The invention discloses an after-finishing embossing technology for an imitated leather embossed fabric. The technology comprises the following steps: preparing a resin treating fluid comprising the following compositions in parts by weight: 75g-100g/kg of water-soluble wear-resistant resin, 20g-30g/kg of hexamethylolmelamine resin, 20g-30g/kg of a softening agent, 4g-5g/kg of a catalyst; completely soaking the imitated leather fabric in the resin treating fluid, then drying, embossing by adopting a glazing calender, and controlling the total pressure of embossing to be 1.8-2.0*108MPa, and the embossing temperature to be 190-200 DEG C; after embossing, roasting the imitated leather fabric. By adopting the low-temperature high-pressure embossing technology, the imitated leather embossed fabric has the relatively strong three-dimensional feeling while the excellent wear resistance, resilience and breaking strength and tearing strength of the fabric is guaranteed.