31. 发明公开

KR1020030047106A 원심 성형법을 이용한 실리카 글래스의 제조 방법 无效
标题翻译：使用离心成型方法制备二氧化硅玻璃的方法
公开(公告)号：KR1020030047106A
公开(公告)日：2003-06-18
申请号：KR1020010077499
申请日：2001-12-07
申请人： 삼성전자주식회사
发明人： 박근덕 , 오정현 , 백영민
IPC分类号： C03B19/12 , C03B37/016 , G02B6/00
CPC分类号： C03B37/016 , C03B2203/26
摘要： PURPOSE: A method for preparing silica glass using centrifugation molding method is provided, which is useful to prepare a multiple mode optical fiber and is improved in the reproducibility of thickness of a molded layer owing to the centrifugal force. CONSTITUTION: The method comprises the steps of (23) mixing a starting material with deionized water, and adding a dispersant to the mixture to prepare sol; (31) injecting the sol into a cylindrical mold, and (33) gelling the sol into a certain thickness along the circumference of the mold with rotating the mold; and repeating the centrifugation molding process at least two times with changing the content of dopant of the sol added to the mold step by step according to the distribution of refractive index of the molded silica glass. The closer the centrifugation molding layer to the center of the mold, the greater the addition amount of the dopant.
摘要翻译：目的：提供一种使用离心成型法制备石英玻璃的方法，其可用于制备多模光纤，并且由于离心力而提高了模制层的厚度的再现性。方法：该方法包括以下步骤：（23）将原料与去离子水混合，并向混合物中加入分散剂以制备溶胶; （31）将溶胶注入圆筒形模具中，（33）通过旋转模具将溶胶沿着模具的圆周胶凝成一定厚度; 并且根据模制石英玻璃的折射率分布，逐渐改变添加到模具中的溶胶的掺杂剂的含量，重复离心模制过程至少两次。离心成型层越靠近模具的中心，掺杂剂的添加量越多。

32. 发明公开

KR1020030022952A 투명 실리카 글래스의 제조 방법 有权
标题翻译：透明二氧化硅玻璃的制造
公开(公告)号：KR1020030022952A
公开(公告)日：2003-03-19
申请号：KR1020010055811
申请日：2001-09-11
申请人： 재단법인 포항산업과학연구원
发明人： 전명철 , 김선욱
IPC分类号： C03B19/12
CPC分类号： C03B19/12
摘要： PURPOSE: Provided is a method for manufacturing transparent silica glass with good transparency and near theoretical density by vacuum sintering silica compacts derived from the silica sol comprising silica powder(fumed silica), dispersant and polyethyl oxazoline-dissolved water. CONSTITUTION: The method for manufacturing transparent silica glass comprises the steps of: (i) preparing a silica sol by mixing silica powder, fumed silica (40-100nm), dispersant such as tetramethyl ammonium hydroxide(TMAH) or tetraethyl ammonium hydroxide(TEAH), and deionized water containing polyethyl oxazoline(PEOZ), being 1,000-1,000,000 in molecular weight, as a binder; (ii) adding gelling agents, aliphatic ester compounds such as methyl lactate and ethyl formate; (iii) pouring the silica sol into a mold and gelling; (iv) demolding to get a bulky gel; (v) drying at 30-80deg.C; (vi) thermal treating at 5-50deg.C/hr to 300-600deg.C for removal of organics; (vii) thermal treating at 100deg.C/hr to 500-1000deg.C in Cl2 atmosphere for removal of hydroxide ions and metallic impurities; (viii) sintering at 1350deg.C for 1hr under vacuum between 10-1 and 10-6 torr. The step for removing foams in silica sol is optionally added to the next of step (i).
摘要翻译：目的：提供一种通过真空烧结由二氧化硅粉末（热解法二氧化硅），分散剂和聚乙基恶唑啉溶解的水的二氧化硅溶胶衍生的二氧化硅凝胶制造透明度和理论密度接近的透明石英玻璃的方法。构成：制造透明石英玻璃的方法包括以下步骤：（i）通过混合二氧化硅粉末，煅制二氧化硅（40-100nm），分散剂如四甲基氢氧化铵（TMAH）或四乙基氢氧化铵（TEAH））制备二氧化硅溶胶，和含有分子量为1,000-1,000,000的聚乙基恶唑啉（PEOZ）的去离子水作为粘合剂; （ii）加入胶凝剂，脂肪族酯化合物如乳酸甲酯和甲酸乙酯; （iii）将二氧化硅溶胶倒入模具中并凝胶化; （iv）脱模以得到笨重的凝胶; （v）30-80℃干燥; （vi）以5-50℃/小时热处理至300-600℃以除去有机物; （vii）在Cl2气氛中以100℃/小时热处理至500-1000℃，以除去氢氧根离子和金属杂质; （viii）在1350℃下在10-1和10-6托之间的真空下烧结1小时。在硅溶胶中去除泡沫的步骤任选加入到步骤（i）的下一步骤中。

33. 发明授权

KR100346105B1 굴절율 분포를 가지는 실리카 글래스의 제조 방법 失效
标题翻译：具有折射率分布的石英玻璃的制造方法
公开(公告)号：KR100346105B1
公开(公告)日：2002-08-01
申请号：KR1020000052345
申请日：2000-09-05
申请人： 삼성전자주식회사
发明人： 박근덕
IPC分类号： C03B19/12
摘要： 본 발명은 실리카 글래스의 제조 방법에 있어서, 출발 물질을 분산매에 혼합하여 솔을 형성하는 분산 과정과; 상기 솔을 성형틀에 넣어 일정 형태의 습윤젤로 성형하고, 상기 습윤젤을 성형틀로부터 분리하는 성형 과정과; 상기 습윤젤을 미리 설정된 온도 및 습도 조건하에서 건조시켜 습윤젤 내의 분산매를 제거함으로써 미리 설정된 수분 함량 분포를 가진 1차 건조젤을 형성하는 건조 과정과; 상기 1차 건조젤을 첨가제 용액 속에 넣어 1차 건조젤 내의 잔존 수분과 첨가제 용액간의 가수 분해를 유도하는 가수 분해 과정과; 상기 가수 분해 과정을 거친 1차 건조젤을 다시 건조시켜 2차 건조젤을 형성하는 재건조 과정과; 상기 2차 건조젤에 반응 가스를 공급하여 불순물을 제거한 후 소결시켜 유리화하는 열처리 과정을 포함함을 특징으로 하는 굴절율 분포를 가지는 실리카 글래스의 제조 방법을 제공한다.

34. 发明授权

KR1019930000200B1 졸-겔법에 의한 희토류원소 도우프글래스의 제조방법 失效
标题翻译：通过溶胶凝胶法生产稀土元素玻璃的方法
公开(公告)号：KR1019930000200B1
公开(公告)日：1993-01-14
申请号：KR1019900021079
申请日：1990-12-19
申请人： 스미토모덴키고교가부시키가이샤
发明人： 이또우마스미 , 세이도우다쯔히꼬 , 요꼬다히로시
IPC分类号： C03B8/02 , C03B19/12
CPC分类号： C03C1/006 , C03B37/016 , C03B2201/30 , C03B2201/34 , C03B2201/36 , C03C3/095 , C03C4/0071 , Y10S65/901
摘要： 내용 없음.

35. 发明公开

KR850001509A 유리 또는 세라믹 생성물의 성형방법 失效
公开(公告)号：KR850001509A
公开(公告)日：1985-03-30
申请号：KR840004955
申请日：1984-08-17
IPC分类号： C03B37/016 , B28B1/14 , C01B33/145 , C03B8/02 , C03B19/02 , C03B19/12 , C03B20/00 , C03C1/00 , C03C1/02 , C03C3/00 , C04B33/28 , C04B35/00
摘要： 내용없음

36. 发明公开

KR850000374A 유리 또는 세라믹 제품의 제조방법 失效
公开(公告)号：KR850000374A
公开(公告)日：1985-02-27
申请号：KR840003621
申请日：1984-06-26
IPC分类号： B28B1/00 , C03B8/02 , C03B19/12 , C03B20/00 , C03B37/00 , C03B37/016 , C03B37/025 , C03C1/00 , C03C3/00 , C03C13/04 , G02B6/00
摘要： 내용없음.