To perform brazing stably without a flux.SOLUTION: An aluminum alloy clad material includes a brazing material disposed on both surfaces of the core material, the brazing material containing, by mass%, Si: 6.0-14.0%, Fe: 0.05-0.3%, Mg: 0.02-1.5%, Bi: 0.05-0.25%, Sr: 0.0001%-0.1%, and the balance consisting of Al and inevitable impurities, and satisfying a relationship of (Bi+Mg)×Sr≤0.1. Mg-Bi-based compounds contained in the brazing material with a diameter of 0.1 μm or more and less than 5.0 μm in terms of equivalent circle diameter are more than 20 in number per 10,000 μm2 when observed in a surface layer plane direction before brazing, and the Mg-Bi-based compounds with a diameter of 5.0 μm or more are less than 2 in number per 10,000 μm2, and the core material contains Mn: 0.8-1.8%, Si: 0.01-1.0%, Fe: 0.1-0.5%, and the balance consisting of Al and inevitable impurities. A cathode current density of the brazing material layer measured at room temperature in a 5% NaCl solution at a pH of 3 after a brazing heat treatment is 0.1 mA/cm2 or less.SELECTED DRAWING: Figure 1