71. 发明公开

KR1020100019561A 영구적으로 습윤 가능한 미세 섬유 격리판을 갖는 배터리 无效
标题翻译：电池与永久湿纺纤维分离器
公开(公告)号：KR1020100019561A
公开(公告)日：2010-02-18
申请号：KR1020107000266
申请日：2008-06-11
申请人： 이 아이 듀폰 디 네모아 앤드 캄파니
发明人： 아로라,판카즈 , 김,영,에이치. , 프리스크,시몬
IPC分类号： H01M10/24 , H01M2/16
CPC分类号： H01M10/24 , H01M2/162 , H01M6/04 , H01M6/22 , H01M10/345
摘要： Alkaline batteries are disclosed that advantageously include separators comprising at least one porous layer of fine fibers having a diameter of between about 50 nm and about 3000 nm that provide improved combinations of reduced thickness, dendritic barrier against short-circuiting and low ionic resistance as compared with known battery separators. The fine fibers show improved wet-ability in the alkaline electrolytes.
摘要翻译：公开了碱性电池，其有利地包括分离器，其包括直径在约50nm和约3000nm之间的至少一个细小纤维多孔层，其提供了减小的厚度，抗短路的树枝状屏障和低离子电阻的改善的组合，与已知的电池分离器。细纤维在碱性电解质中显示出改进的湿润性能。

72. 发明授权

KR100925862B1 조성물, 아연 전극, 배터리 및 그들의 제조방법 有权
标题翻译：组合物，锌电极，电池及其制造方法
公开(公告)号：KR100925862B1
公开(公告)日：2009-11-06
申请号：KR1020087004364
申请日：2002-03-15
申请人： 매시 유니버시티 마너와투 (투리티아)
发明人： 할사이먼버너즈 , 리우진롱
IPC分类号： C01G9/00 , H01M4/60 , H01M10/24
CPC分类号： H01M4/244 , H01M4/364 , H01M4/48 , H01M4/62 , H01M4/628 , H01M10/24 , H01M10/26 , Y02E60/124 , Y10T29/49108
摘要： 사이클 수명이 향상된 재충전가능한 전기화학적 전지용 조성물, 그의 제조방법 및 활성 매스로서 상기 조성물을 함유하는 아연 전극이 설명된다. 본 발명의 전극 활성 매스는 전기화학적으로 활성적인 아연 소스와 적어도 한가지의 지방산 또는 그의 염, 에스테르 또는 유도체 또는 알킬 설폰산 또는 그의 염 또는 에스테르 또는 유도체를 포함한다. 본 발명의 아연 전극은 공지의 아연 전극에 비해 낮은 형상변형과 감소된 수지형돌기 형성을 나타내는 것으로 추정되므로, 그로부터 수차례의 충전/방전 사이클을 통해서도 개선된 용량 보유율을 갖는 전기화학적 전지를 만드는 것이 가능하다.
아연 전극, 충전, 방전, 전기화학적 전지

73. 发明授权

KR100898076B1 폐망간전지 및 알카라인전지 재활용 장치 및 방법 失效
标题翻译：二氧化碳和碱性电池的回收设备及其方法
公开(公告)号：KR100898076B1
公开(公告)日：2009-05-18
申请号：KR1020070086836
申请日：2007-08-29
申请人： 주식회사 반디신소재
发明人： 임형학
IPC分类号： B09B3/00 , H01M10/54 , B02C13/00 , B03C1/00
CPC分类号： B03B9/061 , B03B2009/066 , C22B1/005 , C22B7/005 , C22B19/30 , H01M10/24 , H01M10/54 , H01M12/06 , Y02P10/216 , Y02W30/521 , Y02W30/526 , Y02W30/84
摘要： 본 발명은 폐망간전지 및 알카라인전지 재활용 장치 및 방법에 관한 것으로, 폐망간전지 및 알카라인전지를 그 형상에 따라 철재피복전지와 랜턴 전지로 선별하여 상기 철재피복전지는 파쇄, 분쇄, 입도 선별, 자력 선별 공정을 통해 철재조각과 이산화망간을 주로 포함하는 폐전지분말을 회수하여 재활용 처리하고, 상기 철재피복전지의 가연성잔여물과 상기 랜턴 전지는 열분해 탄화, 1차 분쇄, 1차 입도선별, 2차 분쇄, 2차 입도선별을 통해 아연괴, 탄소봉, 및 그외 나머지 탄화물들의 총 혼합물인 이산화망간을 주로 포함하는 폐전지분말을 유가물로 회수하여 100% 재활용처리한다.
본 발명에 의하면, 종래의 폐망간전지 및 알카라인전지 매립 시 발생하는 사회적 비용 소요 및 환경오염 문제를 완벽하게 해소하고, 종래의 폐망간전지 및 알카라인전지 재활용 기술들과 비교해 볼 때, 종래기술로는 회수하지 못하던 전도성 탄소봉을 포함하여 철재조각, 아연괴, 및 그외 나머지 물질들의 총 혼합물인 이산화망간을 주로 포함하는 폐전지분말 등의 유가물을 상대적으로 저렴한 비용으로 회수할 수 있다.
망간전지, 알카라인전지, 재활용

74. 发明授权

KR100887810B1 알칼리 전지용 증점제 및 알칼리 전지 失效
标题翻译：碱性电池和碱性电池的增稠剂
公开(公告)号：KR100887810B1
公开(公告)日：2009-03-09
申请号：KR1020077005397
申请日：2005-09-06
申请人： 산요가세이고교 가부시키가이샤
发明人： 오타니가즈야 , 야마구치다케아키
IPC分类号： H01M6/22 , H01M6/06 , C08L33/02 , C08L63/00
CPC分类号： H01M4/621 , H01M4/02 , H01M4/244 , H01M4/26 , H01M4/62 , H01M4/622 , H01M6/06 , H01M6/08 , H01M6/22 , H01M10/24 , H01M10/30 , H01M10/345 , H01M2300/0014 , H01M2300/0085
摘要： 본 발명은 1시간 후의 겔 점도(N1h)와 12시간 후의 겔 점도(N12h)의 비(N1h/N12h)가 0.7∼1.3인 알칼리 전지용 증점제(여기에서 겔 점도는, 증점제 2.0중량부, 아연 분말 200중량부 및 37중량% 수산화칼륨 수용액 100중량부로 이루어지는 겔의 JIS K7117-1:1999에 준거하여 측정한 40℃에 있어서의 점도), 및 이것을 음극 겔 중에 이용한 알칼리 전지에 관한 것이다. 본 발명의 증점제를 이용한 알칼리 전지는, 장기에 걸친 방전 특성(방전량 및 방전 시간)의 유지, 내충격성이 개선된 알칼리 전지로 할 수 있다.
摘要翻译：本发明非0.7（N1H / N12h）至1.3是碱性电池的增稠剂（其中凝胶的粘度，增稠剂，2.0重量份锌粉末，200一小时凝胶粘度（N1H），和之后12小时后的凝胶粘度（N12h）重量份JIS K7117-1凝胶，其包含100重量份的氢氧化钾水溶液的37％（重量）：涉及粘度40℃根据1999测得），并且这在碱性电池使用该负极凝胶。使用本发明的增稠剂的碱性电池可以维持在碱性电池中，放电特性的提高耐冲击性（放电量和放电时间）在一段长的时间。

75. 发明公开

KR1020090021928A 폐망간전지 및 알카라인전지 재활용 장치 및 방법 失效
标题翻译：使用的锌碳和碱性电池的回收装置及其方法
公开(公告)号：KR1020090021928A
公开(公告)日：2009-03-04
申请号：KR1020070086836
申请日：2007-08-29
申请人： 주식회사 반디신소재
发明人： 임형학
IPC分类号： B09B3/00 , H01M10/54 , B02C13/00 , B03C1/00
CPC分类号： B03B9/061 , B03B2009/066 , C22B1/005 , C22B7/005 , C22B19/30 , H01M10/24 , H01M10/54 , H01M12/06 , Y02P10/216 , Y02W30/521 , Y02W30/526 , Y02W30/84
摘要： A recycling apparatus for used zinc-carbon and alkaline batteries and a method thereof are provided to recycle the batteries by using a crusher, a pulverizing device, a selector and a heat resolution brazier. A recycling apparatus for used zinc-carbon and alkaline batteries comprises the followings: a first pulverizing device(130) pulverizing a crushed battery coated with an iron material; a fist vibration selector(140) collecting waste battery powder by using a wire net; a magnetic separator(150) collecting the iron material; a heat resolution brazier(160) carbonizing a final residue; a second pulverizing device(170) peeling off waste battery carbide; a second vibration separator(180) collecting lantern battery carbon; a third pulverizing device(190) pulverizing the first grinded waste battery carbide; and a third vibration separator(200) classifying waste battery powder, a terminal spring and a cathode spelter of the lantern battery.
摘要翻译：提供了一种用于使用的锌 - 碳和碱性电池的回收设备及其方法，用于通过使用破碎机，粉碎装置，选择器和分辨热分析器来回收电池。用于使用的锌 - 碳和碱性电池的回收设备包括：第一粉碎装置（130），粉碎用铁材料涂覆的破碎电池; 通过使用丝网收集废电池粉末的第一振动选择器（140）; 收集铁材料的磁选机（150）; 热分解火焰（160）碳化最终残渣; 剥离废电池碳化物的第二粉碎装置（170）收集灯笼电池碳的第二振动分离器（180）第一粉碎装置（190），粉碎所述第一研磨废电池碳化物; 以及对所述灯笼电池的废电池粉末，端子弹簧和阴极装置进行分类的第三振动分离器（200）。

76. 发明公开

KR1020080077972A 폴리올레핀 미세 다공막 및 그 제조 방법, 및 전지용세퍼레이터 및 전지 有权
标题翻译：微孔聚烯烃薄膜，其制造方法，细胞和细胞分离器
公开(公告)号：KR1020080077972A
公开(公告)日：2008-08-26
申请号：KR1020087013387
申请日：2006-11-22
申请人： 도레이 배터리 세퍼레이터 필름 주식회사
发明人： 기미시마고타로 , 가이마이노리미쓰
IPC分类号： C08J9/22 , C08J9/26 , C08J5/22 , H01M10/05
CPC分类号： H01M10/4235 , H01M2/1653 , H01M10/052 , H01M10/24 , Y10T428/249921
摘要： A microporous polyolefin membrane characterized by comprising a polyethylene resin. It is further characterized in that (a) the shutdown temperature is 135°C or lower which is the temperature at which the gas permeability as measured with heating at a heating rate of 5 °C/min reaches 1x10^5 sec/100 cm^3, (b) the maximum degree of melt shrinkage in the transverse direction in the temperature range of 135-145°C is 40% or lower as measured by thermomechanical analysis at a load of 2 gf and a heating rate of 5 °C/min, and (c) the meltdown temperature is 150°C or higher which is the temperature at which the gas permeability as measured with further continuous heating beyond the shutdown temperature reaches 1x10^5 sec/100 cm^3 again.
摘要翻译：其特征在于包含聚乙烯树脂的微孔聚烯烃膜。其特征还在于，（a）关闭温度为135℃以下，即以5℃/分钟的加热速度加热测定的气体渗透性为1×10 5秒/ 100cm -1时的温度，如图3所示，（b）在135-145℃的温度范围内，横向的最大熔融收缩度为40％以下，通过热负荷分析法测定，负荷为2gf，加热速度为5℃/ min，（c）熔融温度为150℃以上，即再次连续加热测定的透气度再次达到1×10 5秒/ 100cm 3以上的温度。

77. 发明授权

KR100853565B1 조성물, 아연 전극, 배터리 및 그들의 제조방법 有权
标题翻译：组合物，锌电极，电池及其制造方法
公开(公告)号：KR100853565B1
公开(公告)日：2008-08-22
申请号：KR1020037012050
申请日：2002-03-15
申请人： 매시 유니버시티 마너와투 (투리티아)
发明人： 할사이먼버너즈 , 리우진롱
IPC分类号： H01M4/60
CPC分类号： H01M4/244 , H01M4/364 , H01M4/48 , H01M4/62 , H01M4/628 , H01M10/24 , H01M10/26 , Y02E60/124 , Y10T29/49108
摘要： 사이클 수명이 향상된 재충전가능한 전기화학적 전지용 조성물, 그의 제조방법 및 활성 매스로서 상기 조성물을 함유하는 아연 전극이 설명된다. 본 발명의 전극 활성 매스는 전기화학적으로 활성적인 아연 소스와 적어도 한가지의 지방산 또는 그의 염, 에스테르 또는 유도체 또는 알킬 설폰산 또는 그의 염 또는 에스테르 또는 유도체를 포함한다. 본 발명의 아연 전극은 공지의 아연 전극에 비해 낮은 형상변형과 감소된 수지형돌기 형성을 나타내는 것으로 추정되므로, 그로부터 수차례의 충전/방전 사이클을 통해서도 개선된 용량 보유율을 갖는 전기화학적 전지를 만드는 것이 가능하다.
아연 전극, 충전, 방전, 전기화학적 전지

78. 发明授权

KR100814881B1 전지용 활물질, 이를 포함하는 전극 및 전지 有权
标题翻译：用于电池的活性材料，以及包含其的电极和电池
公开(公告)号：KR100814881B1
公开(公告)日：2008-03-18
申请号：KR1020060117083
申请日：2006-11-24
申请人： 삼성에스디아이 주식회사
发明人： 김점수 , 박용철 , 이종화 , 허소현 , 정의영
IPC分类号： H01M4/36 , H01M4/02 , H01M10/02
CPC分类号： H01M4/5825 , H01M4/362 , H01M4/602 , H01M10/052 , H01M10/0525 , H01M10/06 , H01M10/24 , H01M10/30
摘要： An active material for a battery is provided to realize excellent lithium ion conductivity and to inhibit a core material from reacting with an electrolyte, thereby imparting excellent capacity, lifespan and thermal stability to a battery. An active material(1) for a battery comprises: a core material(3) comprising a compound capable of electrochemical oxidation/reduction; and a lithium ion conductive layer(5) surrounding the core material, wherein the lithium ion conductive layer comprises a compound selected from lithium ion conductors, lithium ion conductive polymers and mixtures thereof, and the lithium ion conductor is a compound represented by the formula of Li1+yM2-yXz (wherein M is selected from the group consisting of alkali metals, alkaline earth metals, Group 13 and 14 elements, transition metals, rare earth metals and combinations thereof, X is selected from the group consisting of -(PO4), -(VO4), -(NbO4) and combinations thereof, y ranges from 0 to 2, and z ranges from 1 to 3).
摘要翻译：提供了一种用于电池的活性材料，以实现优异的锂离子传导性，并且抑制芯材与电解质反应，从而赋予电池优异的容量，寿命和热稳定性。一种用于电池的活性材料（1）包括：包含能够进行电化学氧化/还原的化合物的芯材（3）以及包围所述芯材的锂离子传导层（5），其中所述锂离子传导层包含选自锂离子导体，锂离子导电聚合物及其混合物的化合物，并且所述锂离子导体是由式 Li1 + yM2-yXz（其中M选自碱金属，碱土金属，第13族和第14族元素，过渡金属，稀土金属及其组合，X选自 - （PO 4）， - （VO4）， - （NbO4）及其组合，y的范围为0至2，z的范围为1至3）。

79. 发明公开

KR1020070102280A 대용량 니켈/수소저장합금 이차전지의 극판군 구조 失效
标题翻译：大容量镍/金属氢氧化物二次电池电极组的结构
公开(公告)号：KR1020070102280A
公开(公告)日：2007-10-18
申请号：KR1020060034213
申请日：2006-04-14
申请人： 에너그린(주)
发明人： 노남종 , 양준현 , 양상기 , 김영록 , 김세강
IPC分类号： H01M4/02 , H01M10/04
CPC分类号： H01M10/345 , C01B3/0031 , H01M2/0217 , H01M10/24 , Y02E60/124
摘要： A structure of an electrode plate assembly for a large capacity nickel/metal storage alloy secondary battery is provided to prevent the pollution in a battery container and to improve the low temperature discharge performance. A structure of an electrode plate assembly for a large capacity nickel/hydrogen storage alloy secondary battery includes an electrode plate assembly comprising a plurality of positive electrode plates(10) connected to a positive electrode pole(30), a plurality of negative electrode plates(20) connected to a negative electrode pole(40), and separating membranes(50) installed at all space between the positive electrode plate and the negative electrode plate, wherein the electrode plate assembly is wrapped by a contractible tube, and the positive electrode plate and the negative electrode plate have a pocket type or a paste type.
摘要翻译：提供一种用于大容量镍/金属储存合金二次电池的电极板组件的结构，以防止电池容器中的污染并提高低温放电性能。用于大容量镍/氢储存合金二次电池的电极板组件的结构包括：电极板组件，其包括连接到正极极（30）的多个正极板（10），多个负极板（ 20）连接到负极极（40），以及隔离膜（50），其安装在正极板和负极板之间的所有空间处，其中电极板组件被可收缩的管包裹，并且正极板负极板具有袋型或糊状。

80. 发明授权

KR100737663B1 2차전지 및 그 제조방법 有权
标题翻译：二次电池及其制造方法
公开(公告)号：KR100737663B1
公开(公告)日：2007-07-09
申请号：KR1020067000373
申请日：2005-03-09
申请人： 파나소닉 주식회사
发明人： 이쿠타시게오 , 후쿠모토유스케
IPC分类号： H01M4/02 , C04B41/87 , H01M4/04 , H01M10/05
CPC分类号： H01M4/24 , H01M2/164 , H01M4/02 , H01M4/04 , H01M4/131 , H01M4/133 , H01M4/48 , H01M10/04 , H01M10/052 , H01M10/0525 , H01M10/24 , H01M2004/021 , Y10T29/49115
摘要： 양극과, 음극과, 양극 및 음극의 적어도 한 쪽의 표면에 접착된 다공막을 구비하는 2차전지에 있어서, 다공막은, 세라믹스 입자 및 결착제를 포함하고, 세라믹스 입자는, 세라믹스 전구체로부터 직접 합성한 세라믹스 소성체를 기계적으로 해쇄한 다결정 입자를 포함한다. 다공막의 공극률은, 예를 들면 40∼80%이다. 다공막은, 세라믹스 전구체로부터 세라믹스 소성체를 얻는 공정과, 세라믹스 소성체를 기계적으로 해쇄하여 세라믹스 입자를 얻는 공정과, 세라믹스 입자와 결착제를 포함하는 슬러리를 얻는 공정과, 슬러리를 전극의 표면에 도포하여, 건조시키는 공정을 포함하는 방법에 의해 형성할 수 있다.
摘要翻译：在包含正极，负极和与正极和负极中的至少一个的表面接合的多孔膜的二次电池中，多孔膜包括陶瓷颗粒和粘合剂，陶瓷颗粒包括多晶颗粒通过机械粉碎包含由陶瓷前体直接合成的陶瓷的烧制材料获得。多孔膜的孔隙率例如为40〜80％。多孔膜可以通过以下方法形成：包括以下步骤：从陶瓷前体获得包含陶瓷的烧制材料; 通过机械破碎陶瓷烧制材料获得陶瓷颗粒; 得到包含陶瓷颗粒和粘合剂的浆料; 并将浆料施加到电极的表面上，然后干燥。