The invention discloses a domestic 08Ni3DR steel thin multi-pass welding process, which is characterized by comprising the following steps of: machining a welding part into a single V-shaped or symmetrical double V-shaped groove, employing thin layer multi-pass welding, wherein on each layer, the weld pass thickness is less than 3mm, the diameter of a welding wire is 3.2mm, the welding current is 350 to 380A, the welding voltage is 34 to 38V and the welding speed is 36 to 45cm per minute, and controlling the interlayer and inter-pass temperature to be less than or equal to 150 DEG C; and performing dehydrogenation treatment and overall stress relief heat treatment after welding, and manufacturing a pressure container with the temperature level of 100 DEG C below zero such as main low temperature methanol wash equipment H2S and a CO2 absorption tower by employing the process, wherein the impact work kv2 of the welding joint of the equipment at the temperature of 101 DEG C below zero is more than or equal to 47J, and the mean value of the technical index and physical level is higher than American society of mechanical engineers (ASME) standard technical index.