- 专利标题： 프리-세라믹 성형체를 제조하기 위한 고분자 폴리실란 및 그의 제조 방법
- 专利标题（英）：High-molecular polysilane and method for the production thereof for producing pre-ceramic molded bodies
- 专利标题（中）：- 高分子量聚硅烷及其生产预制陶瓷成型体的生产方法
- 申请号：KR20177036655 申请日：2013-12-12
- 公开(公告)号：KR20180001568A 公开(公告)日：2018-01-04
- 发明人： 그라베,노르만
- 申请人： 비제이에스 세라믹스 게엠베하
- 申请人地址： Senefelderstrasse *, ***** Gersthofen, Germany
- 专利权人： 비제이에스 세라믹스 게엠베하
- 当前专利权人： 비제이에스 세라믹스 게엠베하
- 当前专利权人地址： Senefelderstrasse *, ***** Gersthofen, Germany
- 代理人： 양영준; 서정애
- 优先权： DE102012223260 2012-12-14
- 国际申请： PCT/EP2013/076346 2013-12-12
- 国际公布： WO2014090932 2014-06-19
- 主分类号： C08G77/60
- IPC分类号： C08G77/60 ; C04B35/571 ; C04B35/626 ; C04B35/80 ; C08G77/00 ; D01F6/78 ; D01F9/10
摘要：
(i) 2종이상의실란단량체및 (ii) 1종이상의알칼리금속을반응시키며, 여기서상기실란단량체는하기구조단위: - 1개이상의아릴기, - 1개이상의알킬기, - 1개이상의알케닐기 및 - 상기실란단량체중 1종의규소원자에결합된 3개이상의할로겐원자를함유하는것인단계를포함하며, 상기반응단계가에테르-함유용매, 특히바람직하게는디옥산중에서일어나는것을특징으로하는, 폴리실란의제조방법이개시된다. 수득된폴리실란은고분자량및 100℃에서 1500 내지 3000 Pa·s의점도를갖는다. 폴리실란은가공되어탄화규소섬유및 섬유복합재를형성하는데매우적합하다.
摘要（中）：
一种方法通过使至少两种硅烷单体和至少一种碱金属反应来生产聚硅烷。 硅烷单体具有以下结构单元：至少一个芳基，至少一个烷基，至少一个链烯基和至少三个卤素原子。 其中至少三个卤素原子键合到硅烷单体之一的硅原子上，反应步骤在含醚溶剂中进行，特别优选在二恶烷中进行。 得到的聚硅烷的分子量高，在100℃下的粘度为1500〜3000Pa·s。 聚硅烷非常适合加工成碳化硅纤维和纤维复合材料。
摘要（英）：
(I) sikimyeo reaction of two or more silane monomers and (ii) an alkali metal at least one, in which the silane monomer for the structural unit: - at least one aryl group, and - one or more alkyl groups, - one or more alkenyl characterized in that taking place in a contained solvent, and particularly preferably dioxane-group and wherein said reaction step is an ether, comprising the steps to contain at least three halogen atoms bonded to silicon atoms in one kind of the silane monomer , a method for producing polysilane which is disclosed. The obtained polysilane has a viscosity of 1500 to 3000 Pa · s in a high molecular weight and 100 ℃. Polysilane is processing is well suited for forming the silicon carbide fibers and fiber composites.
信息查询:
EspacenetIPC结构图谱:
| C | 化学；冶金 |
| --C08 | 有机高分子化合物；其制备或化学加工；以其为基料的组合物 |
| ----C08G | 用碳—碳不饱和键以外的反应得到的高分子化合物 |
| ------C08G77/00 | 在高分子主链中形成含硅键合，有或没有硫、氮、氧，或碳键合反应得到的高分子化合物 |
| --------C08G77/60 | .其中所有的硅原子是与氧以外的原子键合 |