41. 发明公开

KR1020010065805A 속경화형 에폭시계 분체도료용 촉매 无效
标题翻译：催化剂用于快速硬化环氧粉末涂料
公开(公告)号：KR1020010065805A
公开(公告)日：2001-07-11
申请号：KR1019990065750
申请日：1999-12-30
申请人： 주식회사 케이씨씨
发明人： 김도훈 , 최승엽 , 권오원 , 현재규 , 김봉수
IPC分类号： C08G59/18
CPC分类号： C08G59/18 , C08G59/68 , C09D5/03
摘要： PURPOSE: Provided is a catalyst for quick hardened epoxy powder coating which promotes the reaction of epoxy binder resin and hardening agents so that it hardens the film of a metal surface for a short time. CONSTITUTION: The catalyst for quick hardened epoxy powder coating is characterized by reacting imidazole adduct compound wherein epoxy resin compound that consists of bisphenol-type epoxy resin and aliphatic epoxy resin and imidazole compound are mixed to metallic compound. The softening temperature of the catalyst is 90-120deg.C and its viscosity is 30-50 poise(150deg.C).
摘要翻译：目的：提供快速硬化环氧粉末涂料的催化剂，促进环氧树脂粘合剂树脂和硬化剂的反应，使其在短时间内硬化金属表面的膜。构成：用于快速硬化环氧粉末涂料的催化剂的特征在于使咪唑加合物化合物反应，其中由双酚型环氧树脂和脂族环氧树脂组成的环氧树脂化合物和咪唑化合物混合到金属化合物中。催化剂的软化温度为90〜120℃，粘度为30-50泊（150℃）。

42. 发明公开

KR1020010065804A 에폭시수지 분체도료용 다관능성 페놀 경화제의 제조방법 失效
标题翻译：用于环氧树脂粉末涂料的多功能酚醛硬化剂的生产工艺
公开(公告)号：KR1020010065804A
公开(公告)日：2001-07-11
申请号：KR1019990065749
申请日：1999-12-30
申请人： 주식회사 케이씨씨
发明人： 김봉수 , 최승엽 , 권오원 , 김도훈 , 신진철
IPC分类号： C08G8/10 , C08G59/00
摘要： PURPOSE: Provided is a production process of multi-functional phenol hardener for epoxy resin powder coating which reduces the generation of multiple holes within a hardening film after being exposed in water and doesn't lower the hardening speed. CONSTITUTION: The production process of multi-functional phenol hardener for epoxy resin powder coating is characterized by condensing epoxy resin compound wherein bisphenol-type epoxy resin shown in a chemical formula 1 and novolac epoxy resin shown in a chemical formula 2 are mixed at 1/0.1-3 ratio and excess of polyvalent phenol compound are added under the presence of catalyst as additive.
摘要翻译：目的：提供用于环氧树脂粉末涂料的多功能酚固化剂的生产方法，其在暴露于水中之后减少硬化膜内多孔的产生，并且不降低硬化速度。构成：环氧树脂粉末涂料用多功能酚类固化剂的制造方法，其特征在于将化学式1所示的双酚型环氧树脂和化学式2所示的酚醛清漆型环氧树脂以1 / 在催化剂存在下添加0.1-3％的比例和过量的多价酚化合物作为添加剂。

43. 发明公开

KR1020000047286A 노블락 변성 에폭시 수지의 제조방법 및 이를이용한분체도료 조성물 有权
标题翻译：生产NOVOLAK脱漆环氧树脂的方法和其中的粉末涂料组合物
公开(公告)号：KR1020000047286A
公开(公告)日：2000-07-25
申请号：KR1019980064079
申请日：1998-12-31
申请人： 주식회사 케이씨씨
发明人： 김도훈 , 최승엽 , 김봉수
IPC分类号： C09D163/04 , C09D5/03 , C08G59/00
CPC分类号： C09D163/04 , C08G59/00 , C09D5/03
摘要： PURPOSE: Novolak denatured resin for steel pipe or reinforcing rod, and powdery coating composition therefrom are provided which are excellent in adhesive property for substrate, cathode spattering, and flexibility, and are able to be produced by rapid hardening(not more than 2 minutes) at low temperature(not more than 200°C). CONSTITUTION: An epoxy resin is prepared by the following steps: preparing epoxy resin containing hydroxyl group by mixing 35-45 parts by weight of phenol with 100 parts of aliphatic epoxy compounds and polymerizing thereof, wherein the equivalents of hydroxyl group is 1000-2000g/eq and the number average molecular weight is 400-1000; adding 400-440 parts by weight of bisphenol type epoxy resin and 90-230 parts by weight of phenol to 100 parts of the resultant epoxy resin to obtain polymerized bisphenol type epoxy resin, wherein epoxy equivalents is 500-2000g/eq and the number average molecular weight is 500-5000; and adding 5-30 parts by weight of novolak epoxy of which epoxy equivalents is 150-400g/eq and 1-5 parts by weight of polyphenol to obtain polymerized novolak denatured epoxy resin, wherein epoxy equivalents is 500-2000g/eq, the number average molecular weight is 500-5000, and the softening point is 90-130°C.
摘要翻译：目的：提供用于钢管或增强棒的酚醛清漆变性树脂及其粉末涂料组合物，其具有优异的基材粘合性能，阴极溅射和柔韧性，并且能够通过快速硬化（不超过2分钟）在低温（不高于200℃）。构成：通过以下步骤制备环氧树脂：通过将35-45重量份的苯酚与100份脂族环氧化合物混合并聚合制备含羟基的环氧树脂，其中羟基的当量为1000-2000g / eq，数均分子量为400-1000; 向100份得到的环氧树脂中添加400-440重量份双酚型环氧树脂和90-230重量份苯酚，得到聚合双酚型环氧树脂，其中环氧当量为500-2000g / eq，数均分子量为500-5000; 并加入5-30重量份环氧当量为150-400g / eq的酚醛清漆环氧树脂和1-5重量份多酚，得到环氧当量为500-2000g / eq的聚合酚醛清漆变性环氧树脂，数量平均分子量为500-5000，软化点为90-130℃。

44. 发明公开

KR1019990060696A 고 내후성 반광 분체도료의 제조방법 有权
公开(公告)号：KR1019990060696A
公开(公告)日：1999-07-26
申请号：KR1019970080939
申请日：1997-12-31
申请人： 주식회사 케이씨씨
发明人： 강충구 , 최승엽 , 권오원 , 김도훈 , 정치욱
IPC分类号： C09D5/03 , C09D167/00
摘要： 본 발명은 고 내후성 반광 분체도료의 제조방법에 관한 것으로, 좀 더 상세하게는 (1) 말단에 서로 다른 두 종의 관능기를 가지는 폴리에스테르 수지 29∼57중량%, 당량이 70∼600인 하이드록시 또는 에폭시기를 가지는 경화제 1∼20중량%, -NCO 당량이 80∼350인 메톡시기 또는 -NCO기를 가지는 경화제 1∼10중량%, 티타늄 다이옥시드 26∼32중량%, 체질안료 18중량% 이하, 소광제 5중량% 이하, 및 기타 첨가제 18중량% 이하를 프리믹싱 탱크에 사입하고 프리믹싱시킨 후 분산기에서 90∼130℃로 용융 분산시켜 고속믹서로 분쇄하고 100∼340메쉬로 여과시켜 도료를 제조하는 단계; (2) 카르복시기만을 갖는 폴리에스테르 수지 34∼56중량%, 당량이 70∼350인 하이드록시 또는 에폭시기를 가지는 경화제 1∼17중량%, 티타늄 다이옥시드 26∼32중량%, 체질안료 18중량% 이하, 소광제 5중량% 이하, 및 기타 첨가제 6중량% 이하를 프리믹싱 탱크에 사입하고 프리믹싱시킨 후 분산기에서 90∼130℃로 용융 분산시켜 고속믹서로 분쇄하고 100∼340메쉬로 여과시켜 도료를 제조하는 단계; 및 (3) 상기 (1)단계 및 (2)단계 도료를 2/8∼8/2의 혼합비로 혼합한 다음, 드라이 브렌딩시키는 단계로 이루어지는 고 내후성 반광 분체도료의 제조방법에 관한 것이다.