KR1019930002440B1 희토류원소함유 확산코팅층 형성방법 失效
标题翻译：用于生产包含稀土元素的扩散涂层的方法
公开(公告)号：KR1019930002440B1
公开(公告)日：1993-03-30
申请号：KR1019900022643
申请日：1990-12-31
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원
发明人： 성병근 , 황순영 , 송진화 , 김규영
IPC分类号： C23C10/00
摘要： A diffusion coated layer containing rare earth elements is formed by (1) making a packing powder composed of 1-5 wt.% aluminum (Al) powder, 1-5 wt.% halide compound and the balance alumina (Al2O3), (2) mixing the packing powder with 10-50 wt.% (based on the weight of the packing powder) rare earth powder, (3) mixing the mixture with dilute organic binder solution, (4) coating a surface of a metal with the obtained mixed solution and drying in the air, (5) burying the dried metal in a retort filled with packing powder, (6) forming aluminide coating layer containing rare earth elements on the metal by charging the retort in a furnace maintaining the temperature range to 800-1,100 deg.C and vacuum or inert gas atmosphere, for 1-10 hours.
摘要翻译：通过（1）制造由1-5重量％的铝（Al）粉末，1-5重量％的卤化物和余量的氧化铝（Al 2 O 3）组成的填充粉末，（2））将包装粉末与10-50重量％（以包装粉末重量计）的稀土粉末混合，（3）将混合物与稀有机粘合剂溶液混合，（4）用所得到的金属表面涂覆混合溶液并在空气中干燥，（5）将干燥的金属埋入填充有填充粉末的蒸馏器中，（6）通过在炉中加入蒸馏器在炉中形成含有稀土元素的铝化物涂层，保持温度范围为800 -1,100℃，真空或惰性气体气氛，1-10小时。

2. 发明公开

KR1019920012507A 희토류원소함유 확산코팅층 형성방법 失效
标题翻译：形成含稀土元素的扩散涂层的方法
公开(公告)号：KR1019920012507A
公开(公告)日：1992-07-27
申请号：KR1019900022643
申请日：1990-12-31
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원
发明人： 성병근 , 황순영 , 송진화 , 김규영
IPC分类号： C23C10/00
摘要： 내용 없음

3. 发明授权

KR1019960010165B1 니켈기 초합금의 알루미나이드-이트륨 복합코팅층 형성방법 失效
标题翻译：镍基复合材料的制备方法镍基合金的涂层
公开(公告)号：KR1019960010165B1
公开(公告)日：1996-07-26
申请号：KR1019930027044
申请日：1993-12-09
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원
发明人： 김익현 , 정환교 , 김선효 , 김규영
IPC分类号： C23C10/34
摘要： The composite coated layer is prepared by coating aluminide on nickel base superalloy by the pack cementation method and plating yttrium by the ion plating method; heating the composite coated layer of aluminide-yttrium under inert gas for 2hrs at 1000-1300deg.C.
摘要翻译：通过包装胶结法在镍基超级合金上涂覆铝化物并通过离子镀法镀钇制备复合涂层; 在1000-1300℃下，在惰性气体下加热铝化钇复合涂层2小时。

4. 发明公开

KR1019950018625A 니켈기 초합금의 알루미나이드-이트륨 복합코팅층 형성방법 失效
标题翻译：形成镍基高温合金的氧化铝 - 钇复合涂层的方法
公开(公告)号：KR1019950018625A
公开(公告)日：1995-07-22
申请号：KR1019930027044
申请日：1993-12-09
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원
发明人： 김익현 , 정환교 , 김선효 , 김규영
IPC分类号： C23C10/34
摘要： 본 발명은 가스터빈 엔진의 터빈 블레이드 재료등에 사용되는 니켈기 초합금의 알루미나이드-이트륨 복합코팅층을 형성하는 방법에 관한 것으로써, 알루미나이징과 이온플레이팅을 행한후 최종적으로 열처리를 행하므로서, 내열, 내식성을 현저히 향상시킬 수 있는 니켈기 초합금의 알루미나이드-이트륨 복합코팅층 형성방법을 제공하고자 하는데, 그 목적이 있다.
본 발명은 니켈기 초합금의 알루미나이드-이트륨 복합코팅층을 형성시키는 방법에 있어서, 통상의 팩 세멘테이션법을 이용하여 니켈기 초합금을 알루미나이드 확산코팅처리하는 단계; 통상의 이온플레이팅 법을 이용하여 이온플레이팅하는 단계; 및 상기 단계에서 형성된 알루미나이드-이트륨 복합코팅층을 1000-1300℃에서 2시간이상 비산화성 분위기에서 열처리하는 단계를 포함하여 구성됨을 특징으로 니켈기 초합금의 알루미나이드-이트륨 복합코팅층 형성방법을 그 요지로 한다.

5. 发明授权

KR1019940001346B1 알루미늄 확산 코팅된 내열스테인레스강 및 그 코팅방법 失效
标题翻译：具有铝扩散涂层的耐热不锈钢及其涂覆方法
公开(公告)号：KR1019940001346B1
公开(公告)日：1994-02-19
申请号：KR1019910025135
申请日：1991-12-30
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원
发明人： 성병근 , 황순영 , 송진화 , 김규영
IPC分类号： C23C10/48
CPC分类号： C23C10/50
摘要： The diffusion coating of Al is applied to a stainless steel workpiece by burying it in a pack containing an Al source, an activator and inert filler materials. The steel and powder is heated at 850-1025 deg.C for 0.5-20 hours. An outer aluminide layer and a chromium rich intermediate layer is formed on the stainless steel without forming an interdiffusion layer containing aluminide precipitates under the aluminide layer. The Al-coated stainless steel is used as high temperature components in the petroleum, chemical and steel industries.
摘要翻译：将Al的扩散涂层通过将其埋入包含Al源，活化剂和惰性填充材料的包装中而施加到不锈钢工件上。钢和粉末在850-1025℃加热0.5-20小时。在不锈钢上形成外铝化物层和富铬中间层，而不在铝化物层下形成含有铝化物析出物的相互扩散层。铝涂层不锈钢用作石油，化工和钢铁行业的高温部件。

6. 发明授权

KR100065361B1 희토류원소함유 확산코팅층 형성방법 失效
公开(公告)号：KR100065361B1
公开(公告)日：1993-09-10
申请号：KR1019900022643
申请日：1990-12-31
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원
发明人： 성병근 , 황순영 , 송진화 , 김규영
IPC分类号： C23C10/00

7. 发明公开

KR1019930013197A 알루미늄 확산 코팅된 내열스테인레스강 및 그 코팅방법 失效
公开(公告)号：KR1019930013197A
公开(公告)日：1993-07-21
申请号：KR1019910025135
申请日：1991-12-30
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원
发明人： 성병근 , 황순영 , 송진화 , 김규영
IPC分类号： C23C10/48
摘要： 본 발명은 항공기엔진의 부품등에 사용되는 내열 스테인레스강의 알루미나이드 코팅방법에 관한 것으로서, 다량의 Ni및 Cr을 함유하는 내열 스테인레스강에 대하여 알루미늄 확산 코팅시에 알루미나이드층 아래에 크롬을 주성분으로 하는 중간층을 형성시켜 코팅의 내열 내식성을 향상시킬수 있는 내열 스테인레스강의 알루미늄 확산 코팅방법 및 그 코팅층을 제공하고자 하는데, 그 목적이 있다.
본 발명은 알루미늄공급원, 활성제, 및 소결방지제로 조성되는 확산피복 팩분알에 내열 스테인레스강을 묻고, 850-1025℃에서 코팅처리하여 알루미나이드 층 아래에 상호확산층 형성없이 크롬을 주성분으로 하는 중간층을 형성하도록 구성되는 내열 스테인레스강의 알루미늄 확산코팅방법 및 이방법에 의해 제조된 코팅층을 그 요지로 한다.

8. 发明授权

KR1019930002441B1 내열 스텐레스강의 알루미늄 확산코팅방법 및 코팅된 내열 스텐레스강 失效
标题翻译：在耐热不锈钢上进行扩散加热的方法及其由生产工艺生产的方法
公开(公告)号：KR1019930002441B1
公开(公告)日：1993-03-30
申请号：KR1019900022638
申请日：1990-12-31
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원
发明人： 황순영 , 송진화 , 성병근 , 김규영
IPC分类号： C23C10/48
摘要： A method for diffusion coating of aluminum on a nickel based super heat resistant alloy comprises (1) charging a heat resistant stainless steel into the packing powder, which containes 1-10 wt.% of a hallogen compound which is selected from NH4Cl, NH4F, NaCl and NaF, 3-30 wt.% aluminum (Al) powder having the grain size of 50-200 meshes and the balance alumina (Al2O3) powder having the grain size of 100-200 meshes; (2) diffusion coating in the temperature range of 800-1,100 deg.C hours under reduction atmosphere for 3-15. And the thickness of the aluminum diffusion coating layer on the heat resistant stainless steel surface is 50-150 μm.
摘要翻译：一种在镍基超耐热合金上扩散涂覆铝的方法包括（1）将耐热不锈钢装入填料粉末中，该填料粉末含有1-10重量％的选自NH 4 Cl，NH 4 F， NaCl和NaF，3-30重量％的粒径为50-200目的铝（Al）粉末和平均粒径为100-200目的氧化铝（Al 2 O 3）粉末; （2）在还原气氛下在800-1100℃的范围内扩散涂层3-15。耐热不锈钢表面铝扩散涂层的厚度为50-150μm。

9. 发明公开

KR1019920012508A 내열 스텐레스강의 알루미늄 확산코팅방법 및 코팅된 내열 스텐레스강 失效
标题翻译：铝耐热不锈钢扩散涂层法和涂层耐热不锈钢
公开(公告)号：KR1019920012508A
公开(公告)日：1992-07-27
申请号：KR1019900022638
申请日：1990-12-31
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원
发明人： 황순영 , 송진화 , 성병근 , 김규영
IPC分类号： C23C10/48
摘要： 내용 없음

10. 发明授权

KR100074901B1 알루미늄 확산 코팅된 내열스테인레스강 및 그 코팅방법 失效
公开(公告)号：KR100074901B1
公开(公告)日：1994-06-29
申请号：KR1019910025135
申请日：1991-12-30
申请人： 주식회사 포스코 , 재단법인 포항산업과학연구원
发明人： 성병근 , 황순영 , 송진화 , 김규영
IPC分类号： C23C10/48