The present invention is a dielectric ceramic composition, comprising a main component including a dielectric oxide, and a sintering auxiliary comprising a first component including an oxide of Li and a second component including an oxide of M1 (note that M1 is at least one kind of element selected from group V elements and VI group elements): wherein said dielectric ceramic composition comprises a plurality of dielectric particles and crystal grain boundaries existing between said dielectric particles next to each other; concentration of M1 element becomes lower from a particle surface to inside thereof in the plurality of dielectric particles; and when assuming that a particle diameter of said dielectric particles is D and a content ratio of the M1 element at said crystal grain boundaries is 100%, a content ratio of the M1 element at a depth T50, where a depth from the particle surface is 50% of said particle diameter D, is 3 to 55%.