의 성능이 감소하는 문제점이 있었다.
본 발명은 가습 상태 조절 밸브를 통해 무가습 상태에서도 연료전지를 운전할 수 있고, 일체형 금속으로 제작된 밀폐된 용기를 사용함으로써 고압에서도 연료전지 운전이 가능하며, 물 보충용 밸브를 통해 연료전지를 운전하는 중에도 가습에 필요한 물을 보충할 수 있으며, 연료전지 가스 공급관의 가열 및 단열을 통해 가습된 반응가스가 연료전지에 공급될 때까지 동일한 가습 상태를 유지하게 함으로써, 반응가스의 응축 및 냉각으로 연료전지의 성능이 감소하는 것을 방지하는 효과가 있다.
摘要翻译：目的：提供一种用于操作燃料电池的气体供给装置，以允许装置在高压下操作，供应给燃料电池的气体的加湿状态易于控制，并且加湿所需的水即使在手术过程中也要加以补充。构成：气体供给装置在对加湿器内的气体供给源供给的反应气体进行加湿后，将反应气体供给到燃料电池，其中，加湿器具有容纳反应气体并利用水进行加湿的容器（30）加湿器气体供应管（13），其一侧插入到容器中以供应待加湿的反应气体; 供水管（33），用于将用于加湿反应气体的水供应到容器; 和与该容器连接的燃料电池气体供应管（15），以将加湿后的反应气体供应到燃料电池。优选地，在容器的外周设置可拆卸的夹套形容器加热器（35），用于通过加热来加热反应气体; 在供水管上设有补水阀（34）。