US20130158220A1 Method Of Manufacture Of Polytetrafluoroethylene Stretched Film, And Polytetrafluoroethylene Stretched Film
有权
基本信息:
- 专利标题： Method Of Manufacture Of Polytetrafluoroethylene Stretched Film, And Polytetrafluoroethylene Stretched Film
- 专利标题（中）：聚四氟乙烯拉伸膜和聚四氟乙烯拉伸膜的制造方法
- 申请号：US13818651 申请日：2011-08-19
- 公开(公告)号：US20130158220A1 公开(公告)日：2013-06-20
- 发明人： Hiroki Uehara , Takeshi Yamanobe , Yasumasa Yukawa , Yasuhiko Matsuoka
- 申请人： Hiroki Uehara , Takeshi Yamanobe , Yasumasa Yukawa , Yasuhiko Matsuoka
- 申请人地址： JP Maebashi-shi, gunma
- 专利权人： NATIONAL UNIVERSITY CORPORATION GUNMA UNIVERSITY
- 当前专利权人： NATIONAL UNIVERSITY CORPORATION GUNMA UNIVERSITY
- 当前专利权人地址： JP Maebashi-shi, gunma
- 优先权： JP2010-189636 20100826
- 国际申请： PCT/JP2011/068752 WO 20110819
- 主分类号： B29C43/14
- IPC分类号： B29C43/14
摘要：
A method of manufacturing a PTFE stretched film that has higher tensile strength at its breaking point. In the method, a resin composition is obtained by mixing an emulsion of PTFE (A) with a number average molecular weight of 5×106 or more and an emulsion of PTFE (B) with a number average molecular weight of 1×106 to 4×106 so that the solid content ratio (A/B) of the PTFE (A) and the PTFE (B) is 99/1 to 10/90. The mixed emulsion is subjected to compression molding in a melted state under a reduced-pressure atmosphere to obtain a film.
摘要（中）：
制造在其断裂点具有较高拉伸强度的PTFE拉伸膜的方法。 在该方法中，通过将数均分子量为5×10 6以上的PTFE（A）的乳液与数均分子量为1×106〜4的PTFE（B）的乳液混合，得到树脂组合物 ×106，使得PTFE（A）和PTFE（B）的固体成分比（A / B）为99/1〜10/90。 将混合乳液在减压气氛下在熔融状态下进行压缩成型，得到膜。
公开/授权文献:
IPC结构图谱:
| B | 作业；运输 |
| --B29 | 塑料的加工；一般处于塑性状态物质的加工 |
| ----B29C | 塑料的成型或连接；塑性状态物质的一般成型；已成型产品的后处理，如修整 |
| ------B29C43/00 | 压力成型，即施加外部压力使造型材料流动；所用的设备 |
| --------B29C43/02 | .定长的制品，即不连续的制品 |
| ----------B29C43/14 | ..在几道工序中 |